Chlorite mesoporous composite material, supported catalyst, preparation method thereof, application and preparation method of cyclohexanone glycerol ketal

A technology of supported catalysts and composite materials, applied in organic compound/hydride/coordination complex catalysts, catalyst carriers, chemical instruments and methods, etc., can solve the problems of low conversion rate of reaction raw materials, achieve less side reactions, High conversion rate of reaction raw materials, simple post-processing effect

Active Publication Date: 2015-12-16
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the defects of low conversion rate of reaction raw materials in the ketal reaction process of the supported catalyst made of existing mesoporous molecular sieve materials, and to provide a spherical chlorite mesoporous material suitable for use as a carrier Composite material, and the preparation method of the spherical chlorite mesoporous composite material, the spherical chlorite mesoporous composite material prepared by the method, the supported catalyst containing the spherical chlorite mesoporous composite material, the supported catalyst The preparation method, the supported catalyst prepared by the method, the application of the supported catalyst in the ketal reaction, and the method of using the supported catalyst to prepare cyclohexanone glycerol ketal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chlorite mesoporous composite material, supported catalyst, preparation method thereof, application and preparation method of cyclohexanone glycerol ketal
  • Chlorite mesoporous composite material, supported catalyst, preparation method thereof, application and preparation method of cyclohexanone glycerol ketal
  • Chlorite mesoporous composite material, supported catalyst, preparation method thereof, application and preparation method of cyclohexanone glycerol ketal

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] In step (1), "providing a mesoporous molecular sieve material with a three-dimensional cubic pore structure" can be directly weighed or selected a product of a mesoporous molecular sieve material with a three-dimensional cubic pore structure, or can be prepared with a three-dimensional cubic pore structure. Mesoporous molecular sieve materials. The preparation method of the mesoporous molecular sieve material with a three-dimensional cubic channel structure can be implemented according to a conventional method, for example, the preparation method can include: preparing a filter cake of a mesoporous molecular sieve material with a three-dimensional cubic channel structure according to the above method, and then The obtained filter cake is dried, and the templating agent in the product obtained after drying is removed. The conditions for removing the template agent may include: a temperature of 300-600° C. and a time of 10-80 hours.

[0051] The process of preparing the ...

Embodiment 1

[0092] This example is used to illustrate the spherical chlorite mesoporous composite material and supported catalyst of the present invention and their preparation methods.

[0093] (1) Preparation of spherical chlorite mesoporous composites

[0094] Dissolve 6g (0.001mol) of triblock copolymer surfactant P123 in 10ml of hydrochloric acid aqueous solution with a pH value of 4 and 220ml of deionized aqueous solution, stir for 4h until P123 dissolves to form a transparent solution, and then add it to the transparent solution Add 6g (0.08mol) of n-butanol and stir for 1h, then place it in a water bath at 40°C, slowly add 12.9g (0.062mol) of tetraethyl orthosilicate into the solution, and keep the temperature at about 40°C. Stir for 24 hours at a pH value of 4.5, then hydrothermally treat at 100°C for 24 hours, then filter and wash with deionized water for 4 times, and then suction filter to obtain filter cake X1 of mesoporous molecular sieve material with three-dimensional cubic...

Embodiment 2

[0113] This example is used to illustrate the spherical chlorite mesoporous composite material and supported catalyst of the present invention and their preparation methods.

[0114] The spherical chlorite mesoporous composite material and the supported catalyst were prepared according to the method of Example 1. The difference was that there was no spray drying step in the process of preparing the supported catalyst, but the benzenesulfonic acid was loaded on the surface only by impregnation. On the spherical chlorite mesoporous composite material, the supported catalyst Cat-2 was prepared.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to a spherical chlorite mesoporous composite material, a preparation method of the spherical chlorite mesoporous composite material, the spherical chlorite mesoporous composite material prepared by the method, a supported catalyst containing the spherical chlorite mesoporous composite material, a preparation method of the supported catalyst, the supported catalyst prepared by the method, the application in ketalation of the supported catalyst, and a preparation method of cyclohexanone glycerol ketal by using the supported catalyst, wherein, the spherical chlorite mesoporous composite material comprises chlorite, a mesoporous molecular sieve material with a three dimensional cubic pore structure, and a mesoporous molecular sieve material with a hexagonal pore structure. The supported catalyst prepared by using the spherical chlorite mesoporous composite material as the carrier in the invention can improve the conversion rate of the reaction raw materials greatly in ketalation.

Description

technical field [0001] The invention relates to a spherical chlorite mesoporous composite material, a method for preparing the spherical chlorite mesoporous composite material, and the spherical chlorite mesoporous composite material prepared by the method contains the spherical chlorite mesoporous composite material A supported catalyst for materials, a method for preparing a supported catalyst, the supported catalyst prepared by the method, the application of the supported catalyst in ketal reaction, and the preparation of cyclohexanone glycerol ketal using the supported catalyst Methods. Background technique [0002] Cyclohexanone glycerol ketal is a fragrance with delicate fragrance and floral and woody fragrance. Compared with carbonyl compounds, it has the advantages of long-lasting fragrance, rich source of raw materials, simple production process and stable chemical properties. Generally, cyclohexanone glycerol ketal is prepared by ketal reaction of glycerin and cyc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J32/00B01J35/10B01J35/08B01J31/26C07D317/72
Inventor 亢宇张明森
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap