A kind of manufacturing method of thin gauge hot-rolled strip steel
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for hot-rolled strip steel and a manufacturing method, which is applied to manufacturing tools, metal rolling, metal rolling, etc., can solve the problems of high power consumption and poor surface quality of the production line, and achieves increasing the number of rolling kilometers and improving the product quality. Effect of surface quality and extended roll change cycle
Active Publication Date: 2019-07-12
NORTHEASTERN UNIV LIAONING
View PDF7 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The purpose of the present invention is to provide a thin-gauge hot-rolled steel strip manufacturing method to solve the problems of high power consumption and poor surface quality of the current ESP production line
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0028] The process layout diagram of the thin-gauge steel strip production process of the present invention is as figure 1 shown. The specific implementation steps are as follows:
[0029] (1) The qualified molten steel produced in the steelmaking workshop is transported to the continuous casting workshop, and is hoisted by a crane to the ladle seat of the ladle turret, and the ladle turret rotates half a circle to the pouring position before pouring.
[0030] (2) After the casting starts, the casting speed of the continuous casting machine is gradually increased to 6.0m / min, the thickness of the continuous casting slab at the mold outlet is 90-110mm, the sector section is pressed down by 10mm, and the thickness of the casting slab at the exit of the continuous casting machine is 80-100mm. After the casting speed stabilizes, the surface temperature of the slab at the exit of the continuous casting machine is 1050-1150°C, and the temperature of the core of the slab is 1300-140...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a manufacturing method for thin-specification hot-rolled strip steel. The manufacturing method is characterized in that a single-machine uniflow thin slab continuous casting machine is directly connected with a rolling mill. The manufacturing method comprises the steps of steel-making, continuous casting, swing type shearing, steel pushing, descaling, side heating, unit rough rolling, fly shearing, coreless coiling, induction heating, descaling, unit finish rolling, strip steel cooling, shearing, coiling, coil discharging, bundling, coil transporting, weighing and marking, transporting and storing. The manufacturing method adopts an endless rolling process or a single-billet rolling process. A temperature of casting billet at an outlet of the continuous casting machine is higher than that of an ESP production line by 100-150 DEG C, so that a utilization rate of waste heat of continuously cast billet is increased, and energy consumption is reduced; compared with the ESP production line, the manufacturing method has the advantages that: swing type shears and a steel pushing roller way are migrated to the front of a roughing mill, so that distances from the swing type shears and the steel pushing roller way to a middle roller way are shortened after rough milling, temperature drop of intermediate billets is reduced, induction heat compensation amount is reduced, and a roll of the roughing mill can be prevented from generating thermal cracks. A descaling device is arranged at an inlet of the roughing mill, and a finish rolling unit adopts an online heating preparation technology and an online quick roll-changing technology, so that surface quality of products is effectively improved.
Description
technical field [0001] The invention belongs to the technical field of hot-rolled strip steel rolling, in particular to a method for manufacturing thin-gauge hot-rolled strip steel. Background technique [0002] The emergence of the ESP thin slab endless rolling production line has made the large-scale and stable production of thin-gauge hot-rolled strip steel a reality. On the Arvedi ESP production line, through the continuous production process, molten steel passes directly through a continuous casting machine and rolling line to produce hot-rolled steel coils. The production line first casts thin slabs, and then directly enters the three-stand large-reduction roughing mill arranged at the exit of the continuous casting machine for rolling, rolling into an intermediate billet with a thickness of 10-20mm, and then the intermediate billet is placed in the induction heater Heating is performed and then rolled to the target thickness by a five-stand finishing mill, after whic...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.