Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of high-strength addition type liquid silicone rubber dipping liquid and its preparation and molding method

A technology of liquid silicone rubber and addition molding, applied in the direction of coating, etc., can solve the problems of the actual application value to be improved, the mechanical strength of silicone rubber impregnated molding products, etc., to achieve reasonable composition and ratio, optimize mechanical properties and processing The effect of high process and mechanical strength

Active Publication Date: 2020-08-07
佛山市方普防护技术有限公司 +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN103214856B discloses a preparation method of dip-molding silicone rubber products, but the mechanical strength of the dip-molding silicone rubber products prepared by it is low, and the practical application value needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength addition type liquid silicone rubber dipping liquid and its preparation and molding method
  • A kind of high-strength addition type liquid silicone rubber dipping liquid and its preparation and molding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The present embodiment prepares the silicone rubber impregnation solution according to the following steps:

[0035] Step 1, 90 parts of 50000mPa·s terminal vinyl silicone oil, 10 parts of 20000mPa·s terminal vinyl silicone oil, 5 parts of polyvinyl silicone oil (vinyl content 4.7%), vinyl MQ silicone resin (vinyl content 0.9%) , M / Q=0.6) 20 parts, put into kneader, knead at room temperature for 1h;

[0036] Step 2. Raise the temperature to 80°C, continue kneading the kneaded product of step 1 for 1 hour, and add silazane in ten times during the kneading process to obtain a specific surface area of ​​175m 2 25 parts per gram of fumed silica; heat up to 120°C, knead for 4 hours; then cool to room temperature, slowly add 50 parts of 5000mPa·s terminal vinyl silicone oil, 30 parts of 1500mPa·s terminal vinyl silicone oil, and continue kneading 1.5h, finally evacuated and kneaded for 1h, and the kneaded final product was obtained after discharging;

[0037] Step 3. Put th...

Embodiment 2

[0041] The present embodiment prepares the silicone rubber impregnation solution according to the following steps:

[0042] Step 1, 70 parts of 50000mPa·s terminal vinyl silicone oil, 30 parts of 20000mPa·s terminal vinyl silicone oil, 5 parts of polyvinyl silicone oil (vinyl content 4.7%), vinyl MQ silicone resin (vinyl content 0.9%) , M / Q=0.6) 20 parts, put into kneader, knead at room temperature for 1h;

[0043] Step 2. Raise the temperature to 80°C, continue kneading the kneaded product of step 1 for 1 hour, and add silazane in ten times during the kneading process to obtain a specific surface area of ​​175m 2 25 parts per gram of fumed silica; then heat up to 120°C and knead for 4 hours; then cool to room temperature, add 50 parts of 5000mPa·s terminal vinyl silicone oil and 20 parts of 1500mPa·s terminal vinyl silicone oil slowly, and continue kneading 1.5h, finally evacuated and kneaded for 1h, and the kneaded final product was obtained after discharging;

[0044] Ste...

Embodiment 3

[0048] The present embodiment prepares the silicone rubber impregnation solution according to the following steps:

[0049] Step 1, 60 parts of 50000mPa·s terminal vinyl silicone oil, 40 parts of 20000mPa·s terminal vinyl silicone oil, 5 parts of polyvinyl silicone oil (vinyl content 4.7%), vinyl MQ silicone resin (vinyl content 0.9%) , M / Q=0.6) 20 parts, put into kneader, knead at room temperature for 1h;

[0050] Step 2. Raise the temperature to 80°C, continue kneading the kneaded product of step 1 for 1 hour, and add silazane in ten times during the kneading process to obtain a specific surface area of ​​175m 2 25 parts per gram of fumed silica; heat up to 130°C, knead for 4 hours; then cool to room temperature, add 50 parts of 5000mPa·s terminal vinyl silicone oil and 20 parts of 1500mPa·s terminal vinyl silicone oil slowly, and continue kneading 1.5h, finally evacuated and kneaded for 1h, and the kneaded final product was obtained after discharging;

[0051] Step 3. Put...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
viscosityaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength addition type liquid silicone rubber impregnating liquid and preparation and forming methods thereof. The high-strength addition type liquid silicone rubber impregnating liquid is characterized by being prepared by mixing vinyl silicone oil, white carbon black, reinforced silicon resin, hydrogen-containing silicone oil, an inhibitor, a catalyst and a defoamer. The impregnating liquid impregnate and cure a mold to obtain a silicone rubber impregnated and formed product. The silicone rubber impregnated and formed product is good in transparence and high in mechanical strength.

Description

technical field [0001] The invention relates to a silicone rubber impregnating solution and a silicone rubber impregnated molded product. Background technique [0002] Liquid silicone rubber has excellent heat resistance, cold resistance, dielectric properties, ozone resistance and atmospheric aging resistance, aging resistance, light resistance, insulation, heat insulation and other properties. low temperature) to +250°C (or higher temperature) range. Addition-type liquid silicone rubber has the advantages of no release of small molecular substances during vulcanization, high product transparency, stable processing dimensions, and wide process applicability. It has been widely used in the fields of automobiles, construction, electronic power, medical equipment, mechanical engineering, and aerospace. , and its processing and molding are more commonly used in injection, molding, extrusion, casting and other molding methods. [0003] The dip molding process has the character...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/07C08L83/05C08K9/04C08K3/36B29B7/90B29C41/02
CPCB29B7/90B29C41/02C08K2201/006C08L83/04C08L2205/025C08L2205/035C08K9/04C08K3/36
Inventor 吴亚玲方松喜丁运生杨绪锋薛攀
Owner 佛山市方普防护技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com