Composite facing material

A composite paste and matrix layer technology, applied in the field of materials, can solve the problems of non-wear resistance, abrasion, neglect of wear resistance, impact resistance, waterproof performance, etc., to ensure softness, solve the problems of non-impact resistance, non-wear resistance, Effect of improving impact and wear resistance

Active Publication Date: 2017-09-19
百晟新材料有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of people's living standards, it is often necessary to use veneer decoration materials for furniture veneer decoration and wall veneer decoration lamps. Impact strength, waterproof performance, etc. Many veneer materials are not wear-resistant, especially on furniture surfaces, wall surfaces and other parts that are often touched by hands, often wear and tear, affecting the overall decorative effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A composite veneer material, which sequentially includes a wear-resistant layer, a matrix layer and an adhesive layer from top to bottom, the wear-resistant layer and the matrix layer are co-extruded, and the matrix layer is bonded to the adhesive layer with hot melt adhesive;

[0021] The wear-resistant layer is made of the following components in mass percentage:

[0022] EPDM: 40%,

[0023] PP: 56%,

[0024] Peroxide DCP: 1%,

[0025] Cross-linking modifier multifunctional epoxy resin: 3%;

[0026] The base layer is formed by adding foaming agent and crosslinking agent DCP microfoaming 10 times by POE;

[0027] The adhesive layer is fabric.

Embodiment 2

[0029] A composite veneer material, which sequentially includes a wear-resistant layer, a matrix layer and an adhesive layer from top to bottom, the wear-resistant layer and the matrix layer are co-extruded, and the matrix layer is bonded to the adhesive layer with hot melt adhesive;

[0030] The wear-resistant layer is made of the following components in mass percentage:

[0031] EPDM: 70%,

[0032] PP: 26%,

[0033] Peroxide DCP: 3%,

[0034] Cross-linking modifier multifunctional epoxy resin: 1%;

[0035] The base layer is formed by adding foaming agent and cross-linking agent DCP micro-foamed 20 times by POE;

[0036] The adhesive layer is fabric.

Embodiment 3

[0038] A composite veneer material, which sequentially includes a wear-resistant layer, a matrix layer and an adhesive layer from top to bottom, the wear-resistant layer and the matrix layer are co-extruded, and the matrix layer is bonded to the adhesive layer with hot melt adhesive;

[0039] The wear-resistant layer is made of the following components in mass percentage:

[0040] EPDM: 50%,

[0041] PP: 25%,

[0042] Peroxide DCP: 2.5%,

[0043] Cross-linking modifier multifunctional epoxy resin: 2.5%;

[0044] The base layer is formed by adding foaming agent and cross-linking agent DCP micro-foaming 15 times from POE;

[0045] The adhesive layer is fabric.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite facing material, comprising a wear-resistant layer, a base layer and a bonding layer sequentially from top to bottom; the wear-resistant layer and the base layer are formed by co-extrusion; the base layer is pasted to the bonding layer through hot melt glue; the wear-resistant layer is made from, by weight, 40-70% of EPDM (ethylene propylene diene monomer), 25-60% of PP (polypropylene), 1-3% of a peroxide, and 1-3% of a crosslinking modifier; the base layer is formed by adding a foaming agent and crosslinking agent DCP to POE (polyolefin elastomer) and micro-foaming; the bonding layer is of fabric. The wear-resistant polyolefin elastomer is combined to the foamed POE material, and therefore, wear resistance and impact resistance are imparted to the surface, and the base layer is imparted softness.

Description

technical field [0001] The invention relates to the technical field of materials, and specifically discloses a composite veneer material. Background technique [0002] With the improvement of people's living standards, it is often necessary to use veneer decoration materials for furniture veneer decoration and wall veneer decoration lamps. Impact strength, waterproof performance, etc., many veneer materials are not wear-resistant, especially on furniture surfaces, wall surfaces and other parts that are often touched by hands, often wear and tear, affecting the overall decorative effect. Contents of the invention [0003] Based on this, it is necessary to provide a composite veneer material for the existing technical problems. By compounding the wear-resistant polyolefin elastomer on the foamed POE material, the surface layer is wear-resistant and impact-resistant, and the base layer is soft. technical effect. [0004] For realizing above-mentioned technical purpose, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B7/12B32B25/16B32B25/08B32B27/32B32B27/06B32B27/12B32B27/18C08L23/16C08L23/12C08L63/00C08K5/14C08L23/08
Inventor 罗峰张瑞洋
Owner 百晟新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap