Flux and casting method using same

A technology of flux and alkaline flux, which is applied in the field of flux and casting using it, can solve the problems of cost increase and casting process cost, and achieve the effect of preventing cost increase and improving quality

Active Publication Date: 2017-11-10
浦项控股股份有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, since both the high alkalinity flux and the high silica rice husk flux have been used to achieve the a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flux and casting method using same
  • Flux and casting method using same
  • Flux and casting method using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] Hereinafter, specific embodiments will be described in detail with reference to the accompanying drawings. However, this invention may be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.

[0041] In the following, reference will be made to Figure 1 to Figure 3 A flux according to an exemplary embodiment and a casting method using the same are described. in the text, figure 1 is a schematic diagram illustrating typical casting equipment, figure 2 is a block diagram schematically illustrating components in a flux and the content of each component according to an exemplary embodiment, and image 3 is a flowchart illustrating a casting method according to an exemplary embodiment.

[0042] First, before describing the flux according to the exemp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a flux supplied to an upper portion of a molten steel in a tundish, and a casting method using the same. The flux is able to totally be displaced with SiO2-based and Al2O3-based flux conventionally used in accordance with a tundish operation environment, or is able to be used by being partially mixed with a first composition and a second composition, the first composition including 45 to 60 wt% of SiO2 based on a total 100 wt% of the flux and 20 to 40 wt% of MgO, the second composition containing the component controlling reoxidization of the molten steel and the melting point and viscosity of the flux. That is, by providing the flux having SiO2 and MgO as the basic composition, it is possible to increase the thermal insulation of the molten steel, suppress the reoxidation of the molten steel, absorb the inclusion easily, and minimize the melting damage of refractory materials. Accordingly, the treatment of the molten steel in the tundish is easy, and the quality of the manufactured steel product can be increased.

Description

technical field [0001] The present disclosure relates to a flux and a casting method using the same, and more particularly, to a flux that can improve the quality of molten steel by being added to a tundish and a casting method using the same. Background technique [0002] Generally, a continuous casting process of casting molten steel into a slab is a process in which molten steel contained in a ladle after completion of secondary refining (in a state in which molten steel is temporarily stored in a tundish) is supplied to a mold and cooled , to manufacture semi-finished products in various shapes, such as slabs, blooms, billets and beam blanks for I-beams. [0003] In the tundish during the continuous casting process, the molten steel is finalized before casting and, to ensure the cleanliness of the molten steel, a flux is added on top of the molten steel to remove inclusions from the molten steel and to inhibit re-oxidation. [0004] Overbased fluxes and high silica rice...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C7/076
CPCC21C7/076Y02P10/20B22D11/108B22D11/111B22D11/16
Inventor 朴贤绪徐成谟文湖晶朴重吉金圣光柳泓玖崔圣民
Owner 浦项控股股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap