High-temperature-resistant TC ceramic floor coating

A technology of high temperature resistance and floor paint, applied in the field of high temperature resistant TC ceramic floor paint, can solve the problem of low applicability and achieve the effect of plump paint film, high crosslink density and bright gloss

Inactive Publication Date: 2018-07-20
SHANGHAI CHAMPS ELYSEES PAINT
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the applicability is not high in some food processing enterprises, hospitals and other places where high temperature disinfection is often required.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] 10 parts of inorganic compound, including 5 parts of kaolin, 5 parts of zinc silicate, and the rest is aluminum oxide.

[0016] 2 parts of multifunctional organic film formers, 1 part of organic silicon and the rest of hexafluorobutyl acrylate.

[0017] 2 parts of inorganic boron crosslinking agent;

[0018] 2 parts of titanium dioxide;

[0019] 2 parts of pigments are high temperature resistant inorganic pigments.

Embodiment 2

[0021] 15 parts of inorganic compound, including 5 parts of kaolin, 5 parts of zinc silicate, and the rest is alumina.

[0022] 3 parts of multifunctional organic film formers, 1 part of organic silicon and the rest of hexafluorobutyl acrylate.

[0023] 2 parts of inorganic boron crosslinking agent;

[0024] 2.5 parts of titanium dioxide;

[0025] 2 parts of pigments are high temperature resistant inorganic pigments.

Embodiment 3

[0027] 20 parts of inorganic compound, including 5 parts of kaolin, 5 parts of zinc silicate, and the rest is alumina.

[0028] 4 parts of multifunctional organic film formers, 2 parts of organic silicon, and the rest are hexafluorobutyl acrylate.

[0029] 2 parts of inorganic boron crosslinking agent;

[0030] 3 parts of titanium dioxide;

[0031] 2 parts of pigments are high temperature resistant inorganic pigments.

[0032] This product can withstand high temperature over 200°C without affecting its performance, its hardness exceeds 6H pencil hardness, and its flexibility is excellent. It is especially suitable for places where high-temperature disinfection is often required, such as food processing enterprises and hospitals.

[0033] The multi-functional organic film-forming material compounded by various inorganic substances has extremely high hardness due to its extremely high cross-linking density after curing. Permeability.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-temperature-resistant TC ceramic floor coating. The high-temperature-resistant TC ceramic floor coating is characterized by comprising, by weight, 10 to 20 parts of an inorganic compound, 6 to 12 parts of a polyfunctional organic film-forming material, 2 parts of an inorganic boron cross-linking agent, 2 to 3 parts of titanium dioxide and 2 parts of a pigment. The high-temperature-resistant TC ceramic floor coating of the invention can withstand a high temperature of more than 200 DEG C without any influence on the performance; and the hardness of the TC ceramic floor coating exceeds the hardness of a 6H pencil, and the flexibility of the TC ceramic floor coating is excellent. The high-temperature-resistant TC ceramic floor coating is especially applicable toplaces needing frequent high-temperature sterilization, e.g., food processing companies and hospitals.

Description

technical field [0001] The invention relates to a high-temperature-resistant TC ceramic floor paint, which belongs to the field of floor paint. Background technique [0002] Floor paint was first invented by Germany in 1934. It is mainly made of oil, tree materials, colors, solvents, etc. It is mainly divided into decorative floor paint, heavy-duty anti-corrosion floor paint, and heavy-duty floor paint. Floor paint is made up of many different substances through many production processes such as mixing, dissolving, and dispersing. Floor paint has the characteristics of bright, real, beautiful, wear-resistant, waterproof, and anti-corrosion. [0003] The paint film of conventional epoxy floor paint on the market will soften when the ambient temperature exceeds 60°C. Therefore, the applicability is not high in places where high-temperature disinfection is often required, such as some food processing enterprises and hospitals. Contents of the invention [0004] The object ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/61
CPCC09D4/06C09D5/18
Inventor 李学全洪跃忠张华
Owner SHANGHAI CHAMPS ELYSEES PAINT