A method for melting ta10 titanium alloy using electron beam cold hearth furnace

An electron beam cooling hearth furnace and titanium alloy technology, applied in the field of titanium alloy, can solve the problems of poor distribution uniformity of TA10 alloy and excessive volatilization of Ni element, etc., and achieve the effect of fast melting speed, good surface quality and uniform composition

Active Publication Date: 2021-03-16
QINGHAI JUNENG TITANIUM IND CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Baoji Titanium Industry Co., Ltd. and Yunnan Titanium Industry Co., Ltd. respectively conducted research on the one-time forming process of electron beam cold hearth furnace melting of TA10 titanium alloy. The research shows that: in the process of smelting TA10 titanium alloy There are problems of excessive volatilization of Ni element and poor distribution uniformity of prepared TA10 alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for melting ta10 titanium alloy using electron beam cold hearth furnace
  • A method for melting ta10 titanium alloy using electron beam cold hearth furnace
  • A method for melting ta10 titanium alloy using electron beam cold hearth furnace

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] The pressing of embodiment 1 material piece 1#~5#, comparative sample piece D1#-D2#

[0070] Raw materials containing titanium, nickel and molybdenum are mixed to make the same exact mass of raw material blocks, which are pressed into specific size blocks and dried. Table 1 shows the composition and preparation conditions of the materials of blocks 1# to 5#.

[0071] Table 1

[0072]

[0073]

[0074] Taking material block 1# as a typical representative to illustrate the preparation method of the material block, the preparation process is as follows:

[0075] a. Sponge titanium (grade 0) and Ni-Mo master alloy with a total weight of 640Kg are all pressed into raw material blocks after mixing. 32 pieces;

[0076] b. The size of the pressed alloy block is: 200mm×200mm×170mm;

[0077] c. Each electronic scale must be calibrated before use, and the measurement accuracy must be tested with a test weight. After the alloy bag is weighed and bagged, it needs to be re-...

Embodiment 2

[0079] The feeding method of embodiment 2 material block 1#~5#, comparison sample material block D1#~D2#

[0080] Put the prepared material block 1#~5# and the comparison sample material block D1#~2# into the feeder 3 of the electron beam cooling bed melting furnace as shown in Table 2 to smelt the TA10 titanium alloy. Block 1# is a typical representative to explain the stacking rules of the material block, and the stacking requirements are:

[0081] a. General requirements for stacking

[0082] Stacking rules on the left: 4 blocks in each row, placed in a single layer, a total of 16 alloy blocks are stacked, a total of 4 rows;

[0083] Stacking rules on the right side: 4 blocks in each row, placed in a single layer, a total of 16 alloy blocks are stacked, totaling 4 rows.

[0084] b. The specific stacking position is shown in Table 2: (A represents the feed block in the stage of gun opening and ingot bottom making, and B represents the feed block in the stable smelting stag...

Embodiment 3

[0087] The preparation of embodiment 3 ingot 1#~5#, comparison sample ingot D1#~D2#

[0088] Put the material blocks 1#~5# prepared in Example 1 and the comparative sample blocks D1#~2# in the feeder according to the stacking rules of Example 2, and then smelt them in the electron beam cooling hearth furnace through the following steps to prepare cast iron. The ingots are respectively marked as ingots 1#~5#, and the comparison sample ingots D1#~D2#. The electron beam cooling furnace melting process includes the following stages:

[0089] (1) Start the electron gun stage

[0090] The stage of firing the gun: heat the condensate shell without melting it, and observe the change of vacuum in the furnace. During the oven drying period, the current range of 1~5# guns should be strictly controlled not to exceed 5.0A; at the same time, the current range of 6~7# guns should be started to not exceed 2.0A to preheat the bottom support. After confirming that all electron guns are in nor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for smelting a TA10 titanium alloy by using an electron beam cold hearth, and belongs to the field of titanium alloys. The method comprises the following steps that (1), materials containing titanium, nickel and molybdenum are mixed and pressed into a material block, and then the material block is dried; and (2) the dried material block is subjected to smelting byusing the electron beam cold hearth, and the TA10 titanium alloy is obtained. Electron beam cold hearth smelting comprises a gun starting stage, a casting ingot bottom making stage, and a stable smelting stage; and the electron beam cold hearth comprises a melting zone, a refining zone and a crystallization zone which are sequentially adjoined, the power of the melting zone in the stable smeltingstage is 800-1100 Kw, the power of the refining zone is 150-180 Kw, and the power of the crystallization zone is 180-210 Kw. The TA10 titanium alloy prepared through the method is good in element distribution uniformity and surface quality.

Description

technical field [0001] The application relates to a method for melting a TA10 titanium alloy by using an electron beam cold hearth furnace, which belongs to the field of titanium alloys. Background technique [0002] With the rapid growth of the amount of titanium alloy used in the aviation industry, the metallurgical quality of the alloy is becoming more and more important. According to statistics from various countries, many flight accidents are caused by premature failure due to metallurgical defects of titanium alloy components. In order to produce high-quality and high-clean titanium alloys for aero-engine rotating parts, in the late 1980s, the cooling bed melting technology was introduced internationally. , has unique advantages in the production of titanium alloy ingots for key aviation components. Electron beam cold hearth furnace smelting (abbreviated as EB) technology can not only eliminate high-density and low-density inclusions, but also recover a large amount ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22B9/22C22C1/03C22C14/00
CPCC22B9/228C22C1/03C22C14/00
Inventor 周武赵统福杜彬陈生李明
Owner QINGHAI JUNENG TITANIUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap