A Jun porcelain and glaze technology, applied in the field of purple Jun porcelain glaze, can solve the problem of single glaze color, and achieve the effects of good fluidity, good gloss, and colorful glaze.

Inactive Publication Date: 2018-11-16
温书强
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But whether it is Yue Kiln Celadon or Xing Kiln White Porcelain, their glaze color is single, either blue or white, without exception.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A purple Jun porcelain glaze is prepared from the following raw materials in parts by weight: 22 parts of anorthite, 12 parts of calcite, 12 parts of borax, 7 parts of manganese oxide, 5 parts of neodymium oxide and 8 parts of fluorite.

[0022] The preparation method of above-mentioned purple Jun porcelain glaze comprises the following steps:

[0023] (1) Weigh the above-mentioned anorthite, calcite, borax, manganese oxide, neodymium oxide and fluorite into a ball mill to pulverize them, mix them evenly and sieve to obtain the mixture powder;

[0024] (2) Put the mixture powder in a crucible for smelting. The crucible is generally set on the flue between the kiln and the chimney, and a supplementary dye room is set under the furnace. When the heat of the flue gas is insufficient or the kiln stops burning, the It can be roasted in a supplementary combustion chamber. There is a small hole on the bottom of the crucible, which is blocked with a hard quartz ball. When the m...

Embodiment 2

[0027] A purple Jun porcelain glaze is made of the following raw materials in parts by weight: 20 parts of anorthite, 10 parts of calcite, 10 parts of borax, 5 parts of manganese oxide, 4 parts of neodymium oxide and 5 parts of fluorite.

[0028] The preparation method is the same as above.

Embodiment 3

[0030] A purple Jun porcelain glaze is prepared from the following raw materials in parts by weight: 25 parts of anorthite, 15 parts of calcite, 15 parts of borax, 10 parts of manganese oxide, 6 parts of neodymium oxide and 10 parts of fluorite.

[0031] The preparation method is the same as above.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a purple Jun porcelain glaze, which is prepared from the following raw materials: anorthite, calcite, borax, manganese oxide, neodymium oxide and fluorite. The purple Jun porcelain glaze has a formula different from the traditional formulas, the natural raw materials cooperate with each other, the made Jun porcelain glaze has stereoscopic impression, good fluidity and goodgloss. And the Jun porcelain fired from the glaze provided by the invention has bright and smooth glaze color, and the glaze beauty is richer and more colorful.

Description

technical field [0001] The invention belongs to the technical field of Jun porcelain, and in particular relates to a purple Jun porcelain glaze. Background technique [0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family with a lot of money is not as good as a piece of Jun porcelain". It is a unique national treasure porcelain in Shenhou Town, Yuzhou City, Henan Province. With its simple shape, exquisite craftsmanship, complex glaze matching, and the magical kiln transformation of "one color in the kiln, a variety of colors in the kiln", the lakes and mountains, clouds and mist, humans and animals Flowers, birds, insects, fish, etc. are known as the first of China's "Five Famous Porcelains" for their infinitely changing graphic colors and wonderful charm. [0003] Ju...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00
CPCC03C8/00
Inventor 温书强
Owner 温书强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap