Highlight anti-warping nylon PA6/PC (Polyamide 6/Polycarbonate) alloy

An anti-warping and nylon technology, applied in the field of high-gloss anti-warping nylon PA6/PC alloy, can solve the problems of non-wear-resistant surface, poor product surface, uneven product, etc., and maintain heat aging resistance and compatibility Good results

Inactive Publication Date: 2019-07-12
SUZHOU WEIRUICHENG NEW MATERIAL
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Conventional PA6 reinforced material has good rigidity effect, and generally adds 10-50% of glass fiber. Due to the arrangement of glass fiber and the shrinkage of the finished product, it is easy to cause uneven products, floating fibers on the surface of the product, and poor surface of the product, which cannot meet the use of high-demand products. At the same time, the reinforced nylon surface has poor smoothness and high density
[0005] PC (polycarbonate) is a high molecular polymer containing carbonate groups in the molecular chain. It has excellent characteristics such as good rigidity, good toughness, small shrinkage rate and stable size, but the internal stress is large, and the surface is not wear-resistant and easy to scratch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highlight anti-warping nylon PA6/PC (Polyamide 6/Polycarbonate) alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A high-gloss anti-warpage nylon PA6 / PC alloy, comprising the following components in parts by weight:

[0033] Polyamide resin (PA6) 50 parts

[0034] Polycarbonate (PC) 50 parts

[0035] Compatibilizer 15 parts

[0036] Antioxidant 1098 0.02 parts

[0037] Antioxidant 626 0.02 parts

[0038] Lubricant 0.5 part.

[0039] Specifically, the viscosity of the polyamide resin (PA6) is 2.8. Among them, the polyamide resin (PA6) is Xinhui Meida M2800.

[0040] Specifically, the viscosity of the polycarbonate (PC) is 2.8. Among them, polycarbonate (PC) is Bayer BAYER2805 of Germany.

[0041] Specifically, the compatibilizer is POE-g-MAH, PE-g-ST, PP-g-ST, ABS-g-MAH, PP-g-MAH, EVA, SEBS, SEBS-g-MAH, PE -Two or more of g-MAH. In addition, a compound compatible toughening agent can be added to reduce stress and improve dispersion. The compound compatible toughening agent is French Arkema 4700 / EEA ethylene-ethyl acrylate copolymer.

[0042] Specifically, the lubricant is ...

Embodiment 2

[0051] The difference between this embodiment and Embodiment 1 is that a high-gloss anti-warpage nylon PA6 / PC alloy includes the following components in parts by weight:

[0052] Polyamide resin (PA6) 60 parts

[0053] Polycarbonate (PC) 40 parts

[0054] 12 parts of compatibilizer

[0055] Antioxidant 1098 0.02 parts

[0056] Antioxidant 626 0.02 parts

[0057] Lubricant 0.5 parts.

[0058] The present invention also discloses a method for preparing the PA6 / PC alloy, comprising the following steps:

[0059] (1) Preparation of raw materials: In parts by weight, it includes 60 parts of polyamide resin (PA6), 40 parts of polycarbonate (PC), 12 parts of compatibilizer, 0.02 parts of antioxidant 1098, 0.02 parts of antioxidant 626, 0.5 parts of lubricant;

[0060] (2) Dry and pretreat the raw materials weighed according to the above proportions, add and blend in sequence, mix in a high-speed mixer for a total of 10 minutes, and then send them to the twin-screw extruder for m...

Embodiment 3

[0063] The difference between this embodiment and Embodiment 1 is that a high-gloss anti-warpage nylon PA6 / PC alloy includes the following components in parts by weight:

[0064] Polyamide resin (PA6) 70 parts

[0065] Polycarbonate (PC) 30 parts

[0066] Compatibilizer 10 parts

[0067] Antioxidant 1098 0.02 parts

[0068] Antioxidant 626 0.02 parts

[0069] Lubricant 0.5 parts.

[0070] The present invention also discloses a method for preparing the PA6 / PC alloy, comprising the following steps:

[0071] (1) Preparation of raw materials: In parts by weight, it includes 70 parts of polyamide resin (PA6), 30 parts of polycarbonate (PC), 10 parts of compatibilizer, 0.02 parts of antioxidant 1098, 0.02 parts of antioxidant 626, 0.5 parts of lubricant;

[0072] (2) Dry and pretreat the raw materials weighed according to the above proportions, add and blend in sequence, mix in a high-speed mixer for a total of 10 minutes, and then send them to the twin-screw extruder for meltin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a highlight anti-warping nylon PA6 / PC (Polyamide 6 / Polycarbonate) alloy which comprises the following components in parts by weight: 50-70 parts of a polyamide resin (PA6), 30-50 parts of polycarbonate (PC), 0.02-0.05 part of an antioxidant 1098, 0.02-0.05 part of an antioxidant 626 and 0.5-2 parts of a lubricant. The alloy disclosed by the invention has the characteristicsof being high in glare, smooth in surface, free of warping, stable in size, and the like, can be used as engineering plastics of structures and appearance parts of electronic appliances, electric appliances, automobiles, and the like, is prepared from safe and environmental-friendly materials, and can be widely applied to products such as structure parts and appearance parts with requirements ofhigh glare and stable sizes in fields such as household electric appliances, machinery and automobiles.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a high-gloss anti-warpage nylon PA6 / PC alloy. Background technique [0002] PA6 (polyamide resin) is also known as nylon 6; English name: Polyamide 6, abbreviated nylon 6; translucent or opaque milky white crystalline polymer, widely used in the manufacture of machinery, automobiles, chemical and electrical device parts. [0003] Conventional PA6 is used as an engineering plastic and is generally reinforced with glass fiber. The purpose is to improve the impact strength, tensile strength, flexural modulus, flexural strength, and reduce shrinkage of the material to meet industrial use. [0004] Conventional PA6 reinforced material has good rigidity effect, and generally adds 10-50% of glass fiber. Due to the arrangement of glass fiber and the shrinkage of the finished product, it is easy to cause uneven products, floating fibers on the surface of the product, and poor pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L69/00C08L51/06C08L55/02C08L23/08C08L53/02C08L51/00C08K5/20C08K5/526
CPCC08K2201/014C08L69/00C08L77/02C08L2201/08C08L2205/03C08L2205/035C08L2205/08C08L51/06C08L55/02C08L23/0853C08L53/025C08L51/006C08L23/0869C08K5/20C08K5/526
Inventor 唐强王克成李世平
Owner SUZHOU WEIRUICHENG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap