Perfumed tow rod added into heating non-combustible cigarette filter rod and preparation method thereof

A heat-not-burn and cigarette filter rod technology, which is applied in e-liquid filter elements, tobacco, and cigar manufacturing, can solve problems such as unsuitable for adding spices, poor richness, and large difference in smoking taste, so as to improve bad smoke Odor absorption, broad application prospects, and low production cost

Inactive Publication Date: 2019-09-13
CHINA TOBACCO JIANGXI IND CO LTD
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some studies have added spices to tobacco slices. Since the temperature of the tobacco slices reaches 200-400°C when heated, the flavors are prone to chemical reactions to produce peculiar smells and bad taste, and the spices are released too quickly, resulting in too much difference in flavor between the front and back sections during smoking. Big
Some studies have put spices in the filter near the lip in the form of incense sticks or explosive beads. Because the temperature is too low, it is not suitable for adding spices with a higher boiling point, and the richness is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Perfumed tow rod added into heating non-combustible cigarette filter rod and preparation method thereof
  • Perfumed tow rod added into heating non-combustible cigarette filter rod and preparation method thereof
  • Perfumed tow rod added into heating non-combustible cigarette filter rod and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A cigarette containing a flavored tow rod is prepared according to the following method, comprising the following steps:

[0030] 1) Material selection: choose a specific surface area of ​​30 ~ 35m 2 / g, the mesh number is 14-18, and the particle size is about 0.8mm, and 9 volcanic rocks are used as the base material;

[0031] 2) Fragrance: Mix ethyl maltol, oxidized isophorone, β-damascone, ethyl acetate, and vanillin in a weight ratio of 20:3:2:2:30, and add volcanic Stone granules, soaked for 48 hours to make the fragrance adsorbed, and the volcanic stone containing the fragrance was prepared, the weight of the fragrance was 2 mg, and the fragrance rate was 22.6%;

[0032] 3) Fragranced filter segment molding: prepare a section of cellulose acetate filter rod with a length of 3 cm, and add 9 fragrant volcanic stone particles evenly into the tow rod for molding;

[0033] 4) Cigarette forming: use the flavored tow rod to make a finished heat-not-burn cigarette. The c...

Embodiment 2

[0035] A cigarette containing a flavored tow rod is prepared according to the following method, comprising the following steps:

[0036] 1) Material selection: choose a specific surface area of ​​20 ~ 25m 2 / g, the mesh number is 18-20, and the particle size is about 1mm. 12 volcanic rocks are used as the base material;

[0037] 2) Fragrance: Mix ethyl maltol, isophorone oxide, β-damascone, jujube tincture, and citric acid in a weight ratio of 20:3:2:2:15, and add volcanic stone particles , soaked for 48 hours to make the fragrance adsorbed, and the volcanic stone containing fragrance was prepared, the weight of fragrance was 2 mg, and the ratio of fragrance was 22.3%;

[0038] 3) Fragranced filter segment molding: prepare a section of cellulose acetate filter rod with a length of 1 cm, and add 12 fragrant volcanic stone particles evenly into the tow rod for molding;

[0039] 4) Cigarette molding: use the flavoring filter to make a finished heat-not-burn cigarette, which con...

Embodiment 3

[0041] A cigarette containing a flavored tow rod is prepared according to the following method, comprising the following steps:

[0042] 1) Material selection: choose a specific surface area of ​​20 ~ 25m 2 / g, 12 volcanic rocks with a mesh number of 18-20 and a particle size of about 1mm are used as the base material;

[0043] 2) Fragrance: Mix ethyl maltol, macrostigmatrienone, β-damascone, and ethyl acetate in a ratio of 20:3:5:2, add volcanic stone particles, soak for 48 hours to make the fragrance Adsorption, the volcanic stone containing fragrance is prepared, the weight of fragrance is 2mg, and the ratio of fragrance is 26.4%;

[0044] 3) Fragranced tow rod section forming: prepare a cellulose acetate filter rod with a length of 2 cm, and add 12 fragrant volcanic stone particles evenly into the tow rod to form;

[0045] 4) Cigarette forming: use the flavored tow rod to make a finished heat-not-burn cigarette. The cigarette is composed of filter section, cooling sectio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a perfuming tow rod added into a heated non-combustible tobacco filter rod. The method is characterized in that a tow rod is designed at the end close to tobacco; the tow rodis positioned between the tobacco section and the cooling section; the specific surface area of the pelelith is large; the porous adsorbability is good; adsorbing tobacco flavors and fragrances and loading the tobacco flavors and fragrances into the tow rod; according to the technical scheme, essence can be continuously released in the smoking process, the bad smoking smell of smoke is improved, essence and spice with the high boiling point can be added, the low-temperature tobacco smoke is more sweet and mellow in brewing, rich in saturation and durable in fragrance, and the perfumed tow rodis simple in preparation process, high in percent of pass, low in production cost and good in stability.

Description

technical field [0001] The invention relates to the field of novel tobacco technology, in particular to a flavoring tow rod added to a filter rod of a heat-not-burn cigarette. Background technique [0002] With the continuous strengthening of tobacco control efforts by governments of various countries and people's increasing emphasis on health, in order to meet changing consumer demand in recent years, major companies at home and abroad have developed various new tobacco products that replace traditional cigarettes, especially heat-not-burn products. cigarette. Because heat-not-burn cigarettes have the unique advantages of not participating in combustion, no tar, and not as sweet and greasy as e-cigarette oil, they are popular among some consumers. However, the audience of heat-not-burn cigarettes is mainly young and middle-aged consumers who are unconventional and have a certain demand for rich cigarette styles. Therefore, when developing heat-not-burn cigarettes, the thre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A24D3/10A24D3/04A24D1/04A24D3/02
CPCA24D1/042A24D3/02A24D3/048A24D3/10
Inventor 洪玮苏加坤蔡继宝邓宇朱春晖徐达郭磊罗娟敏索卫国张晓旭倪悦
Owner CHINA TOBACCO JIANGXI IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap