A method of manufacturing metal spinning parts

A metal spinning and manufacturing method technology, applied in the field of mechanical processing, can solve the problems of serious cold work hardening of materials, large tensile stress on the outer surface, large deformation of parts, etc., to eliminate cold work hardening, improve tensile strength and Elongation, effect of grain refinement

Active Publication Date: 2020-09-11
SICHUAN AEROSPACE LONG MARCH EQUIP MFG CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the spinning forming process, the blank undergoes a large spinning deformation, the outer surface of the product is subjected to a large tensile stress, the deformation of the part is extremely large, and the material is hardened by cold work. In addition, the stress release during the spinning process makes the inner and outer parts of the product There are dense cracks on the surface. Once a large number of cracks or cracks expand and crack, the product will be scrapped directly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method of manufacturing metal spinning parts
  • A method of manufacturing metal spinning parts
  • A method of manufacturing metal spinning parts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment provides a method for manufacturing a metal spinning part, comprising the following steps:

[0030] Step 1: Use a hydraulic press to pre-stretch the O-state LD10 aluminum alloy sheet into a rod-shaped blank, and set the pressure value of the hydraulic press to 20MPa;

[0031] Step 2: After the blank is coated with lubricant, it is placed on the inter-roll spinning machine for the first spinning, the spindle speed is 20r / min, the spindle pump pressure is 10MPa, and then complete annealing treatment: first raise the temperature to 300°C, Insulate for 3 hours, then cool down with the furnace to obtain a processed product;

[0032] Step 3: Coat the primary treatment product with lubricant and place it on the inter-roll spinning machine for the second pass spinning, the spindle speed is 10r / min, and the spindle pump pressure is 15MPa; then carry out incomplete annealing treatment: first raise the temperature to 350°C, hold for 1 hour, cool down at a rate of ...

Embodiment 2

[0036] This embodiment provides a method for manufacturing a metal spinning part, comprising the following steps:

[0037] Step 1: Use a hydraulic press to pre-stretch the O-state LD10 aluminum alloy sheet into a rod-shaped blank, and set the pressure value of the hydraulic press to 20MPa;

[0038] Step 2: After the blank is coated with lubricant, it is placed on the inter-roll spinning machine for the first spinning, the spindle speed is 10r / min, the spindle pump pressure is 20MPa, and then complete annealing treatment: first raise the temperature to 320°C, Insulate for 3 hours, then cool down with the furnace to obtain a processed product;

[0039] Step 3: Coat the primary treatment product with lubricant and place it on the inter-roll spinning machine for the second spinning, the spindle speed is 5r / min, the spindle pump pressure is 30MPa; first perform incomplete annealing treatment, and heat up to 370 ℃, keep warm for 1h, then lower the temperature at a rate of 50°C / h, t...

Embodiment 3

[0043] This embodiment provides a method for manufacturing a metal spinning part, comprising the following steps:

[0044] Step 1: Use a hydraulic press to pre-stretch the O-state LD10 aluminum alloy sheet into a rod-shaped blank, and set the pressure value of the hydraulic press to 20MPa;

[0045] Step 2: After the blank is coated with lubricant, it is placed on the inter-roller spinning machine for the first spinning, the spindle speed is r / min, the spindle pump pressure is 20MPa, and then complete annealing treatment: first raise the temperature to 250°C, Keep warm for 8 hours, then cool down with the furnace to obtain a primary treatment product;

[0046] Step 3: Apply lubricant to the primary treatment product and place it on the inter-roll spinning machine for the second pass spinning, the spindle speed is 10r / min, the spindle pump pressure is 20MPa; first perform incomplete annealing treatment, and heat up to 250 ℃, keep warm for 10h, then lower the temperature at a ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a manufacturing method of a metal spinning part. The manufacturing method of metal spinning parts comprises the following steps of 1, prestretching a metal raw material into a pie blank; 2, conducting first-pass spinning on the blank and then conducting complete annealing treatment on the blank to obtain a primary treated product; 3, conducting second-pass spinning on the primary treated product and then conducting incomplete annealing and quenching treatment to obtain a secondary treated product; and 4, conducting third-pass spinning on the secondary treated product andthen conducting quenching and aging treatment to obtain the metal spinning part. Through the manufacturing method, the crack sensitive rate of products can be eliminated or substantially reduced; thephenomena of surface cracking of spinning products manufactured through the method can be reduced by 90% or more; and the situation that the products are subjected to cold hardening in the spinning process badly, the crack depth of the outer surface of the spinning part is increased and the spinning part gets cracked and is scrapped is avoided.

Description

technical field [0001] The invention belongs to the technical field of mechanical processing, and in particular relates to a process suitable for eliminating or greatly reducing surface cracks of metal spinning parts. Background technique [0002] In the fields of national defense, aviation and aerospace, a large number of LD10 aluminum alloy sheets are used to manufacture important structural products. As an important structural part of a certain type, the head sheet metal parts are made of LD10 aluminum alloy sheets. The blank is processed into a head part. During the spinning forming process, the blank undergoes a large spinning deformation, the outer surface of the product is subjected to a large tensile stress, the deformation of the part is extremely large, and the material is hardened by cold work. In addition, the stress release during the spinning process makes the inner and outer parts of the product Intensive cracks appear on the surface. Once a large number of c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/04
CPCC22F1/002C22F1/04
Inventor 陶明清王子立王春林王凤婷田晔许璐迪
Owner SICHUAN AEROSPACE LONG MARCH EQUIP MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap