Polyester elastomer-based neck hanging line shaping material as well as preparation method and application thereof

A polyester elastomer and polyolefin elastomer technology, which is applied in the field of hanger thread setting material and its preparation, can solve the problems of high impact strength, easy breakage of the hanger thread, and high breaking strength, and achieves hard yellowing and light suppression. Aging degradation, improve the effect of uniform dispersion

Active Publication Date: 2020-11-17
东莞市鼎誉新材料有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problems in the prior art that the hanging neck thread is easy to break and has low resilience, the first purpose of the present invention is to provide a polyester elastomer hanging neck thread setting material, and the polyester elastomer hanging neck thread The shaping material has good resilience, is not easy to deform, and has high breaking strength, high impact strength, and is not easy to break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester elastomer-based neck hanging line shaping material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A kind of hanging neck thread setting material based on polyester elastomer, said hanging neck thread setting material is made of raw materials comprising the following parts by weight:

[0055] Polyester elastomer 50 parts

[0056] TPU 15 parts

[0057] 10 parts polyolefin elastomer

[0058] Compatibilizer 3 parts

[0059] Lubricant 1 part

[0060] Auxiliary 3 parts.

[0061] The polyester elastomer is selected from American DuPont 4069 brand thermoplastic polyester elastomer.

[0062] The polyolefin elastomer is selected from American DuPont 8200 brand polyolefin elastomer.

[0063] The compatibilizer is GMA-g-PE.

[0064] Described lubricant is methyl ethoxy silicone oil.

[0065] Each part of said auxiliary agent includes 2 parts of antioxidant and 1 part of anti-UV agent; said antioxidant is 1,3,5-three (3,5-di-tert-butyl-4-hydroxyphenyl) isocyanate; said The anti-UV agent is light stabilizer 770.

[0066] A method for preparing a polyester elastomer-based...

Embodiment 2

[0069] A kind of hanging neck thread setting material based on polyester elastomer, said hanging neck thread setting material is made of raw materials comprising the following parts by weight:

[0070] Polyester elastomer 55 parts

[0071] TPU 18 parts

[0072] Polyolefin elastomer 14 parts

[0073] 3.5 parts of compatibilizer

[0074] Lubricant 1.5 parts

[0075] Auxiliary 3.2 parts.

[0076] The polyester elastomer is selected from American DuPont 4069 brand thermoplastic polyester elastomer.

[0077] The polyolefin elastomer is selected from American DuPont 8200 brand polyolefin elastomer.

[0078] The compatibilizer is GMA-g-PP.

[0079] The lubricant is ethyl silicone oil.

[0080] Each part of said auxiliary agent includes 2.2 parts of antioxidant and 1.2 parts of anti-UV agent; said antioxidant is pentaerythritol bis-diphosphite bis (2,4-di-tert-butylphenyl) ester; said anti-UV agent is Light stabilizer 622.

[0081] A method for preparing a polyester elastomer...

Embodiment 3

[0084] A kind of hanging neck thread setting material based on polyester elastomer, said hanging neck thread setting material is made of raw materials comprising the following parts by weight:

[0085] Polyester elastomer 60 parts

[0086] TPU 20 parts

[0087] Polyolefin elastomer 18 parts

[0088] Compatibilizer 4 parts

[0089] Lubricant 2 parts

[0090] Auxiliary 3.5 parts.

[0091] The polyester elastomer is selected from American DuPont 4069 brand thermoplastic polyester elastomer.

[0092] The polyolefin elastomer is selected from American DuPont 8200 brand polyolefin elastomer.

[0093] The compatibilizer is SEBS-g-MAH.

[0094] Described lubricant is benzyl silicone oil.

[0095] Each part of the auxiliary agent includes 2.5 parts of antioxidant and 1.5 parts of anti-UV agent; the antioxidant is N, N'-hexamethylene bis (3, 5-di-tert-butyl-4-hydroxyphenylpropanamide) ; The anti-UV agent is ultraviolet absorber UV-327.

[0096] A method for preparing a polyester ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of polymer materials, in particular to a polyester elastomer-based neck hanging line shaping material as well as a preparation method and application thereof. The material is prepared from the following raw materials in parts by weight: 50-70 parts of polyester elastomer, 15-25 parts of TPU, 10-25 parts of polyolefin elastomer, 3-5 parts of a compatilizer, 1-3 parts of a lubricant and 3-4 parts of an assistant. According to the material, the TPU and the polyolefin elastomer are introduced for polymerization, the compatibility of the materials is improved under the action of the compatilizer, the flexibility and toughness of the shaping material are improved by introducing the TPU, and the resilience and impact resistance of the shaping material are improved by combining the polyolefin elastomer; and the shaping material prepared after polymerization can be prepared and molded in a low-temperature environment, so that the preparation difficulty and theenergy consumption cost are reduced, and the product is good in rebound resilience, not liable to deform, high in breaking strength, high in impact strength and not liable to break.

Description

technical field [0001] The invention relates to the field of polymer materials, more specifically, it relates to a polyester elastomer-based hanging neck thread setting material and its preparation method and application. Background technique [0002] The existing earphones are divided into wired and wireless. The two wired earphones are connected by a cable; The connection of the transmitting device requires two separate earphones to be equipped with a Bluetooth unit and an independent battery, but the technology is difficult, the cost is high, and it is easy to drop a single earphone, so that the entire pair of earphones cannot be used in pairs. In this regard, in order to achieve a better wearing effect, the current wireless Bluetooth headset generally adopts a hanging neck structure to improve its stable connection structure and avoid falling; but in actual use, the connection between the hanging neck line and the headset is easy Fracture will affect the service life of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/00C08L75/04C08L23/02C08L51/06C08L83/04C08K13/06C08K9/10C08K9/04C08K3/34C08K3/36C08K5/29C08K5/3435H04R1/10
CPCC08L67/00H04R1/10C08L2207/04C08L2205/08C08L2205/035C08L75/04C08L23/02C08L51/06C08L83/04C08K13/06C08K9/10C08K9/04C08K3/34C08K3/36C08K5/29C08K5/3435
Inventor 龚勋
Owner 东莞市鼎誉新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com