A kind of preparation method of worm-like precipitated calcium carbonate

A precipitated calcium carbonate, worm-like technology, applied in the direction of calcium carbonate/strontium/barium, chemical instruments and methods, calcium/strontium/barium compounds, etc., to achieve the effect of high specific surface area, high purity and low price

Active Publication Date: 2022-03-29
ANHUI PROVINCE XUNCHENG CITY HUANA NEW MATERIAL TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the morphology prepared by this method is calcite chain, not worm-like calcium carbonate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of worm-like precipitated calcium carbonate
  • A kind of preparation method of worm-like precipitated calcium carbonate
  • A kind of preparation method of worm-like precipitated calcium carbonate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A preparation method for worm-like precipitated calcium carbonate, comprising the steps of:

[0033] (1) After the quicklime is digested and reacted, the obtained milk of lime is adjusted to a specific gravity of 1.050 to obtain a calcium hydroxide suspension;

[0034] (2) Take 15 kg of calcium hydroxide suspension, add 0.1 mol magnesium chloride and 0.2 mol strontium chloride to it, make a solution with a molar concentration of cations of 1 mol / L as a crystal form control agent, stir and mix evenly, and then add the carbonization tower, Control the stirring rate to 20Hz, the carbonization start temperature is 21.0°C, pass a mixed gas of carbon dioxide with a concentration of 30% into the suspension, and the flow rate is 2.0m 3 / h until the pH drops to 9.0 to stop carbonation and obtain a PCC suspension;

[0035] (3) Add a phosphoric acid solution with a mass concentration of 5% to the PCC suspension at a rate of 220ml / min until the pH drops to 7.0, stop the reaction, ...

Embodiment 2

[0038] A preparation method for worm-like precipitated calcium carbonate, comprising the steps of:

[0039] (1) After the quicklime is digested and reacted, the obtained milk of lime is adjusted to a specific gravity of 1.060 to obtain a calcium hydroxide suspension;

[0040](2) Take 15 kg of calcium hydroxide suspension, add 0.3 mol of magnesium oxide to it, make a solution with a concentration of 3 mol / L as a crystal form control agent, stir and mix evenly, then add to the carbonization tower, control the stirring rate to 20 Hz, and carbonize The initial temperature is 23.0°C, and a mixed gas of carbon dioxide with a concentration of 31% is introduced into the suspension with a flow rate of 2.0m 3 / h until the pH drops to 9.0 to stop carbonation and obtain a PCC suspension;

[0041] (3) Add a phosphoric acid solution with a mass concentration of 5% to the PCC suspension at a rate of 250ml / min until the pH drops to 7.0, terminate the reaction, let it stand for 20 minutes, an...

Embodiment 3

[0044] A preparation method for worm-like precipitated calcium carbonate, comprising the steps of:

[0045] (1) After the quicklime is digested, the milk of lime obtained is adjusted to a specific gravity of 1.065 to obtain a calcium hydroxide suspension;

[0046] (2) Take 15kg of calcium hydroxide suspension, add 0.4mol magnesium bicarbonate and 0.1mol barium chloride to it, make a solution with a cation concentration of 5mol / L as a crystal form control agent, stir and mix evenly, and then add to the carbonization tower , the stirring rate is controlled at 20Hz, the carbonization start temperature is 24°C, and a mixed gas of carbon dioxide with a concentration of 33% is passed into the suspension with a flow rate of 2.2m 3 / h until the pH drops to 9.0 to stop carbonation and obtain a PCC suspension;

[0047] (3) Add a phosphoric acid solution with a mass concentration of 5% to the PCC suspension at a rate of 280ml / min until the pH drops to 7.0, stop the reaction, let it stan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of worm-like precipitated calcium carbonate, which comprises the steps of digesting quicklime and adjusting the specific gravity to obtain a calcium hydroxide suspension; adding magnesium, strontium or barium element salts or their compounds into the suspension as a crystal form Control agent, stir and mix evenly, then add to the carbonization tower, pass through the mixed gas containing carbon dioxide to carry out calcium carbonate reaction, until the pH drops to 9.0 to stop carbonation, and obtain PCC suspension; slowly add phosphoric acid solution to the PCC suspension, Until the pH drops to 7.0, stop the reaction, let it stand, and then filter the suspension according to the conventional method, dry, pulverize, and classify to obtain worm-like precipitated calcium carbonate powder. In this method, by adding magnesium, strontium or barium element salts or their compounds as crystal form control agents, the end point of the reaction is controlled, and the final pH is adjusted with phosphoric acid. The obtained worm-like precipitated calcium carbonate has high purity, high whiteness, and specific surface area. Advanced advantages.

Description

technical field [0001] The invention belongs to the technical field of inorganic materials, in particular to a preparation method of worm-like precipitated calcium carbonate. Background technique [0002] Calcium carbonate, as a green and environmentally friendly inorganic material, has a wide range of uses. Due to the low cost of obtaining calcium carbonate raw materials, the production cost and related technologies are relatively mature. Secondly, calcium carbonate as a filler can improve the mechanical properties, appearance and structure adjustment of products, and greatly reduce the cost of products. It can be used in rubber, plastic, papermaking , ink, plastic and other fields. Calcium carbonate is used in coatings, sealants, etc. Well-dispersed calcium carbonate particles can form a good space site structure and improve the anti-sagging performance and mechanical properties of products, which is of great significance in automotive coatings and construction adhesives....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01F11/18
CPCC01F11/182C01P2004/03C01P2006/12C01P2006/80C01P2006/60
Inventor 李仁才朱勇文庆福杨爱梅廖海才马建堂
Owner ANHUI PROVINCE XUNCHENG CITY HUANA NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap