A technology of sodium alginate and fire extinguishing agent, which is applied in the direction of fire prevention equipment, etc.

Active Publication Date: 2021-07-06
GUANGDONG RONGQIAOTAI NEW MATERIALS TECH CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a kind of ready-to-mix sodium alginate hydrogel fire extinguishing agent and preparation method thereof, to solve the problems in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ready-to-prepare sodium alginate hydrogel fire extinguishing agent
  • Ready-to-prepare sodium alginate hydrogel fire extinguishing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] S1: Prepare materials:

[0046] Weigh 2-acrylamide-2-methylpropanesulfonic acid, dispersant, cyclohexane, chitosan, ammonium dihydrogen phosphate, ammonium sulfate, additives, white carbon black and fluorocarbon surfactant in proportion, and set aside ;

[0047] Weigh sodium alginate, acrylic acid, N-isopropylacrylamide, N,N-methylenebisacrylamide, sodium acrylate, attapulgite, ammonium persulfate, tetramethylethylenediamine, and the second additive in proportion , Calcium chloride, Calcium nitrate and Calcium carbonate, spare.

[0048] : Prepare the filler:

[0049] Take ammonium dihydrogen phosphate, ammonium sulfate and additives, stir for 10 minutes, and then add them to a supersonic jet mill for pulverization. The pulverization time is 10 minutes to obtain superfine material A; take white carbon black, add it to a supersonic jet mill, and pulverize it. The pulverization time is 10min, and the superfine material B is obtained;

[0050] Take ultra-fine material A...

Embodiment 2

[0058] S1: Prepare materials:

[0059] Weigh 2-acrylamide-2-methylpropanesulfonic acid, dispersant, cyclohexane, chitosan, ammonium dihydrogen phosphate, ammonium sulfate, additives, white carbon black and fluorocarbon surfactant in proportion, and set aside ;

[0060] Weigh sodium alginate, acrylic acid, N-isopropylacrylamide, N,N-methylenebisacrylamide, sodium acrylate, attapulgite, ammonium persulfate, tetramethylethylenediamine, and the second additive in proportion , Calcium chloride, Calcium nitrate and Calcium carbonate, spare.

[0061] : Prepare the filler:

[0062] Take ammonium dihydrogen phosphate, ammonium sulfate and additives, stir for 13 minutes, and then add them to a supersonic airflow mill for pulverization. The pulverization time is 15 minutes to obtain superfine material A; The pulverization time is 15min, and the superfine material B is obtained;

[0063] Take ultra-fine material A and ultra-fine material B, stir and heat up to 42°C, then add fluorocar...

Embodiment 3

[0071] S1: Prepare materials:

[0072] Weigh 2-acrylamide-2-methylpropanesulfonic acid, dispersant, cyclohexane, chitosan, ammonium dihydrogen phosphate, ammonium sulfate, additives, white carbon black and fluorocarbon surfactant in proportion, and set aside ;

[0073]Weigh sodium alginate, acrylic acid, N-isopropylacrylamide, N,N-methylenebisacrylamide, sodium acrylate, attapulgite, ammonium persulfate, tetramethylethylenediamine, and the second additive in proportion , Calcium chloride, Calcium nitrate and Calcium carbonate, spare.

[0074] : Prepare the filler:

[0075] Take ammonium dihydrogen phosphate, ammonium sulfate and additives, stir for 15 minutes, and then add them to a supersonic jet mill for pulverization. The pulverization time is 20 minutes to obtain superfine material A; take white carbon black, add it to a supersonic jet mill, and pulverize it. The crushing time is 25min to obtain superfine material B;

[0076] Take ultra-fine material A and ultra-fine m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a ready-to-prepare sodium alginate hydrogel fire extinguishing agent which comprises modified sodium alginate hydrogel, filler and water-absorbent resin, the filler comprises a first additive, a second additive and a third additive, and the first additive is a conventional dry powder fire extinguishing agent and comprises ammonium dihydrogen phosphate, ammonium sulfate, auxiliaries and other materials. When the first additive is prepared, firstly, main materials such as ammonium dihydrogen phosphate and ammonium sulfate are crushed by a supersonic jet mill to obtain superfine mixed powder, and the mixed powder is fine in particle size, narrow in particle size distribution, high in overall surface activity and convenient for subsequent modification; according to the ready-to-prepare sodium alginate hydrogel fire extinguishing agent and the preparation method thereof, the component design is reasonable, the process operation is simple, preparation of the sodium alginate hydrogel fire extinguishing agent can be achieved, and the fire extinguishing agent is excellent in fire extinguishing performance and has high practicability.

Description

technical field [0001] The invention relates to the technical field of fire extinguishing agents, in particular to a ready-to-mix sodium alginate hydrogel fire extinguishing agent. Background technique [0002] Among various disasters, fire is one of the main disasters that most often and commonly threatens public safety and social development, and when a fire occurs, fire extinguishers are our common fire fighting and rescue equipment. [0003] Among the existing fire extinguishing agents on the market, the most common fire extinguishing agents are water fire extinguishing agent, dry powder fire extinguishing agent, foam fire extinguishing agent, carbon dioxide fire extinguishing agent, haloalkane fire extinguishing agent, with the progress and development of science and technology, hydrogel fire extinguishing agent gradually entered Our sight, but the existing hydrogel fire extinguishing agent has poor mechanical strength, and it is easy to break through the covering layer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A62D1/00C08F251/00C08F220/06C08F220/54C08F222/38C08F220/58
CPCA62D1/0064C08F251/00C08F220/06C08F220/54C08F222/385C08F220/585
Inventor 不公告发明人
Owner GUANGDONG RONGQIAOTAI NEW MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap