Diamond gel highlight and preparation method thereof

A technology of jelly and diamond, which is applied in the field of diamond jelly highlights and its preparation. It can solve the problems of low smoothness, stickiness, and poor use feeling, and achieve the effect of enhancing smoothness, reducing stickiness, and improving use feeling.

Active Publication Date: 2021-11-26
JOTM DAILY CHEM HANGZHOU CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Through the above-mentioned related technologies, but the current diamond jelly highlight is a liquid highlight, which contains more ester emollients. Compared with powder and paste highlights, it is more sticky during use, resulting in a less silky feeling and a smoother feeling of use. poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diamond gel highlight and preparation method thereof
  • Diamond gel highlight and preparation method thereof
  • Diamond gel highlight and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] Embodiment 1: a kind of diamond jelly high light, the specific components and weight included are as shown in table 1, made by the following steps: S1: polymethylsilsesquioxane, polydimethylsiloxane, Phenyl polytrimethicone and the second emollient are mixed, the temperature is controlled at 80°C during the mixing process, and the stirring speed is 500r / min during the mixing process, and the first mixture is obtained after stirring evenly;

[0060] S2: Mix and stir the first emollient, the first skin conditioning agent and the second skin conditioning agent at a stirring speed of 800 r / min, and obtain the second mixture after stirring evenly;

[0061] S3: first cool down the first mixture to 50°C, and the cooling rate is 4°C / min; then add the second mixture to the first mixture, stir during the mixing process, and add pearlescent agent, adhesive, and preservative after stirring evenly , continue to stir, and homogenize for 30 minutes after stirring evenly to obtain a di...

Embodiment 2-3

[0062] Embodiment 2-3: A diamond jelly highlight, the difference from Example 1 is that the control temperature in step S1 is 60°C, the homogenization time in step S3 is 10min, and the specific components and weights are different at the same time, the specific components included Components and weight are shown in Table 1.

Embodiment 4-5

[0063] Embodiment 4-5: a kind of diamond jelly highlight, the difference with embodiment 1 is that the second emollient has different components and weight, and the specific components and weight included are as shown in table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of cosmetics, and particularly discloses diamond gel highlight and a preparation method thereof. The diamond gel highlight is prepared from the following components in percentage by weight: 38%-45% of polymethylsilsesquioxane, 4.5%-6% of polydimethylsiloxane, 8.5%-10% of phenyl polytrimethylsiloxane, 19%-22% of a pearling agent, 2%-4% of a first softening and moistening agent, 3.5%-5% of a second softening and moistening agent, 10%-14% of a first skin conditioner, 2%-5% of a second skin conditioner, 1.8%-2% of an adhesive and 0.5%-0.8% of a preservative; and the first softening and moistening agent is prepared from the following components in percentage by weight: 40%-60% of neopentyl glycol dicaprate, 20%-40% of aloe extract and the balance of fructus forsythiae extract. The preparation method comprises the following steps that the siloxane raw material and the second softening and moistening agent are uniformly mixed to obtain a first mixture; the first softening and moistening agent, the first skin conditioning agent and the second skin conditioning agent are uniformly mixed to obtain a second mixture; and the second mixture is added into the first mixture for being uniformly mixed, other raw materials are added, and uniformly mixing is carried out to obtain the diamond gel highlight. The diamond gel highlight has a relatively good soft and smooth feeling.

Description

technical field [0001] The invention relates to the technical field of cosmetics, in particular to a diamond jelly highlighter and a preparation method thereof. Background technique [0002] At present, high light usually refers to high light cosmetics such as high light powder. Highlighting powder uses the diffuse scattering of light to modify small flaws on the face, making the skin appear shiny and shaping the three-dimensional effect of the face. [0003] At present, the highlights on the market mainly include powder highlights, paste highlights and liquid highlights. Powder highlights and cream highlights are more common, but their durability is worse than liquid highlights, and people are gradually using liquid highlights for makeup. Diamond jelly highlighter refers to a glossy, translucent liquid highlighter, mainly composed of emollients, pearlescent agents, colorants and other raw materials; diamond jelly highlighter has a good moisturizing effect and long-lasting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/891A61K8/37A61K8/9789A61K8/9794A61K8/9728A61K8/88A61K8/44A61Q19/00A61Q1/12A61P29/00A61P17/10
CPCA61K8/891A61K8/37A61K8/9794A61K8/9789A61Q19/00A61Q1/12A61P29/00A61P17/10A61K8/44A61K8/88A61K8/9728A61K8/73A61K2800/5922
Inventor 姚增辉从云玲
Owner JOTM DAILY CHEM HANGZHOU CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap