Antibacterial deodorant pet urinal mat and producing method thereof

A manufacturing method and technology of urine pads, which are applied in the field of pet urine pads, can solve problems such as poor stability and durability, pets are easy to cause injury, and single function, and achieve good stability and durability, outstanding antibacterial and deodorizing effects, and healthy The effect of living environment

CN108432642AInactive Publication Date: 2018-08-24南京凯创协同纳米技术有限公司
5 Cites 2 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2018-08-24
Estimated Expiration
Not applicable · inactive patent
Patent Text Reader

Abstract

The invention relates to an antibacterial deodorant pet urinal mat and a producing method thereof. An oxidation agent, an organic iron catalyst, an antibacterial agent and an adsorption agent are mixed according to proportions, and then subjected to homogenization and curing treatment, an antibacterial deodorant agent is obtained after grinding the mixture, the antibacterial deodorant agent is added into high-absorptivity resin, then laminated with wood pulp and toilet paper in order, the antibacterial deodorant pet urinal mat is produced by covering the product with a surface layer of non-woven fabrics and PE (poly ethylene) film bottom cloth. The antibacterial deodorant pet urinal mat has outstanding antibacterial and deodorant effects, good stability and durability and good product dispersing effect, and the processing technology is simple and convenient.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The present invention relates to pet pee pads; more particularly, the present invention relates to antibacterial and deodorizing pet pee pads. In addition, the present invention also relates to a manufacturing method of the pet urine pad. Background technique

[0002] At present, with the enrichment and satisfaction of people's material life, more and more people are pursuing spiritual sustenance, and pets just fill our spiritual dependence and comfort. Some psychiatrists also pointed out that pets are good for human mental health and play an irreplaceable role for human beings. However, with the advent of summer, under the humidity and high temperature, the smell of pets becomes more intense and prominent, and many pet owners are annoyed by the unpleasant and irritating smell brought by pets. And there are many smells that are extremely difficult to get rid of. After washing with soap, washing powder, detergent, etc., the unpleasant smell came out n...

Examples

Embodiment 1

[0024] Follow the steps below to make an antibacterial and deodorant pet pee mat:

[0025] (1) Weigh 0.5 parts by mass of sodium ferrate, 0.5 parts by mass of ferric citrate, 1 part by mass of zinc gluconate, and 1 part by mass of humic acid. After homogenization and solidification, grind to 80 mesh to obtain antibacterial and deodorant Agent A;

[0026] (2) Add 0.2 parts by mass of antibacterial deodorant A to 100 parts by mass of sodium polyacrylate resin, and mix well to obtain mixture B;

[0027] (3) Press the mixture B with wood pulp and toilet paper in order to obtain the absorption layer C;

[0028] (4) The upper and lower sides of the absorbent layer C are respectively covered with a non-woven surface layer and a PE film base cloth to prepare an antibacterial and deodorant pet urine pad.

[0029] The antibacterial and deodorizing effects of the thus obtained antibacterial and deodorant pet urine pads are tested as follows:

[0030] Both the ordinary urine pad and th...

Embodiment 2

[0032] (1) Weigh 1.0 parts by mass of sodium bismuthate, 1.0 parts by mass of iron acetylacetonate, 1.5 parts by mass of nano-zinc, and 2.5 parts by mass of white carbon black, homogenize and solidify, grind to 60 mesh, and obtain an antibacterial deodorant A;

[0033] (2) Add 0.2 parts by mass of antibacterial deodorant A to 100 parts by mass of sodium polyacrylate resin, and mix well to obtain mixture B;

[0034] (3) Press the mixture B with wood pulp and toilet paper in order to obtain the absorption layer C;

[0035] (4) The upper and lower sides of the absorbent layer C are respectively covered with a non-woven surface layer and a PE film base cloth to prepare an antibacterial and deodorant pet urine pad.

[0036] The antibacterial and deodorizing effects of the thus obtained antibacterial and deodorant pet urine pads are tested as follows:

[0037] Both the ordinary urine pad and the antibacterial and deodorizing urine pad of the present invention are made into a size ...

Embodiment 3

[0039] (1) Weigh 1.0 parts by mass of sodium bismuthate, 1.0 parts by mass of iron acetylacetonate, 2 parts by mass of basic zinc chloride, and 2 parts by mass of attapulgite, homogenize and solidify, and grind to 20 mesh to obtain antibacterial Deodorant A;

[0040] (2) Add 2.5 parts by mass of antibacterial deodorant A to 100 parts by mass of sodium polyacrylate resin, and mix well to obtain mixture B;

[0041] (3) Press the mixture B with wood pulp and toilet paper in order to obtain the absorption layer C;

[0042] (4) The upper and lower sides of the absorbent layer C are respectively covered with a non-woven surface layer and a PE film base cloth to prepare an antibacterial and deodorant pet urine pad.

[0043] The antibacterial and deodorizing effects of the thus obtained antibacterial and deodorant pet urine pads are tested as follows:

[0044] Both the ordinary urine pad and the antibacterial and deodorizing urine pad of the present invention are made into a size of...