Nicuzn based ferrite and electronic component using the same

A technology of electronic components and ferrite, applied to electrical components, inductors with magnetic cores, circuits, etc., can solve problems such as improving DC superposition characteristics and not disclosing the composition of the invention

Active Publication Date: 2009-09-23
TDK CORPARATION
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the purpose of the technology disclosed in the publication is not to improve the DC superposition characteristics, and the composition of the present invention is not disclosed in the specific examples of the publication.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nicuzn based ferrite and electronic component using the same
  • Nicuzn based ferrite and electronic component using the same
  • Nicuzn based ferrite and electronic component using the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Hereinafter, the NiCuZn-based ferrite (oxide magnetic material) of the present invention will be described in detail.

[0015] For the substantial main component in the NiCuZn system ferrite of the present invention contains: Fe 2 o 3 Contains 45.0-49.0 mol% of iron oxide (especially preferably 47.0-48.8 mol%); 5.0-14.0 mol% of copper oxide as CuO (especially 7.0-12 mol%); 1.0-32.0 mol of zinc oxide as ZnO % (particularly preferably 14.0 to 28.0 mol%); NiO contains nickel oxide as the balance mol%.

[0016] Furthermore, in the NiCuZn-based ferrite of the present invention, with respect to the main component, as a subcomponent, Bi 2 o 3 Calculated, bismuth oxide is greater than 0.25% by weight, 0.40% by weight or less (especially preferably 0.26~0.33% by weight); 2 In total, tin oxide is 1.00 to 2.50% by weight (especially preferably 1.00 to 2.20% by weight).

[0017] For the composition range of the above-mentioned main components, if iron oxide (Fe 2 o 3 ) conte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is a NiCuZn series ferrite, which contains the following main components: 45.0-49.0 mol% of iron oxide in terms of Fe2O3; 5.0-14.0 mol% of copper oxide in terms of CuO; 1.0-32.0 mol% of zinc oxide in terms of ZnO %; in terms of NiO, nickel oxide is the balance mole %, relative to the main component, it also contains: in terms of Bi2O3, 0.25 to 0.40% by weight of bismuth oxide (excluding 0.25% by weight); in terms of SnO2, oxide 1.00 to 2.50% by weight of tin, so that the DC superposition characteristics can be greatly improved.

Description

technical field [0001] The present invention relates to a NiCuZn-based ferrite, and an electronic component manufactured using the same. In particular, it relates to a ferrite used as a material of an electronic component forming a closed magnetic circuit, and an electronic component manufactured using the same. Background technique [0002] So far, ferrite, as a magnetic material containing oxides such as Ni, Cu, and Zn, has been used as a core (magnetic core) material for various electronic components, or a laminated chip inductor, etc., due to its excellent magnetic properties. Materials for inductor parts, etc. [0003] Considering that this magnetic core or inductor component will be used in various temperature environments, it is required that the rate of change of the initial magnetic permeability μi relative to the temperature change is small, that is, the temperature characteristic of the initial magnetic permeability μi is good (relative to the temperature little ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/34C04B35/30H01F17/00
CPCH01F17/04C04B2235/3281C04B35/62655C04B2235/3284C04B2235/3279H01F1/344C04B2235/656C04B2235/3293C04B35/62685C04B35/265C04B2235/3298C04B35/63416C04B35/26
Inventor 和田龙一青木卓也桃井博高桥幸雄佐藤高弘
Owner TDK CORPARATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com