Thick armor plate with high tension and method for manufacturing the same

A thick steel plate, high tension technology, applied in the direction of manufacturing tools, heat treatment process control, furnace type, etc., to achieve the effect of reducing the fracture area, preventing fracture opening, and improving toughness

Inactive Publication Date: 2009-12-09
KOBE STEEL LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, according to the methods described in Patent Document 3 and Patent Document 4, only about 15% of the uniform elongation can be obtained, and further improvement of the uniform elongation is required in order to adapt to ships.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thick armor plate with high tension and method for manufacturing the same
  • Thick armor plate with high tension and method for manufacturing the same
  • Thick armor plate with high tension and method for manufacturing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0105] The steel obtained by smelting in a small vacuum furnace and having the composition shown in Table 1 below (the balance is Fe and unavoidable impurities) was heated at 1100° C. for 30 minutes to form an austenite single phase, and then hot rolled. The final rolling temperature was 800°C, and the final plate thickness was 12.5 mm.

[0106] The obtained hot-rolled material was cooled under the conditions shown in Table 2 below using water cooling equipment and a heat treatment furnace. In Table 2, T1~T4, t1~t2, R1~R3 are related to the aforementioned figure 1 Corresponds to the number above.

[0107] After cooling to the slow cooling end temperature T4, it was air-cooled to room temperature, and a thick steel plate (thickness 12.5 mm) was produced.

[0108] Measure the microstructure [ferrite fraction, residual γ fraction, C content in residual γ] and base metal properties [yield point (YP), tensile strength (TS)] of the obtained thick steel plate according to the follo...

Embodiment 2

[0138] The steel obtained by smelting in a small vacuum furnace with the composition shown in the following Table 5 or Table 6 (the balance is Fe and unavoidable impurities) was heated at 1100° C. for 30 minutes to form an austenite single phase and then hot rolled. The final rolling temperature was 800°C, and the final plate thickness was 12.5 mm. In the following Table 5 or Table 6, use the following formula (1) to calculate the value of “[N]-0.292×[Ti]” according to the composition of the steel, and “(14 / 10.8)×([B]-0.0003 )" and display the value.

[0139] The obtained hot-rolled material was cooled under the conditions shown in Table 7 below using water cooling equipment and a heat treatment furnace. In Table 7, T1~T4, t1~t2, R1~R3 are related to the aforementioned figure 1 Corresponds to the number above.

[0140] After cooling to the slow cooling end temperature T4, it was air-cooled to room temperature, and a thick steel plate (thickness 12.5 mm) was produced.

[01...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A high-tensile thick steel plate characterized by containing, in mass %: C: 0.02-0.20%, Si: 0.2-0.5%, Mn: 1-1.8%, Cu and / or Ni: 0.2-1% in total , the balance is Fe and unavoidable impurities, and the ferrite fraction: 80% by volume or more, the retained austenite fraction: 1% by volume or more, and the amount of C in the retained austenite is 0.80~ 1.10% by mass.

Description

technical field [0001] The present invention relates to a thick steel plate used for large structures such as ships and a method of manufacturing the same, and more particularly to a thick steel plate with a strength of 490 MPa or more and less than 590 MPa (hereinafter referred to as 490 MPa grade) and a thickness of about 5 mm or more. Background technique [0002] If ships collide with each other or run aground, the ship will break and open, water will seep and sink, and cargo and fuel will flow out of the ship, causing marine pollution, which has become a social problem. Therefore, various steel plates for ship hulls have been proposed which can absorb the impact energy received by the ship hull and prevent the disadvantages caused by the destruction of the ship hull when ships collide with each other or when the ship runs aground. [0003] As a steel plate for ship hulls excellent in such impact absorbing performance, Patent Document 1 proposes a steel plate that contai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/16C22C38/08C22C38/14C22C38/12C22C38/20C22C38/40C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50C21D9/46C21D11/00
Inventor 村上俊夫冈崎喜臣田村荣一
Owner KOBE STEEL LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com