Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

White waterborne wood base coat for medium density fiberboard and preparation technology thereof

A technology of white primer and MDF, applied in coating and other directions, to achieve the effect of improving utilization rate, reducing environmental pollution and good appearance effect

Inactive Publication Date: 2013-01-16
ZHEJIANG FEIDA ZHONGKE FINE CHEM
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing water-based wood white primers have great defects on the cross-section edge sealing of MDF

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] Density board edge banding water-based wood white primer is composed of slurry, resin and additives, the slurry includes water, dispersant, slurry wetting agent, slurry defoamer, titanium dioxide, kaolin, heavy calcium and Talcum powder, described auxiliary agent comprises lauryl alcohol ester, dipropylene glycol methyl ether, defoamer, wetting agent, leveling agent and thickener, and the mass percent of described each component in white primer is: water : 7.3%; Dispersant: 0.5%; Slurry wetting agent: 0.4%; Slurry defoamer: 0.4%; Titanium dioxide: 20.7%; Kaolin: 7.7%; Heavy calcium: 7.7%; Talc powder: 11% ; Resin: 38.0%; Lauryl alcohol ester: 2.3%; Dipropylene glycol methyl ether: 2.3%; Defoamer: 0.4%; Wetting agent: 0.4%;

[0073] The dispersant uses Shenzhen Haichuan Industrial Co., Ltd. Hydropatat5040 main component: sodium polycarboxylate, the slurry wetting agent uses TG from Air Products Company, and the slurry defoamer uses Degussa Tego Airex902w. Main component:...

Embodiment 2

[0093] Density board edge banding water-based wood white primer is composed of slurry, resin and additives, the slurry includes water, dispersant, slurry wetting agent, slurry defoamer, titanium dioxide, kaolin, heavy calcium and Talcum powder, described auxiliary agent comprises lauryl alcohol ester, dipropylene glycol methyl ether, defoamer, wetting agent, leveling agent and thickener, and the mass percent of described each component in white primer is: water : 7.0%; dispersant: 0.3%; slurry wetting agent: 0.3%; slurry defoamer: 0.3%; titanium dioxide: 21.6%; kaolin: 6.2%; heavy calcium: 6.2%; talcum powder: 9.4% ; Resin: 41.0%; Lauryl alcohol ester: 3.2%; Dipropylene glycol methyl ether: 3.2%; Defoamer: 0.3%; Wetting agent: 0.3%; The preparation process is the same as in Example 1.

[0094] The formula is characterized by good coverage and crack resistance.

Embodiment 3

[0096] Density board edge banding water-based wood white primer is composed of slurry, resin and additives, the slurry includes water, dispersant, slurry wetting agent, slurry defoamer, titanium dioxide, kaolin, heavy calcium and Talcum powder, described auxiliary agent comprises lauryl alcohol ester, dipropylene glycol methyl ether, defoamer, wetting agent, leveling agent and thickener, and the mass percent of described each component in white primer is: water : 6.3%; dispersant: 0.2%; slurry wetting agent: 0.2%; slurry defoamer: 0.2%; titanium dioxide: 18%; kaolin: 5.2%; heavy calcium: 6.7%; talcum powder: 9.5% ; Resin: 45.0%; Lauryl alcohol ester: 3.3%; Dipropylene glycol methyl ether: 3.3%; Defoamer: 0.5%; Wetting agent: 0.5%; The preparation process is the same as in Example 1.

[0097] This formula is characterized by the best anti-cracking effect.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses white waterborne wood base coat for a medium density fiberboard and a preparation technology thereof. The preparation technology comprises the processes of: mixing 6.0-8.0 parts of water, 0.2-0.5 part of dispersing agents, 0.2-0.4 part of slurry wetting agents, 0.2-0.4 part of slurry defoaming agents, 18-22 parts of titanium white powder, 5.0-8.0 parts of kaolin, 5.0-8.0 parts of triple superphosphate, 8.0-12.0 parts of talc powder in parts by weight and dispersing to form the slurry, wherein the fineness of the slurry is less than or equal to 50 mu m; mixing 38.0-45.0parts of resins with the slurry; under the condition of stirring, respectively adding 2.0-4.0 parts of dodecyl acetate, 2.0-4.0 parts of dipropylene glycol methyl ether, 0.3-0.6 part of antifoaming agents, 0.3-0.6 part of wetting agents, 0.3-0.6 part of flatting agents and 0.4-0.8 part of thickening agents, and evenly stirring, discharging and packing. The base coat can control water vapour entering the medium density fiberboard. The paint film has 200-300% of drawing tension, also can not crack, and has good sealing and anti-cracking effects. Besides, the invention has the advantages of quick drying speed and good rubbing property.

Description

【Technical field】 [0001] The invention relates to the field of wood coatings, in particular to a density board edge-sealing water-based wood white primer and a preparation process thereof. 【technical background】 [0002] Existing water-based woodware white primers have great defects on the cross-section edge sealing of density boards. It is mainly caused by cracking of the paint film in wet weather. The main reason is that the density board is plywood. In humid weather, water vapor will enter the density board, foam the glue and wood fiber in the density board, make it expand, and cause the paint film on the surface to crack. 【Content of invention】 [0003] The purpose of the present invention is to solve the problems existing in the prior art, and to propose a water-based wood white primer for density board edge sealing and its preparation process, which will not cause cracking of the paint film in a humid environment. [0004] In order to achieve the above object, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/12C09D7/12
Inventor 朱国强毛赵国吴法理袁华龙严俊雨沈杰吕君
Owner ZHEJIANG FEIDA ZHONGKE FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com