Method for preparing magnetizable ceramic

A technology for the preparation of ceramics and ceramic products, applied in the field of preparation of magnetizable ceramics, can solve the problems of low yield, limited use, and lack of firm connection, and achieves the effect of solving the combination problem and achieving remarkable innovation.

CN102153333AInactive Publication Date: 2011-08-17FOSHAN CERAMIC R & D CENT SHANGHAI INST OF CERAMICS CHINESE ACAD OF SCI
3 Cites 54 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2011-08-17
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
Patent Text Reader

Abstract

The invention discloses a method for preparing magnetizable ceramic. The method is characterized in that: a magnetizable substance is added into nonmagnetic ceramic powder, and a magnetizable ceramic product is prepared by adopting a ceramic preparation process; and the ceramic preparation process comprises proportioning, blending, shaping and sintering. The magnetizable substance is directly added into the ceramic raw materials, and the magnetizable substance is sintered in a ceramic body by a ceramic high-temperature sintering process at the same time of keeping the original magnetizable property, so that the bonding problem of the magnetizable substance and the ceramic product is solved, the process is simple, the preparation is convenient, and the method has good popularization value.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the technical field of ceramic materials, in particular to a preparation method of magnetizable ceramics. Background technique

[0002] Ceramics are commonly used materials in people's daily life, especially traditional ceramics, namely construction, bathroom, daily use, arts and crafts ceramics, such as wall and floor tiles, bathroom, tableware and art ceramics, etc. It plays an important role in protecting one's health and is an essential daily necessities for people's lives. At present, the main functions of these ceramic materials are limited to the use characteristics determined by their own materials and processing characteristics. For example, wall and floor tiles are mainly used for decoration and beautification. Sanitary ceramics meet people’s needs for washing and cleaning. Cooking, carrying items and other daily needs. Arts and crafts ceramics meet people's needs for space decoration and collection. The extension ...

Examples

preparation example Construction

[0026] like figure 1Shown, the present invention is a kind of preparation method of magnetizable ceramics, it is to mix magnetizable substance in non-magnetic ceramic powder, adopt ceramic preparation process, prepare magnetizable ceramic products. Non-magnetic ceramic powder is selected from one or more of various ceramic raw materials, ceramic blanks, and ceramic glazes; ceramic raw materials include: natural minerals, processed minerals, and chemical products; ceramic blanks include: ceramic wall and floor tile blanks, sanitary ceramic blanks , Daily-use ceramic blanks, industrial ceramic blanks; magnetizable substances are selected from substances that can obtain magnetic characteristics under the action of an external magnetic field, including metal oxides, metals, alloys, minerals, and various forms of substances composed of them; metal oxides Substances, metals, alloys, minerals each alone or a mixture of more than one and other substances; metal oxides include soft fer...

Embodiment 1

[0030] Weigh 14 kg of granulated blanks of ceramic polished tiles, 6 kg of nickel-zinc ferrite granulated powders, dry-stir and mix them into a mixture, press the mixture into 400×400×8mm bricks, after drying, Fired at 1200°C for 30 minutes, the resulting ceramic tiles have a magnetizable function.

Embodiment 2

[0032] Weigh 12 kg of ceramic glazed tile blanks, 8 kg of soft magnetic ferrite powder, mix them into a mixed slurry by wet method, dry and granulate the mixed slurry, press it into a brick adobe of 200×300×6mm, and dry it , fired at 1150°C for 30 minutes to obtain a biscuit body, glazed on the biscuit body, and then fired at 1120°C, the obtained ceramic glazed tile has a magnetizable function.