Molybdenum-containing nickel-saving austenitic stainless steel with excellent corrosion resistance and manufacturing method thereof

A technology for austenitic stainless steel and its manufacturing method, which is applied in the field of nitrogen-containing nickel-free austenitic stainless steel and its manufacturing, and can solve the problems of reducing corrosion resistance and negative corrosion resistance

Active Publication Date: 2012-02-01
BAOSTEEL DESHENG STAINLESS STEEL
View PDF13 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the Cr content in these patented composition systems is generally lower than 18% in 304 austenitic stainless steel, which reduces the corrosion resi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Molybdenum-containing nickel-saving austenitic stainless steel with excellent corrosion resistance and manufacturing method thereof
  • Molybdenum-containing nickel-saving austenitic stainless steel with excellent corrosion resistance and manufacturing method thereof
  • Molybdenum-containing nickel-saving austenitic stainless steel with excellent corrosion resistance and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0048] The alloy metallographic diagram of Example 1 is as figure 1 As shown (room temperature is austenite structure), the sample is electrolytically corroded, the corrosive agent is saturated oxalic acid solution, and the corrosion current is 0.2~0.4A / cm 2 . Table 2 shows the mechanical properties and corrosion properties of the steel of the invention and the comparative steel. The mechanical properties are all taken from hot-rolled annealed sheets, processed and tested according to JIS 13B standards. The equivalent of pitting corrosion resistance is calculated according to the general formula PREN=Cr%+3.3Mo%+30N%-Mn%.

[0049] Table 1 Composition of Examples and Comparative Examples Unit: Percent by Weight

[0050]

[0051]

[0052] Table 2 Performance of Examples and Comparative Examples

[0053]

[0054] Note: Comparative Examples 1, 2, 3, 4 are CN101148740, CN101381852, CN101509104, and 304 austenitic stainless steel respectively.

[0055] It can be s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses molybdenum-containing nickel-saving austenitic stainless steel with excellent corrosion resistance and a manufacturing method thereof. The molybdenum-containing nickel-saving austenitic stainless steel with excellent corrosion resistance contains: by weight, 0.03 to 0.10% of C, 0.2 to 1.0% of Si, 4.0 to 9.0% of Mn, 16.5 to 18.0% of Cr, 1.5 to 3.5% of Ni, 0.15 to 0.35% of N, 0.2 to 0.8% of Mo, 0.01 to 2.5% of Cu, less than or equal to 0.1% of one or more of V, Nb, Ca and B, and the balance Fe and unavoidable impurities. Through the manufacturing method, Ni content is controlled in a rang of 1.5 to 3.5%, and Mn and N elements are added to replace precious metal Ni to be utilized for austenitizing, so that a microstructure of room-temperature austenite is obtained. The manufacturing method adopts 0.2 to 0.8% of Mo and utilizes a synergistic effect of Cr, Mo and N to improve corrosion resistance. Through the manufacturing method, the pitting-resistance equivalent number of the molybdenum-containing nickel-saving austenitic stainless steel with excellent corrosion resistance is great than or equal to 18 and the pitting potential is great than or equal to 330mV, wherein the properties of the molybdenum-containing nickel-saving austenitic stainless steel with excellent corrosion resistance are equivalent to or superior to corresponding properties of 304 austenitic stainless steel.

Description

technical field [0001] The invention relates to a nitrogen-containing nickel-sparing austenitic stainless steel and a manufacturing method thereof, in particular to a molybdenum-containing nickel-sparing austenitic stainless steel with excellent corrosion resistance and a manufacturing method thereof. The PREN of the material is greater than or equal to 18. Background technique [0002] The most widely used 300-series austenitic stainless steel usually contains 8% to 12% nickel, and the cost of nickel element accounts for about 80% of the cost of raw materials. Since 2005, the price of nickel, an important alloying element in stainless steel, has continued to rise, leading to an increase in the cost of raw materials for stainless steel production. At the same time, it is predicted that the shortage of rare and precious metal nickel has a certain long-term nature. This makes reducing the cost of stainless steel production a key issue for the development of iron and steel ente...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/58
Inventor 张伟胡锦程江来珠王治宇宋红梅韩俭
Owner BAOSTEEL DESHENG STAINLESS STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap