Heat treatment method of novel alloy steel hollow car axle material
A heat treatment method and technology of hollow axles, applied in heat treatment equipment, manufacturing tools, quenching agents, etc., can solve the problems that the heat treatment process technology for manufacturing axles is not given, and achieve the effect of excellent low-temperature impact toughness and wide allowable range
Inactive Publication Date: 2014-09-24
TSINGHUA UNIV +1
View PDF3 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Among them, the CRH2 type is imported from Japan, which adopts the technical route of carbon steel and surface strengthening treatment; the other types are imported from Europe, and uses quenched and tempered alloy steel EA4T and 30NiCrMoV12. The chemical composition and mechanical performance requirements are specified, but the key heat treatment technology for manufacturing axles is not given
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] The present invention provides a heat treatment method for a novel alloy steel hollow axle material. The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments.
[0016] A series of novel alloy steel hollow axle materials are processed by the method of the present invention, and the specific methods are shown in Table 1.
[0017] Table 1 heat treatment parameter table
[0018]
[0019] The method of the present invention is easy to control and is suitable for industrialized production. The grain size of the new alloy steel hollow axle blank after the above heat treatment process is 8-9 grades, and the microstructure at 1 / 2 of the radius of the axle body can be seen figure 1 ; Its strength, plasticity, toughness and fatigue properties are shown in Table 2, all of which exceed the requirements of the European high-speed hollow axle standard EN13261. In the case of increased strength, the plasticity still...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| crystal size | aaaaa | aaaaa |
Login to View More
Abstract
The invention belongs to the technical field of heat treatment processes of alloy steel hollow car axle materials for high-speed passenger trains and particularly relates to a heat treatment method of a novel alloy steel hollow car axle material. The heat treatment method is characterized by pre-heating novel alloy steel with shaft blank sizes at the temperature of 910-950 DEG C, quenching the novel alloy steel at the temperature of 900-940 DEG and tempering the novel alloy steel at the temperature of 620-670 DEG C. The heat treatment method has the advantages that the developed novel alloy steel hollow car axle material for the high-speed passenger trains is domestically and independently developed, mechanical properties of axles which are treated by a heat treatment process matched with the material all exceed requirements of the European hollow car axle standard EN13261, the axles are good in obdurability matching, especially, high in smooth specimen fatigue strength and notch specimen fatigue strength and excellent in low temperature impact toughness, so that the axles can be used under various domestic weather conditions. According to the heat treatment method of the novel alloy steel hollow car axle material, heat treatment process technical assurance is provided for finally producing novel alloy steel hollow car axles at the speed of 200km / h-350km / h.
Description
technical field [0001] The invention belongs to the technical field of heat treatment technology for alloy steel hollow axle materials used in high-speed railway passenger cars, and in particular relates to a heat treatment method for novel alloy steel hollow axle materials. Background technique [0002] In recent years, the high-speed railway with a speed of more than 200 km / h has developed rapidly in my country. It not only revitalizes the traditional railway industry, but also drives other related industries and promotes the development of my country's national economy. So far, there are four types of high-speed (above 200 km / h) passenger car axles operated by Chinese railways: CRH1, CRH2, CRH3 and CRH5, which mainly rely on imports. Among them, the CRH2 type is imported from Japan, which adopts the technical route of carbon steel and surface strengthening treatment; the other types are imported from Europe, and uses quenched and tempered alloy steel EA4T and 30NiCrMoV12....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & AuthorityPatents(China)
IPC IPC(8): C21D1/60C21D1/18C22C38/24C22C38/46
Inventor朱静顾家琳刘淑华周惠华吴海英潘涛汝继来李照智施惠基穆恩生钟虓龑
OwnerTSINGHUA UNIV