Permanent anti-static electricity partes aequales (PA6)/ polyolefin elastomer (POE) alloy and preparation method thereof

An antistatic and antistatic masterbatch technology, applied in the field of antistatic composite materials and their preparation, can solve problems such as low electrical conductivity, and achieve the effects of low cost, good heat resistance and light color

Inactive Publication Date: 2015-04-08
SHANGHAI SUNNY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PA6 / POE alloy has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω.m, the conductivity is much smaller than that of metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permanent anti-static electricity partes aequales (PA6)/ polyolefin elastomer (POE) alloy and preparation method thereof
  • Permanent anti-static electricity partes aequales (PA6)/ polyolefin elastomer (POE) alloy and preparation method thereof
  • Permanent anti-static electricity partes aequales (PA6)/ polyolefin elastomer (POE) alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0025] The raw material formula of preparing antistatic masterbatch in embodiment 1-5 is as follows:

[0026]

[0027] Put the above components into a high mixer according to the proportion and mix them for 2-5 minutes, discharge the material, and then use a screw extruder to extrude and granulate. The processing temperature is 150-200°C, and the screw speed is 25-35HZ.

[0028]

[0029]

[0030] According to the samples prepared in Examples 1-5, the surface resistivity test was carried out for comparison.

[0031] The test performance comparison is shown in the table below:

[0032] project

[0033] The surface resistivity of the permanent antistatic masterbatch developed according to the above formula and process can reach 10 6 -10 8 Ω.m. can be widely used in modified PA6 / POE alloys; compared with the existing technology, it has a long-lasting antistatic effect, a small amount of addition but good antistatic effect, little impact on the performance of ...

Embodiment 5

[0034] Example 5 has the lowest surface resistivity and the highest cost performance.

Embodiment 6-10

[0037] Permanent antistatic PA6 / POE alloy and preparation method thereof

[0038] The raw material formula of embodiment 6-10 is as follows:

[0039]

[0040] Put the above components into a high-speed mixer according to the proportion and mix them for 2-5 minutes, discharge the material, and then use a screw extruder to extrude and pelletize.

[0041]

[0042] According to the samples prepared in Comparative Examples 1-5, the performance test comparison was carried out, and the ASTM standard was adopted.

[0043] The test performance comparison is shown in the table below:

[0044]

[0045] Compared with the existing technology, the permanent antistatic PA6 / POE alloy developed according to the above formula and process has a long-lasting antistatic effect, achieves a permanent antistatic effect, good antistatic effect, high comprehensive mechanical properties, and is close to pure PA6 / POE alloy. The performance of POE alloy, light color can be made into various col...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a permanent anti-static electricity partes aequales (PA6) / polyolefin elastomer (POE) alloy and a preparation method of the permanent anti-static electricity PA6 / POE alloy. The alloy material comprises the following components and part by weight contents: 3-8 parts of a self-control anti-static electricity master batch, 40-75 parts of the PA6, 15-25 parts of the POE and 1-5 parts of a compatilizer . Raw materials are weighed and taken according to the weight ratio. The raw materials are placed in a high mixing machine and the raw materials are blended for 2-5 minutes. The raw materials are discharged. Then pelletings are squeezed from a double screw rod extruder. The machining temperature is 190-205 DEG C. The number of revolutions of a screw rod is 35-40 HZ. Compared with the prior art, the permanent anti-static electricity PA6 / POE alloy has the advantages that the anti-static electricity effect is permanent and the effect of permanent anti-static electricity is achieved. The anti-static electricity effect is good. Analyse mechaniscs performance is high. The permanent anti-static electricity PA6 / HDPE alloy is close to the pure PA6 / POE alloy performance. Color is light. The permanent anti-static electricity PA6 / POE alloy can be matched to various kinds of colors. The permanent anti-static electricity PA6 / POE has the advantages of being low in cost, good in heat resistance and the like. Surface electrical resistivity of the permanent anti-static electricity PA6 / POE alloy can be arrived at 106-108 omega-m.

Description

technical field [0001] The invention relates to an antistatic composite material and a preparation method thereof, in particular to a permanent antistatic PA6 / POE alloy and a preparation method thereof. Background technique [0002] Nylon 6 has become the current application due to its good comprehensive mechanical properties, high heat resistance, good wear resistance, self-lubrication, good flame retardancy, excellent chemical corrosion resistance, and excellent barrier properties. The widest range of engineering plastics. POE is non-toxic, odorless, low density, low price, and has excellent properties such as aging resistance, ozone resistance, and chemical medium resistance. POE can be used as an impact modifier for engineering plastics, used in the production of impact-resistant mechanical parts, corrosion-resistant parts, automobiles, electrical parts and other products. Adding POE to PA6 can effectively improve its hygroscopicity and improve the stability of the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/02C08L23/08C08L51/08C08L51/06C08K13/02C08K3/16C08K3/24C08K5/46C08K5/524C08K5/57C08K5/098C08K3/36B29B9/06B29C47/92B29C48/92
CPCB29C2947/92704B29C2947/92895B29C2947/92885B29C47/92B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 郭建鹏张强孟成铭杨涛
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com