Oxidized graphene-rhamnolipid composite material and preparation method and application thereof

A rhamnolipid and composite material technology, which is applied in chemical instruments and methods, other chemical processes, adsorption water/sewage treatment, etc., can solve the problems of high biological toxicity, low adsorption capacity, and poor treatment effect, and achieve biological Low toxicity, large adsorption capacity, and easy solid-liquid separation

Active Publication Date: 2015-04-29
HUNAN UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there have been researches on composite materials combining graphene oxide with chitosan, polyethersulfone and calcium alginate at home and abroad, and have been used in the treatment of dye wastewater, but the adsorption capacity is low and the treatment effect is low. Poor, high biological toxicity and other defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oxidized graphene-rhamnolipid composite material and preparation method and application thereof
  • Oxidized graphene-rhamnolipid composite material and preparation method and application thereof
  • Oxidized graphene-rhamnolipid composite material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Preparation method of graphene oxide-rhamnolipid composite material and application of methylene blue dye adsorption.

[0036] (1) Preparation of graphene oxide-rhamnolipid composite material: Weigh 100 mg of graphene oxide and add it to 100 ml of dimethylformamide, ultrasonically strip it for 1 hour to form graphene oxide mixture, and then add graphene oxide mixture to Add 400mg rhamnolipid with a mass content of 90%, 400mg EDC and 80mg DMAP and mix evenly. After ultrasonic reaction at 25°C-45°C for 3h, add 50ml of anhydrous methanol and stir for 15min to produce precipitation; After washing with water and ethanol, centrifuge at 10,000 rpm for 15 minutes, wash and filter with deionized water, and finally vacuum freeze-dry at -110°C for 3 days to obtain the graphene oxide-rhamnolipid composite material.

[0037] (2) Application of graphene oxide-rhamnolipid composite material for adsorption of methylene blue dye: Weigh 10 mg of graphene oxide-rhamnolipid composite mater...

Embodiment 2

[0040] Preparation method of graphene oxide-rhamnolipid composite material and application of methylene blue dye adsorption.

[0041](1) Preparation of graphene oxide-rhamnolipid composite material: Weigh 100 mg of graphene oxide and add it to 100 ml of dimethylformamide, ultrasonically strip it for 1 hour to form graphene oxide mixture, and then add graphene oxide mixture to Add 300mg rhamnolipid with a mass content of 90%, 500mg EDC and 100mg DMAP and mix evenly. After ultrasonic reaction at 25°C-45°C for 3h, add 60ml of anhydrous methanol and stir for 15min to produce precipitation; After washing with water and ethanol, centrifuge at 10,000 rpm for 15 minutes, wash and filter with deionized water, and finally vacuum freeze-dry at -110°C for 2 days to obtain graphene oxide-rhamnolipid composite material. The graphene oxide-rhamnolipid composite material that above-mentioned steps makes is carried out scanning electron microscope, transmission electron microscope and Fourier ...

Embodiment 3

[0046] Preparation method of graphene oxide-rhamnolipid composite material and application of adsorbed methyl violet dye.

[0047] (1) Preparation of graphene oxide-rhamnolipid composite material: Weigh 100 mg of graphene oxide and add it to 100 ml of dimethylformamide, ultrasonically strip it for 1 hour to form graphene oxide mixture, and then add graphene oxide mixture to Add 200mg rhamnolipid with a mass content of 90%, 600mg EDC and 100mg DMAP and mix evenly. After ultrasonic reaction at 25℃~45℃ for 3h, add 50ml anhydrous methanol and stir for 15min to produce precipitation; After washing with water and ethanol, centrifuge at 10,000 rpm for 15 minutes, wash and filter with deionized water, and finally vacuum freeze-dry at -110°C for 3 days to obtain the graphene oxide-rhamnolipid composite material.

[0048] (2) Adsorption of methyl violet by graphene oxide-rhamnolipid composite material: Weigh 5mg, 10mg, 15mg, 20mg graphene oxide-rhamnolipid composite material in 25ml, co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
adsorption capacityaaaaaaaaaa
clearance rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene oxide-rhamnolipid composite material, which is in the form of black gray powder and has a layered porous nanostructure. The invention also discloses a preparation method of the composite material, which includes the following steps: adding graphene oxide into a dispersant, and ultrasonically dispersing to form a graphene oxide mixed liquid; adding rhamnolipid, 1-ethyl -(3-Dimethylaminopropyl) carbodiimide hydrochloride and 4-dimethylaminopyridine and ultrasonic reaction, then add a certain amount of anhydrous methanol and stir to produce precipitation; the precipitated product is washed and centrifuged, and finally vacuum Graphene oxide-rhamnolipid composites were prepared by freeze-drying. The present invention also relates to the application of the composite material prepared by the above method in the adsorption of cationic dyes. The composite material prepared by the invention has low biotoxicity, is not easy to agglomerate, and the preparation method is simple and feasible, and has the advantages of no secondary pollution, easy solid-liquid separation and the like during the adsorption treatment process of cationic dyes.

Description

technical field [0001] The invention belongs to the field of material preparation and environmental protection, and in particular relates to a graphene oxide-rhamnolipid composite material, a preparation method thereof and the application of adsorbing cationic dyes. Background technique [0002] With the development of the economy, dyes are widely used in textiles, leather, food, paint, ink and rubber and other fields. Therefore, the environmental problems caused by dye wastewater in my country are becoming increasingly prominent. Most dyes have strong chemical stability and biodegradability, so they can exist in water for a long time and cause serious environmental pollution. At present, in order to reduce the pollution of dye wastewater to the environment, methods such as photocatalytic degradation, membrane filtration, flocculation and precipitation, electrochemical technology, and adsorption have been applied to the decolorization of dye wastewater. Adsorption treatment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): B01J20/22B01J20/30C02F1/28
Inventor袁兴中吴志斌王侯曾光明钟华王乐乐肖智华冷立健黄丹莲梁婕陈耀宁
OwnerHUNAN UNIV