Water-based metal rust-proof varnish and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A metal anti-rust and varnish technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of poor anti-rust effect of varnish, and achieve the effect of long anti-rust time, high hardness and fast self-drying speed
Inactive Publication Date: 2014-03-26
徐州市水性漆厂
View PDF4 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, there are many water-based antirust products on the market, but most of them are anti-corrosion through the addition of pigments and fillers, which cover the luster of the metal surface, and the antirust effect of varnishes without these fillers is very poor.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0023] Raw material components: 12 parts of deionized water, 80 parts of water-based polymer emulsion, 1 part of salt spray resistant agent HALOX SW-111, 0.5 part of corrosion inhibitor HALOX-550, 0.1 part of wetting and leveling agent ELEMENTIS U-99, wax 2 parts of emulsion, 4 parts of alcohol ester 12, 0.2 part of pH regulator, 0.2 part of associative thickener DOW RM-8W.
[0024] Preparation:
[0025] (1) Add deionized water, water-based polymer emulsion, salt spray resistance, and corrosion inhibitors in proportion to the paint mixing tank and stir evenly, and grind at high speed in a sand mill for half an hour;
[0026] (2) Add wetting and leveling agent, wax emulsion, and alcohol ester twelve medium-speed dispersion in sequence;
[0027] (3) Add PH regulator to adjust to 8.0;
[0028] (4) Slowly add associative thickener;
[0029] (5) Screening and filling.
Embodiment 2
[0031] Raw material components: 15 parts of deionized water, 77 parts of water-based polymer emulsion, 2 parts of salt spray resistant agent HALOX SW-111, 0.3 part of corrosion inhibitor HALOX-550, 0.1 part of wetting and leveling agent ELEMENTIS U-99, wax 2 parts of emulsion, 3 parts of alcohol ester twelve, 0.3 part of pH regulator, 0.3 part of associative thickener DOW RM-8W.
[0032] The preparation method is as follows:
[0033] Preparation:
[0034] (1) Add deionized water, water-based polymer emulsion, salt spray resistance, and corrosion inhibitors in proportion to the paint mixing tank and stir evenly, and grind at high speed in a sand mill for half an hour;
[0035] (2) Add wetting and leveling agent, wax emulsion, and alcohol ester twelve medium-speed dispersion in sequence;
[0036] (3) Add PH regulator to adjust to 8.0;
[0037] (4) Slowly add associative thickener;
[0038] (5) Screening and filling.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to water-based metal rust-proof varnish and a preparation method thereof, and belongs to the field of coating. The water-based metal rust-proof varnish comprises the following components in parts by weight: 5 to 15 parts of deionized water, 70 to 80 parts of water-based polymer emulsion, 1 to 2 parts of a salt-mist-resistant agent, 0.5 to 1 part of a corrosion inhibitor, 0.1 to 0.3 part of a wetting and leveling agent, 2 to 3 parts of wax emulsion, 4 to 6 parts of alcohol ester-12, 0.2 to 0.4 part of a pH regulator and 0.2 to 0.5 part of an associative thickener. The water-based metal rust-proof varnish can form a paint film quickly at room temperature, has high transparency, light color, high glossiness and good plumpness, is smooth and fine, and perfectly takes on the metal effect of a substrate. High-performance materials are selected, so that the paint film has strong ultraviolet-resistant ability, good adhesive force, high weather resistance, yellowing resistance, water tolerance, scraping resistance, high hardness and long rust-proof time, and is bright and clean as new after being washed by rain. The product is non-toxic and odorless, does not contain components which are harmful to a human body and the environment, and is real environment-friendly water-based corrosion-resistant coating. The water-based metal rust-proof varnish is convenient to construct and high in self-drying speed, improves the efficiency and reduces the energy.
Description
technical field [0001] The invention relates to a water-based paint and belongs to the field of paint. Specifically, it is a water-based metal antirust varnish and a preparation method thereof. Background technique [0002] The continuous improvement of today's material and spiritual life makes people have a special liking for the original ecological things, especially the best-selling log furniture all reflect people's desire for nature in the fast-paced and high-pressure environment. At present, there are many water-based antirust products on the market, but most of them are anti-corrosion through the addition of pigments and fillers, which cover the luster of the metal surface, and the antirust effect of varnishes without these fillers is very poor. Contents of the invention [0003] The purpose of the present invention is to provide a water-based metal antirust varnish, which is an environment-friendly anticorrosion paint. Another object of the present invention is t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).