Biodegradable polymer composition for the manufacture of articles having a high heat deflection temperature

A heat distortion temperature and biodegradation technology, applied in the field of heat distortion temperature products, can solve problems such as deformation and adverse effects on industrial processability

Active Publication Date: 2016-01-13
NOVAMONT SPA
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, although this technique causes a significant increase in the heat deflection temperature of the article, it also causes its deformation
Therefore, special precautions have to be taken during the design and production phases of said articles, which has an adverse effect on their industrial processability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biodegradable polymer composition for the manufacture of articles having a high heat deflection temperature
  • Biodegradable polymer composition for the manufacture of articles having a high heat deflection temperature
  • Biodegradable polymer composition for the manufacture of articles having a high heat deflection temperature

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0114] Table 1 - Compositions in Example 1

[0115]

[0116] Values ​​are expressed in parts when not explicitly indicated.

[0117] PLA = polylactic acid containing 98% L-lactic acid and 2% D-lactic acid, melting point Tm = 165°C, weight average molecular weight Mw = 166000, intrinsic viscosity = 0.97dl / g and shear viscosity = 120Pas, according to standard ASTM -D3835 at T=190℃, shear rate=1000s -1 Measured with capillary D=1 mm and L / D=10.

[0118] AAPE = poly(butylene sebacate-co-butylene terephthalate) (PBST) containing 56 mole % terephthalic acid relative to the total amount of aliphatic and aromatic diacids, And have MFI=14g / 10min (190 ℃ and 2.16kg), and shear viscosity η=570Pas, according to standard ASTM-D3835 at T=180 ℃, shear rate=104s -1 Measured with capillary D=1 mm and L / D=30.

[0119] Anti-caking agent = vegetable sourced oleamide

[0120] Nucleating agent = micronized talc (particle size = 2-10 microns)

[0121] Cellulose fiber = 100% pure cellulose fi...

Embodiment 2

[0142] The molded samples were then subjected to an annealing treatment in a Venti-Line VL115 model furnace with circulating air using the following operating conditions: temperature = 90°C, time = 60 minutes in an unconfined environment.

[0143] After cooling and further conditioning for 1 day at T=23° C. and 55% RH, the annealed specimens were then investigated to determine dimensional stability, mechanical properties and heat distortion temperature HDT.

[0144] The results of this characterization are shown in Tables 5-7.

Embodiment 3-5

[0146] The molded test pieces according to Example 1 were subjected to three different annealing treatments using the operating conditions shown in Table 3:

[0147] Table 3 - Annealing Conditions

[0148]

[0149] After cooling and reconditioning for 1 day at T=23°C and 55% RH, the annealed samples were investigated to determine their dimensional stability (PDC) and heat deflection temperature (HDT) (Tables 6-7).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The present invention relates to biodegradable polymer compositions which are especially suitable for the manufacture of articles having a high heat deflection temperature (HDT) by injection molding and thermoforming.

Description

technical field [0001] The present invention relates to biodegradable polymer compositions which are particularly suitable for the manufacture of articles having a high heat deflection temperature (HDT) by injection molding and thermoforming. [0002] The invention also relates to processes for the preparation of said compositions and articles obtained therewith. Background technique [0003] Polylactic acid is a biodegradable thermoplastic polyester derived from renewable sources. Its mechanical properties make it an ideal candidate to replace conventional thermoplastic polymers, especially in applications where high rigidity is required, such as in the manufacture of disposable tableware, rigid containers or caps for beverage containers. [0004] Although polylactic acid can be used in standard machinery with minimal modifications, some of its properties have so far prevented its widespread and comprehensive use as a replacement for conventional thermoplastics. [0005] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/04
CPCC08L67/02C08L67/04B29C45/0001B29C51/002B29C51/42B29C71/02B29C2071/022B29K2067/046B29K2105/0005B29K2105/0085B29K2105/0088B29K2995/0016B29K2995/006C08L2201/06C08L2201/08C08L2203/30C08L2205/02C08L2205/03C08L2205/24C08L2207/04
Inventor N·马瑞尼A·拉里斯
Owner NOVAMONT SPA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com