Anti-aging antibacterial pc/abs blended alloy and preparation method thereof

An anti-aging, mixed gold technology, applied in the field of polymer materials, can solve the problems of limiting PC application, high processing temperature, large residual stress, etc., achieve good social value and experience value, increase added value, and improve mechanical properties.

Active Publication Date: 2016-08-17
STARWAY INTERNATIONAL HOME LIVING CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the price of PC is relatively expensive, the processing temperature is high, the residual stress is large, and the fluidity is poor, which limits the application of PC to a large extent.
Compared with PC, acrylonitrile-butadiene-styrene copolymer (ABS) is cheap, has excellent performance, has gloss, and is easy to form and process, but its heat resistance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-aging antibacterial pc/abs blended alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An aging-resistant and antibacterial PC / ABS blended alloy and a preparation method thereof, the formula consists of:

[0020] High viscosity ABS (5% butadiene, density 1.04 g / cm 3 ) is 12%;

[0021] PC (with a density of 1.18 g / cm 3 , molecular weight is 40000) is 40%;

[0022] Photostable antibacterial agent nano-titanium dioxide (50nm) is 3%;

[0023] UV absorber benzophenones is 2%;

[0024] Light calcium carbonate (particle size is 1um) is 40%;

[0025] Antioxidant 1010 is 1%;

[0026] The compatibilizer ABS-g-MAH is 2%.

[0027] The preparation method of aging-resistant and antibacterial PC / ABS blended alloy is as follows: fully dry high-viscosity ABS, Dow PC, light-stable antibacterial agent, ultraviolet absorber, nanofiller and other additives in an 80°C blast oven, and pass 1000-rpm high-speed mixer stirs evenly; then the raw materials are extruded, granulated, After drying, PC / ABS alloy particles can be obtained.

Embodiment 2

[0029] An aging-resistant and antibacterial PC / ABS blended alloy and a preparation method thereof, the formula consists of:

[0030] High viscosity ABS (6% butadiene, density 1.05 g / cm 3 ) is 20%;

[0031] PC (with a density of 1.19 g / cm 3 , molecular weight is 50000) is 30%;

[0032] Light stable antibacterial agent nano-titanium dioxide (100nm) is 4%;

[0033] UV absorber salicylic acid is 4%;

[0034] Hard calcium carbonate (particle size is 10um) is 40%;

[0035] Antioxidant 168 is 1%;

[0036] The compatibilizer ABS-g-MAH is 1%.

[0037] The preparation method of aging-resistant and antibacterial PC / ABS blended alloy is as follows: fully dry high-viscosity ABS, Dow PC, light-stable antibacterial agent, ultraviolet absorber, nanofiller and other additives in an 80°C blast oven, and pass The high-speed mixer at 2000 rpm stirs evenly; then the raw materials are extruded, granulated, After drying, PC / ABS alloy particles can be obtained.

Embodiment 3

[0039] An aging-resistant and antibacterial PC / ABS blended alloy and a preparation method thereof, the formula consists of:

[0040] High viscosity ABS (butadiene content 7%, density 1.06 g / cm 3 ) is 25%;

[0041] PC (with a density of 1.20 g / cm 3 , molecular weight is 60000) is 50%;

[0042] Photostable antibacterial agent nano-titanium dioxide (200nm) is 3%;

[0043] The ultraviolet absorber benzotriazepine is 4%;

[0044] Nano calcium carbonate (particle size is 100nm) is 15%;

[0045] Antioxidant 264 is 1%;

[0046] The compatibilizer ABS-g-MAH is 2%.

[0047] The preparation method of aging-resistant and antibacterial PC / ABS blended alloy is as follows: fully dry high-viscosity ABS, Dow PC, light-stable antibacterial agent, ultraviolet absorber, nanofiller and other additives in an 80°C blast oven, and pass 3000-rpm high-speed mixer stirs evenly; then the raw materials are extruded, granulated, After drying, PC / ABS alloy particles can be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

Anti-aging and antibacterial PC / ABS blended alloy and its preparation method, its components include: PC, ABS, light stable antibacterial agent, ultraviolet absorber, nano filler and other additives, in parts by weight: ABS is 10-25% , PC is 30-50%, light-stable antibacterial agent is 0.5-5%, ultraviolet absorber is 0.5-5%, nanofiller is 15-45%, other additives are 1-5%, and its preparation method is: The raw materials with the above proportions are dried in a blast oven, and stirred evenly by a high-speed mixer at 1000-5000 rpm; the raw materials are extruded, granulated, and dried by a single-screw extruder at a specific temperature to obtain granules. The invention not only has good anti-aging performance, but also has excellent antibacterial performance, and the product has good mechanical properties, and can be used in products such as automobile interior decoration, electronic appliances, mechanical equipment, furniture articles and the like.

Description

technical field [0001] The invention relates to an aging-resistant and antibacterial PC / ABS blended alloy and a preparation method thereof, belonging to the technical field of polymer materials. Background technique [0002] Polycarbonate (PC) is an increasingly widely used engineering plastic, which has comprehensive and stable mechanical properties, thermal properties and electrical properties. However, the price of PC is relatively expensive, the processing temperature is high, the residual stress is large, and the fluidity is poor, which limits the application of PC to a large extent. Compared with PC, acrylonitrile-butadiene-styrene copolymer (ABS) is cheap, has excellent performance, has gloss, and is easy to form and process, but its heat resistance is poor. By blending PC and ABS, an alloy with good overall performance and relatively high performance and price can be obtained. The solubility parameter of PC is 19.5 (J / cm 3 )1 / 2, the solubility parameter of ABS is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L55/02C08L51/06C08K13/02C08K3/22C08K3/26C08K5/07C08K5/134C08K5/526B29B9/06B29C47/92B29C48/92
Inventor 叶根林
Owner STARWAY INTERNATIONAL HOME LIVING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More