Frit particle binder and preparation method thereof

A technology of frit particles and binders, which is applied in the field of architectural ceramics, can solve the problems of easily being sucked away by frit particles and binders, and achieve the effects of no influence on the color effect and avoiding pinholes and air bubbles
CN104291684AActive Publication Date: 2015-01-21江苏鑫宝门窗制造有限公司
4 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
江苏鑫宝门窗制造有限公司
Publication Date
2015-01-21

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention provides a frit particle binder and a preparation method thereof. The frit particle binder comprises the following components by mass fraction: 6.5-7.5% of nonionic polyurethane associative thickening agent, 3.2-4.4% of white carbon black, 1-1.5% of defoaming agent, 0.3-1.3% of dispersing agents and the balance of solvents. A using method of the frit particle binder comprises the steps of uniformly mixing frit particles with the frit particle binder and applying the mixture to the surface of a green body. The other using method of the frit particle binder comprises the steps of firstly laying the frit particles on the surface of the green body according to a designed pattern and then spraying or glazing a layer of frit particle binder on the surfaces of frit particles. By adopting the frit particle binder provided by the invention, the problem that the frit particles face a preheating zone at low negative pressure and are easy to suck away when entering a kiln to be fired is solved. The preparation method of the frit particle binder is simple in production equipment and process.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the technical field of architectural ceramics, in particular to a frit particle binder and a preparation method thereof. Background technique

[0002] With the development of frit particles with various decorative effects, the application of different decorative effects played by distributing frit particles on adobe is more and more favored by manufacturers, and the market it brings is also immeasurable. At present, it is mainly to spread a certain thickness of frit particles (particle size is 15-150 mesh) on the surface of the green body or the glaze surface by means of cloth, and spray a layer of fixing agent to fix the particles on the surface of the green body. When reprocessing the glazed surface, the quality of frit particles directly determines the quality of brick decoration. In production, too small particles are easy to introduce pinholes or air bubbles during firing, and more importantly, fine particles (especially ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More