A kind of molten steel thin slag agent and production method thereof

A production method and technology of thin slag agent, which are applied in the field of molten steel thin slag agent, can solve problems such as affecting the quality of finished steel and unsatisfactory thin slag effect, and achieve improved slag removal effect, strong slag accumulation ability, and strong thin slag performance. Effect

Active Publication Date: 2016-06-15
海城市金福锋科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the molten steel thinner slag agent is used to react with the residue to reduce the melting point and viscosity of the residue, improve the fluidity of the slag, remove the slag hanging on the wall, absorb the inclusions in the steel, and purify the molten steel. Above, the effect of dilute slag is still not ideal, which greatly affects the quality of finished steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A molten steel thin slag agent, which is composed of the following components in proportion by weight: 30 parts of potassium feldspar, 50 parts of low-sodium feldspar, and 20 parts of fused silica sand;

[0025] K in the potassium feldspar 2 O content 2 O content 3-5%, SiO 2 The content of > 65%; K in low sodium feldspar 2 O content 2 O content 2 The content of > 65%; SiO in fused silica sand 2 content > 99%;

[0026] The production method of molten steel thin slag agent, the steps are as follows:

[0027] 1) Process potassium feldspar and low-sodium feldspar into fine powder with particle size of 1-0mm respectively, and process fused silica sand into fine powder with particle size of 1.5-0mm;

[0028] 2) Stir and mix the above powder according to the proportion, and pack the finished product into bags.

Embodiment 2

[0030] A molten steel thin slag agent, which is composed of the following components in proportion by weight: 40 parts of potassium feldspar, 45 parts of low-sodium feldspar, and 15 parts of fused silica sand;

[0031] K in the potassium feldspar 2 O content 2 O content 3-5%, SiO 2 The content of > 65%; K in low sodium feldspar 2 O content 2 O content 2 The content of > 65%; SiO in fused silica sand 2 content > 99%;

[0032] The production method of molten steel thin slag agent, the steps are as follows:

[0033] 1) Process potassium feldspar and low-sodium feldspar into fine powder with particle size of 1-0mm respectively, and process fused silica sand into fine powder with particle size of 1.5-0mm;

[0034] 2) Stir and mix the above powder according to the proportion, and pack the finished product into bags.

Embodiment 3

[0036] A molten steel thin slag agent, which is composed of the following components in proportion by weight: 50 parts of potassium feldspar, 40 parts of low-sodium feldspar, and 10 parts of fused silica sand;

[0037] K in the potassium feldspar 2 O content 2 O content 3-5%, SiO 2 The content of > 65%; K in low sodium feldspar 2 O content 2 O content 2 The content of > 65%; SiO in fused silica sand 2 content > 99%;

[0038] The production method of molten steel thin slag agent, the steps are as follows:

[0039] 1) Process potassium feldspar and low-sodium feldspar into fine powder with particle size of 1-0mm respectively, and process fused silica sand into fine powder with particle size of 1.5-0mm;

[0040] 2) Stir and mix the above powder according to the proportion, and pack the finished product into bags.

[0041] The physical and chemical indicators of the molten steel thin slag agent finished product of above-mentioned embodiment 1-3 are:

[0042] Chemical Composi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a slag fluxing agent for molten steel and a production method of the slag fluxing agent. The slag fluxing agent comprises components in parts by weight as follows: 30-50 parts of potassium feldspar, 30-50 parts of low albite and 10-20 parts of fused quartz sand, wherein in the potassium feldspar, the content of K2O is smaller than 10%, the content of Na2O is 3%-5%, and the content of SiO2 is larger than 65%; in the low albite, the content of K2O is smaller than 1%, the content of Na2O is smaller than 10%, and the content of SiO2 is larger than 65%; the content of SiO2 in the fused quartz sand is larger than 99%. The slag fluxing agent has high slag accretion capability, can cleanly remove slag, reduces iron loss, improves the slag removal effect, can remove wall hanging residues, absorbs inclusions in steel, purifies the molten steel and has high slag fluxing performance; the content of original slag accounting for about 5% of the molten steel can be reduced to about 1% after slag fluxing, the quality of steel is improved to a great extent, and use demands of a user are met.

Description

technical field [0001] The invention relates to smelting flux materials, in particular to a molten steel thin slag agent and a production method thereof. Background technique [0002] At present, the widely used steelmaking methods mainly include intermediate frequency furnace steelmaking and electric furnace steelmaking. With the continuous progress of steelmaking technology, users' requirements for steel quality continue to increase. During the steelmaking process of intermediate frequency furnace steelmaking and electric furnace steelmaking, the slag content of molten steel is about 5%. At present, the molten steel thinner slag agent is used to react with the residue to reduce the melting point and viscosity of the residue, improve the fluidity of the slag, remove the slag hanging on the wall, absorb the inclusions in the steel, and purify the molten steel. Above, the effect of dilute slag is still unsatisfactory, which greatly affects the quality of finished steel prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C5/54
Inventor 王相丰裘伟王维
Owner 海城市金福锋科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com