A kind of waterproof and moisture-permeable polyurethane thermoplastic elastomer and preparation method thereof

A thermoplastic elastomer, waterproof and moisture-permeable technology, applied in the field of thermoplastic elastomers, can solve the problems of high cost unit price, difficult to degrade in nature, difficult production process, etc., and achieve the effects of low production cost, convenient operation control and high production efficiency

Active Publication Date: 2018-09-28
东莞宏石功能材料科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The production process of traditional polytetrafluoroethylene composite film is not easy and the cost is high, it is difficult to be degraded by nature, and the combustion temperature is as high as 405°C. Large-scale use makes polytetrafluoroethylene composite film gradually become a killer of the environment and other side effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of waterproof and moisture-permeable polyurethane thermoplastic elastomer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A waterproof and moisture-permeable polyurethane thermoplastic elastomer, the waterproof and moisture-permeable polyurethane thermoplastic elastomer is made of polyurethane granules, and the polyurethane granules are composed of the following raw materials in parts by weight:

[0042] 50 parts of polyester polyol or polyether polyol

[0043] 40 parts of diisocyanate

[0044] 10 parts of chain extender;

[0045] Among them, polyester polyol is made of polybasic acid and polyol according to the molar ratio of 1:1.01 through dealcoholization and dehydration polycondensation by vacuum melting method. Its hydroxyl value is 20mgKOH / g and acid value is 0.1mgKOH / g.

[0046] The polybasic acid is a mixture of azelaic acid, terephthalic acid and isophthalic acid in a weight ratio of 2:0.5:1.4.

[0047] The polyhydric alcohol is ethylene glycol, 1,3-butanediol, 1,4-butanediol, diethylene glycol, neopentyl glycol, 2-methyl-1,3-propanediol, hexanediol, 3 -Methyl 1,5-pentanediol, ...

Embodiment 2

[0055] A waterproof and moisture-permeable polyurethane thermoplastic elastomer, the waterproof and moisture-permeable polyurethane thermoplastic elastomer is made of polyurethane granules, and the polyurethane granules are composed of the following raw materials in parts by weight:

[0056] 60 parts of polyester polyol or polyether polyol

[0057] 32.5 parts of diisocyanate

[0058] 7.5 parts of chain extender;

[0059] Among them, polyester polyol is made of polybasic acid and polyol according to the molar ratio of 1:1.05 through dealcoholization and dehydration polycondensation by vacuum melting method. Its hydroxyl value is 40mgKOH / g and acid value is 0.5mgKOH / g.

[0060] The polybasic acid is succinic acid, adipic acid, azelaic acid, sebacic acid, terephthalic acid, isophthalic acid or maleic acid.

[0061] Described polyhydric alcohol is made of 1,3-butanediol, 2-methyl-1,3-propanediol, 3-methyl 1,5-pentanediol and 1,4-cyclohexanedimethanol with weight ratio 1: A mixt...

Embodiment 3

[0069] A waterproof and moisture-permeable polyurethane thermoplastic elastomer, the waterproof and moisture-permeable polyurethane thermoplastic elastomer is made of polyurethane granules, and the polyurethane granules are composed of the following raw materials in parts by weight:

[0070] 70 parts of polyester polyol or polyether polyol

[0071] 25 parts diisocyanate

[0072] 5 parts of chain extender;

[0073] Among them, polyester polyol is made of polybasic acid and polyol according to the molar ratio of 1:1.1 through dealcoholization and dehydration polycondensation by vacuum melting method. Its hydroxyl value is 70mgKOH / g and acid value is 1mgKOH / g.

[0074] The polybasic acid is a mixture of azelaic acid, terephthalic acid and isophthalic acid in a weight ratio of 3:1:1.8.

[0075] Described polyhydric alcohol is made of 1,3-butanediol, 2-methyl-1,3-propanediol, 3-methyl 1,5-pentanediol and 1,4-cyclohexanedimethanol with weight ratio 1: A mixture composed of 1:1.8:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
acid valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of the thermoplasticity elastomer, in particular to a water-proof moisture-permeable polyurethane thermoplasticity elastomer and a preparation method thereof. The water-proof moisture-permeable polyurethane thermoplasticity elastomer is prepared from polyurethane colloidal particles, wherein the polyurethane colloidal particles are prepared from the following raw materials in parts by weight: 40-90 parts of polyester polyol or polyether polyol, 15-45 parts of diisocyanate and 3-12 parts of chain extender; the polyester polyol is obtained in a way that at least one of polyatomic acid and polyester and polyhydric alcohol are subjected to dealcoholization and dehydration condensation according to a mole ratio of 1to (1.01-1.2) in a vacuum fusion method, the hydroxyl value of the polyester polyol is 20-120mgKOH / g, and the acid value of the polyester polyol is 0.1-2mgKOH / g. The thermoplasticity elastomer has the advantages of good plasticization processing, high natural degradation speed and environmental protection, can be regulated according to the moisture-permeable requirements and can also resist bacteria and avoid dust mists.

Description

technical field [0001] The invention relates to the technical field of thermoplastic elastomers, in particular to a waterproof and moisture-permeable polyurethane thermoplastic elastomer and a preparation method thereof. Background technique [0002] The production process of traditional polytetrafluoroethylene composite film is not easy and the cost is high, it is difficult to be degraded by nature, and the combustion temperature is as high as 405 ℃. Large-scale use makes polytetrafluoroethylene composite film gradually become a killer of the environment and other side effects. Contents of the invention [0003] In order to overcome the shortcomings and deficiencies in the prior art, the object of the present invention is to provide a waterproof and moisture-permeable polyurethane thermoplastic elastomer, which is well plasticized and processed, can be adjusted according to moisture permeability requirements, and has a fast natural degradation rate , green and environment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/76C08G18/73C08G18/75C08G18/66C08G18/42C08G18/48
CPCC08G18/664C08G18/6674C08G18/724C08G18/73C08G18/755C08G18/7614C08G18/7671
Inventor 黄聪杰
Owner 东莞宏石功能材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com