Liquid crystal display element, liquid crystal alignment film and liquid crystal alignment treatment agent

A technology of liquid crystal alignment film and liquid crystal alignment, which can be used in instruments, optics, nonlinear optics, etc., and can solve problems such as high power consumption

Active Publication Date: 2019-06-07
NISSAN CHEM CORP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this standard type device needs to constantly apply a voltage in order to obtain a transmissive state, so it consumes a lot of power when it is used in many cases in a transparent state, such as window glass, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid crystal display element, liquid crystal alignment film and liquid crystal alignment treatment agent
  • Liquid crystal display element, liquid crystal alignment film and liquid crystal alignment treatment agent
  • Liquid crystal display element, liquid crystal alignment film and liquid crystal alignment treatment agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0333] The following examples are given to illustrate the present invention in more detail, but they are not limitedly interpreted.

[0334] "Abbreviations of Compounds Used in Synthesis Examples, Examples, and Comparative Examples"

[0335] L1 (liquid crystal): MLC-6608 (manufactured by MERCK CORPORATION)

[0336] R1 (polymerizable compound): a compound represented by the following formula [R1]

[0337] P1 (photoinitiator): a compound represented by the following formula [P1]

[0338]

[0339] (specific side chain type diamine compound)

[0340] A1: 1,3-diamino-4-[4-(trans-4-n-heptylcyclohexyl)phenoxy]benzene

[0341] A2: 1,3-diamino-4-[4-(trans-4-n-heptylcyclohexyl)phenoxymethyl]benzene

[0342] A3: 1,3-diamino-4-{4-[trans-4-(trans-4-n-pentylcyclohexyl)cyclohexyl]phenoxy}benzene

[0343] A4: Diamine compound represented by the following formula [A4]

[0344] A5: 1,3-diamino-4-octadecyloxybenzene

[0345]

[0346] (Second diamine compound)

[0347] B1: 3,5-diami...

Synthetic example 1

[0399] Mix D1 (2.96g, 15.1mmol), A1 (2.91g, 7.65mmol), B1 (0.93g, 6.11mmol) and C2 (0.17g, 1.57mmol) in NEP (21.0g) and react at 40°C for 8 hours , A polyamic acid solution (1) having a resin solid content concentration of 25% by mass was obtained. The number average molecular weight of this polyamic acid was 23,600, and the weight average molecular weight was 71,800.

Synthetic example 2

[0401] Mix D2 (3.83g, 15.3mmol), A2 (6.04g, 15.3mmol) and B1 (2.33g, 15.3mmol) in NMP (26.4g), react at 50°C for 2 hours, add D1 (2.94g, 15.0 mmol) and NMP (23.8 g) were reacted at 40° C. for 6 hours to obtain a polyamic acid solution (2) whose resin solid content concentration was 25% by mass. The number average molecular weight of this polyamic acid was 22,500, and the weight average molecular weight was 67,100.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

Provided are: a liquid crystal display element that shows high adhesion between a liquid crystal layer and a vertical liquid crystal alignment film and excellent vertical alignment properties of a liquid crystal and has good optical characteristics such as transparency in the no voltage-applied state and scattering properties in the voltage-applied state; a vertical liquid crystal alignment film to be used in the liquid crystal display element; and a liquid crystal aligning agent therefor. The liquid crystal display element is provided with the liquid crystal alignment film that is obtained using the liquid crystal aligning agent containing component (A) and component (B). Component (A): a polymer containing at least one structure selected from the group consisting of an aliphatic ring, an aromatic ring and a linear alkyl group and having a side chain that is capable of vertically aligning a liquid crystal. Component (B): at least one generator selected from the group consisting of a photo radical generator, a photo acid generator and a photo base generator.

Description

technical field [0001] The present invention relates to a transmissive-scattering type liquid crystal display element that is transparent when no voltage is applied and that is scattered when voltage is applied, a liquid crystal alignment film used in the liquid crystal display element, and a liquid crystal alignment treatment agent for forming the liquid crystal alignment film. Background technique [0002] As a liquid crystal display element using a liquid crystal material, a TN (twisted nematic, Twisted Nematic) mode is actually used. This mode utilizes the optical rotation characteristics of liquid crystals to switch light, and a polarizing plate is required when used as a liquid crystal display element. However, the utilization efficiency of light becomes low due to the use of the polarizing plate. [0003] As a liquid crystal display element with high light utilization efficiency without using a polarizing plate, there is a liquid crystal display element that switches...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02F1/1337C08G73/10C08G77/04G02F1/1334
CPCC08G77/14C08G77/20C08G77/26C08G77/80G02F1/1334G02F1/1337G02F1/13347G02F1/133742
Inventor 三木徳俊片山雅章巴幸司菊池奈穂保坂和義
Owner NISSAN CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com