Alumina ceramic wafer treatment process

A kind of technology of alumina ceramics and processing technology, which is applied in the direction of chemical instruments and methods, cleaning methods and utensils, and cleaning methods using liquids, etc., which can solve the problems of smooth surface, small friction coefficient, inability to bond ceramic sheets and rubber, and poor bonding. Firmness and other issues, to achieve the effect of strong surface adsorption, light weight, and prolong the service life of the equipment

Inactive Publication Date: 2016-07-06
解伟伟
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much superior. Ordinary ceramic sheets and rubber cannot be bonded together. After using glue, the bond is not firm, and the ceramic sheets need to be processed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A process for treating alumina ceramic sheets, the steps are as follows:

[0027] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0028] (2) Ketone washing: Soak the cleaned ceramic sheet in 20% acetone for half an hour and dry it;

[0029] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 80% sodium carbonate solution for half an hour and dry it;

[0030] (4) Pickling: Soak the ceramic sheet dried in step (3) in 8% sulfuric acid solution and dry.

Embodiment 2

[0032] A process for treating alumina ceramic sheets, the steps are as follows:

[0033] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0034] (2) Ketone washing: Soak the cleaned ceramic sheet in 25% acetone for half an hour and dry it;

[0035] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 85% sodium carbonate solution for half an hour and dry it;

[0036] (4) Pickling: Soak the ceramic sheet dried in step (3) in 10% sulfuric acid solution and dry.

Embodiment 3

[0038] A process for treating alumina ceramic sheets, the steps are as follows:

[0039] (1) Cleaning with distilled water: Place the ceramic piece in 100% pure water for cleaning and drying;

[0040] (2) Ketone washing: Soak the cleaned ceramic sheet in 30% acetone for half an hour and dry it;

[0041] (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 90% sodium carbonate solution for half an hour and dry it;

[0042] (4) Pickling: Soak the ceramic sheet dried in step (3) in 12% sulfuric acid solution and dry.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

A treatment process for alumina ceramic sheets, the steps are as follows: (1) Distilled water cleaning: wash and dry the ceramic sheets in 100% pure water; (2) Ketone washing: place the cleaned ceramic sheets in 20‑30 % acetone and dried; (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 80-90% sodium carbonate solution and dry; (4) Pickling: Dry the ceramic sheet in step (3) The ceramic sheet is placed in 8‑12% sulfuric acid solution for soaking and drying; the beneficial effects of the present invention are: high hardness, excellent wear resistance, light weight, and strong surface adsorption, which is the surface adsorption of untreated ceramic sheet The strength is 10‑20, and it is very strong and durable after being combined with glue and rubber.

Description

technical field [0001] The invention relates to the technical field of alumina ceramic sheet processing, in particular to an alumina ceramic sheet processing process. Background technique [0002] Alumina ceramics: high alumina content, relatively dense structure, and special properties, so it is called special ceramics. Al2O3. The ceramic material is a close-packed hexagonal structure composed of oxygen ions, and aluminum ions fill two-thirds of the octahedral gaps. This is the same stable α-Al2O3 structure as natural corundum, so the ceramic has a high melting point and high Hardness, with excellent wear resistance. The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much super...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/80B08B3/04B08B3/08
CPCC04B41/00B08B3/04B08B3/08C04B41/009C04B41/80
Inventor 解伟伟
Owner 解伟伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap