A kind of technology of alumina ceramics and processing technology, which is applied in the direction of chemical instruments and methods, cleaning methods and utensils, and cleaning methods using liquids, etc., which can solve the problems of smooth surface, small friction coefficient, inability to bond ceramic sheets and rubber, and poor bonding. Firmness and other issues, to achieve the effect of strong surface adsorption, light weight, and prolong the service life of the equipment

Inactive Publication Date: 2016-05-11
解全义
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much superior. Ordinary ceramic sheets and rubber cannot be bonded together. After using glue, the bond is not firm, and the ceramic sheets need to be processed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A process for processing alumina ceramic chips, the steps are as follows:

[0023] (1) Cleaning with distilled water: Place the ceramic pieces in 100% pure water for cleaning and drying;

[0024] (2) Ketone washing: soak the cleaned ceramic pieces in 20% acetone for half an hour and dry;

[0025] (3) Alkaline washing: soak the ketone-washed ceramic pieces in 90% sodium carbonate solution for half an hour, and dry.

Embodiment 2

[0027] A process for processing alumina ceramic chips, the steps are as follows:

[0028] (1) Cleaning with distilled water: Place the ceramic pieces in 100% pure water for cleaning and drying;

[0029] (2) Ketone washing: soak the cleaned ceramic pieces in 25% acetone for half an hour and dry;

[0030] (3) Alkaline washing: soak the ketone-washed ceramic pieces in a 95% sodium carbonate solution for half an hour and dry.

Embodiment 3

[0032] A process for processing alumina ceramic chips, the steps are as follows:

[0033] (1) Cleaning with distilled water: Place the ceramic pieces in 100% pure water for cleaning and drying;

[0034] (2) Ketone washing: soak the cleaned ceramic pieces in 30% acetone for half an hour and dry;

[0035] (3) Alkaline washing: The ketone-washed ceramic pieces are soaked in 100% sodium carbonate solution for half an hour and dried.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a treatment process for an aluminum oxide ceramic chip. The treatment process comprises the following step one of distilled water washing, wherein the ceramic chip is placed into 100% pure water to be washed and dried; the step two of acetone washing, wherein the washed ceramic chip is placed into acetone with the concentration being 20-30% to be soaked and dried; the step three of alkaline washing, wherein the ceramic chip subjected to acetone washing is placed into a sodium carbonate solution with the concentration being 90-100% to be soaked and dried. The treatment process has the advantages that hardness is high, a wear-resisting property is excellent, the weight is low, surface adsorption force is large and is 10-20 times that of an untreated ceramic chip, and after being combined with rubber through glue, the ceramic chip is extremely firm and durable.

Description

Technical field [0001] The invention relates to the technical field of alumina ceramic sheet processing, in particular to an alumina ceramic sheet processing technology. Background technique [0002] Alumina ceramics: high alumina content, relatively dense structure and special properties, so it is called special ceramics. Al2O3. The ceramic material is a close-packed hexagonal structure composed of oxygen ions, and aluminum ions are filled in two-thirds of the octahedral gap. This is the same stable α-Al2O3 structure as natural corundum, so ceramics have a high melting point and high Hardness and excellent wear resistance. The hardness of the ceramic patch is ≥HRA85, second only to the hardness of diamond, and the surface is smooth and the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the ceramic patch material has better performance than other metal materials. It is much more supe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/80B08B3/04B08B3/08
CPCC04B41/00B08B3/04B08B3/08C04B41/009C04B41/80
Inventor 解全义
Owner 解全义
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap