hemostatic material

A hemostatic material and fiber technology, applied in bandages, surgery, drug delivery, etc., can solve the problems of insufficient fiber absorption, no antibacterial performance, harsh reaction conditions, etc., to achieve good liquid absorption performance and antibacterial performance, good vertical The effect of absorption performance and mild reaction conditions

Active Publication Date: 2019-08-06
JIANGSU NEWVALUE MEDICAL PROD CO LTD +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these modification methods, on the one hand, have harsh reaction conditions, cumbersome steps, and are not easy to control; on the other hand, the distribution position and quantity of substituents on the molecular chain of the product obtained from the reaction are uncertain, making it difficult to effectively control the liquid absorption performance of the product.
In addition, the above products do not have antimicrobial properties either
These problems will greatly limit the clinical application of dressings prepared from chitin fibers, especially in the treatment of burns and chronic wounds.
[0005] In particular, in the past chitin fibers, people often control the liquid absorption performance of the fiber by controlling the degree of substitution, but the inventors of the present invention found that if the substitution is too low, the liquid absorption of the fiber is insufficient, and if the substitution is too high, Although the liquid absorption is significantly increased, the fiber shape is difficult to maintain, that is, the fibers will be dissolved or dispersed by the absorbed liquid
At this time, the outflow of liquid will cause a certain degree of loss of suction function.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • hemostatic material
  • hemostatic material
  • hemostatic material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0112] Weigh 5g of chitin fiber with a length of 6cm and p / (m+n+p) of 0.25, disperse it in 50mL of isopropanol, add 2.54g of 2-hydroxyethyl acrylate, and shake well at room temperature at 50℃ Under the conditions of constant temperature water bath for 48h, separate the reacted chitin fiber and the reaction mixture, wash twice with 80% (v / v) methanol aqueous solution, take out the fiber, spin dry, and disperse in 80% (v / v) v) Add 30% (w / v) potassium hydroxide aqueous solution dropwise to methanol aqueous solution, adjust the pH of the methanol and potassium hydroxide aqueous solution mixture to 11.0, soak for 1 hour, and then separate the soaked fiber from the mixture , Washed 3 times with 80% (v / v) methanol aqueous solution, dehydrated, and dried at 40°C to obtain a liquid-absorbent fiber with a viscosity average molecular weight (Mη) of 3 million and a degree of substitution of the total acryloyl substance of 0.17.

[0113] Dissolve the absorbent fiber in 1% CD 3 COOD's D 2 In O...

Embodiment 2

[0115] Weigh 5 g of chitin fibers with a length of 6 cm and a p / (m+n+p) of 0.10, disperse them in 50 mL of isopropanol, add 7.09 g of 2-hydroxypropyl acrylate, and shake well at room temperature at 70°C Under the conditions of constant temperature water bath for 48h, separate the reacted chitin fiber and the reaction mixture, wash twice with 80% (v / v) methanol aqueous solution, take out the fiber, spin dry, and disperse in 80% (v / v) v) Add 30% (w / v) potassium hydroxide aqueous solution dropwise to methanol aqueous solution, adjust the pH of the methanol and potassium hydroxide aqueous solution mixture to 11.0, soak for 1 hour, and then separate the soaked fiber from the mixture , Washed 3 times with 80% (v / v) methanol aqueous solution, dehydrated, and dried at 40°C to obtain a liquid-absorbent fiber with a viscosity average molecular weight of 3 million and a degree of substitution of acryloyl groups of 0.30.

[0116] Dissolve the absorbent fiber in 1% CD 3 COOD's D 2 In O, -NCH ...

Embodiment 3

[0118] Weigh 5 g of chitin fibers with a length of 6 cm and a p / (m+n+p) of 0.10, disperse them in S0 mL of isopropanol, add 14.17 g of 2-hydroxypropyl acrylate, and shake well at room temperature at 70°C Under the conditions of constant temperature water bath for 48h, separate the reacted chitin fiber and the reaction mixture, wash twice with 80% (v / v) methanol aqueous solution, take out the fiber, spin dry, and disperse in 80% (v / v) v) Add 30% (w / v) potassium hydroxide aqueous solution dropwise to methanol aqueous solution, adjust the pH of the methanol and potassium hydroxide aqueous solution mixture to 11.5, soak for 1 hour, and then separate the soaked fiber from the mixture , Spin dry, and put in saturated CaCl 2 Soak in the solution for 1 hour, take out the fiber, wash it 3 times with 80% (v / v) methanol aqueous solution, and then dry it at 40°C after dehydration to obtain a viscosity average molecular weight of 500,000 and a degree of substitution of the total acryloyl sub...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention aims to provide fiber suitable for clinical application, in particular to the application of hemostasis, scalding, chronic wound treatment and others. The invention is a hemostatic material, wherein the hemostatic material includes fiber, and the material is possessed of biodegradability; the hemostatic material is characterized in that the fiber includes a polymer expressed by the following structural formula: FORMULA, wherein R is at least one of groups consisting of -NH2, -CH2CH20H, -OCH2CH2CH2OH, -OH, -ONa, -OK, -OCa; m, n and p respectively represent the quantity percent of corresponding repeat unit in the polymer molecule and can meet the following relationship formula: m+n+p=1, p / (m+n+p)=0.05-0.30; the degree of substitution D is defined as m / (m+n+p), the total degree of substitution of fiber is defined as Ds, and the degree of substitution of polymer at the center of the fiber cross section is defined as D0; when the degree of substitution of the edge of the fiber cross section is defined as D, the following relationship formula can be satisfied: Ds=0.09-0.8, Do / D=0-0.7.

Description

Technical field [0001] The present invention relates to a hemostatic material, in particular, to a hemostatic material containing fibers that can absorb liquid through swelling, and the material can be degraded in the human body. Background technique [0002] Chitin has good biocompatibility, biodegradability, hemostasis, and promotion of wound healing. It can absorb various tissue engineering scaffold materials such as surgical sutures, wound dressings, drug carrier materials, artificial skin, etc. China has a wide range of application prospects. [0003] The chitin is dissolved in organic or inorganic acid to form a viscous colloid. After spinning, coagulation, washing, drying and other processes, chitin fibers can be prepared for preparation of wound dressings. Chinese patent document CN1129748A (chitin fiber and its production method and application), Chinese patent document CN1149093A (chitin fiber and its preparation method), Chinese patent document CN101250759A (medical chi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L15/28A61L15/42A61L15/44A61L24/00A61L24/08D01F9/00
CPCA61L15/28A61L15/42A61L15/44A61L24/001A61L24/08A61L2300/232A61L2400/04D01F9/00C08L5/08
Inventor 周应山徐礼勤龚祖光杨柳清王立平蒋锐
Owner JIANGSU NEWVALUE MEDICAL PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com