Low-temperature curing hammer tone powder coating and preparation method thereof

A powder coating and low-temperature technology, which is applied in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of high curing temperature and cannot be popularized, and achieves simple preparation methods, suitable for large-scale production and application, and good artistic effect

Active Publication Date: 2017-02-15
ANHUI MEIJIA NEW MATERIAL
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commonly used thermosetting and thermoplastic powder coatings are generally baked at a temperature above 180°C and cured for about 20 minutes. Such a high curing temperature limits the application of powder coatings to heat-resistant substrates such as metals; in the field of heat-sensitive substrates, due to its curing The temperature is too high to promote

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature curing hammer tone powder coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The technical solutions in the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention. The following examples are only used to illustrate the technical solution of the present invention more clearly, but not to limit the protection scope of the present invention.

[0023] A low temperature curing hammer grain powder coating

[0024] In terms of parts by mass, it includes the following components: 25-40 parts of polyester resin, 25-40 parts of epoxy resin, 10-25 parts of titanium dioxide, 10-20 parts of filler, 0.1-0.3 parts of hammering agent, 0.00 parts of pigment ~5 parts, low-temperature curing accelerator 0.5~2.0 parts.

[0025] As shown in the table below, each component in the preferred embodiments is expressed in parts by mass.

[0026] components Example 1 Example 2 Example 3 Example 4 Example 5 polyester resin 30 30 30 30 30 epoxy resin 30 30 30 30 30...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
epoxy equivalentaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-temperature curing hammer tone powder coating, which is prepared from the following ingredients in parts by mass: 25-40 parts of polyester resin, 25-40 parts of epoxy resin, 10-25 parts of titanium pigment, 10-20 parts of a padding, 0.1-0.3 part of a hammer tone agent, 0-5 parts of a pigment and 0.5-2.0 parts of a low-temperature curing accelerant. The polyester resin and the low-temperature curing accelerant are matched for use, so that the curing temperature of the powder coating is 120-140 DEG C, and the curing time of the powder coating is 20min; the hammer tone agent is a modified cellaburate polymer; the mass ratio of polyester resin to epoxy resin is 1:1. The invention also provides a preparation method of the powder coating. The low-temperature curing powder coating prepared by the method has the advantages that the application range of the powder coating is enlarged to include heat-sensitive materials; the application range is expanded, and the powder coating has a hammer tone effect and favorable artistic quality and conforms to the modern aesthetic appreciation demand.

Description

technical field [0001] The invention relates to a powder coating, in particular to a low-temperature curing hammer grain powder coating. Background technique [0002] Powder coating has the advantages of environmental friendliness, low production cost and simple production process, and its application range is increasing. Commonly used thermosetting and thermoplastic powder coatings are generally baked at a temperature above 180°C and cured for about 20 minutes. Such a high curing temperature limits the application of powder coatings to heat-resistant substrates such as metals; in the field of heat-sensitive substrates, due to its curing The temperature is too high to promote. In addition, with the improvement of people's living standards, the requirements for quality of life also increase; powder coatings with hammer effect can cover the defects of the substrate, and at the same time, the appearance is closer to the needs of the public. Therefore, the application of hamme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D163/00C09D5/28C09D5/03C09D7/12
CPCC08L2205/03C09D5/033C09D5/28C09D163/00C09D167/00C08L63/00C08L1/14C08K2003/2241C08K5/3445C08L67/00
Inventor 王方银王峰张雪梅
Owner ANHUI MEIJIA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap