Frit dry granules with characteristics of one-time sintering and golden brown color, and preparation method thereof

A technology of brown and frit, which is applied in the field of once-fired golden brown frit dry granules and its preparation, can solve the problems of occupying warehouse storage space, increasing the labor load of employees, and reducing the qualified rate of products, so as to reduce employees and improve quality. The effect of controlling the degree and improving production efficiency

Active Publication Date: 2013-07-31
GUANGDONG DOWSTONE TECH
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the low-temperature glaze firing cycle is generally about 160 minutes, it is several times slower than the high-temperature biscuit firing time (50-70 minutes) of the first firing, which will cause a lot of inconvenience in production
Firstly, the cost of firing is higher than that of general one-time firing; in addition, the bricks supplied by the bisque firing line are larger than the demand of the glaze firing line, and the excess bricks need to be removed manually, and then mov

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Frit dry granules with characteristics of one-time sintering and golden brown color, and preparation method thereof
  • Frit dry granules with characteristics of one-time sintering and golden brown color, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Weigh 10 parts of albite, 10 parts of lithium porcelain stone, 28 parts of quartz, 6 parts of limestone, 21 parts of dolomite, 10 parts of barium carbonate, 8 parts of non-calcined alumina, 5 parts of raw zinc oxide, 3 parts of fluorite, 6 parts of golden brown material, mixed uniformly, melted at 1460℃, kept for 3 hours, discharged water quenched, dried, and granulated to make the particle fineness of 10-30 meshes to obtain golden brown frit dry particles, such as figure 1 Shown

Embodiment 2

[0033] Weigh 7 parts of albite, 6 parts of lithium porcelain stone, 28 parts of quartz, 4 parts of limestone, 18 parts of dolomite, 8 parts of barium carbonate, 10 parts of non-calcined alumina, 8 parts of raw zinc oxide, 2 parts of fluorite, 3 parts of golden brown material, mixed uniformly, melted at a temperature of 1480°C, kept for 2.5 hours, discharged with water, quenched, dried, and granulated to make the particle fineness 10-30 meshes to obtain golden brown frit dry particles.

Embodiment 3

[0035] Weigh 12 parts of albite, 9 parts of lithium porcelain stone, 25 parts of quartz, 6 parts of limestone, 21 parts of dolomite, 8 parts of barium carbonate, 8 parts of non-calcined alumina, 7 parts of raw zinc oxide, 4 parts of fluorite, 4 parts of golden brown material, mixed uniformly, melted at a temperature of 1450°C, kept for 3 hours, discharged water quenched, dried and granulated to make the particle fineness 10-30 meshes to obtain golden brown frit dry particles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The present invention discloses frit dry granules with characteristics of one-time sintering and golden brown color, and a preparation method thereof. Raw materials for preparing the frit dry granules comprise sodium feldspar, lithium porcelain stone, quartz, limestone, dolomite, barium carbonate, non-calcined alumina, raw zinc oxide, fluorite, and a golden brown material. The frit dry granules have characteristics of high melting point, good high temperature flowability, suitable expansion coefficient, wide sintering range, good combination with a ceramic blank, one-time sintering, golden brown color, good gloss, translucent property, shining under light irradiation, and good artistic effect.

Description

technical field [0001] The invention belongs to the technical field of ceramic frit production, in particular to a dry granule of once-fired golden brown frit and a preparation method thereof. Background technique [0002] The natural stone texture is soft, beautiful and elegant, with elegant style. However, large-scale natural stone is extremely scarce and has certain radioactivity. Glass-ceramics is a mixture of microcrystals and glass formed by sintering and crystallizing glass with a certain particle size distribution. The texture is firm and crystal clear. However, glass-ceramic is relatively single in the pattern design process. Antique bricks can make up for this, and thousands of designs can be obtained through micro-powder cloth, screen, roller or inkjet technology to satisfy more consumers. But it does not have the spatial three-dimensionality and crystal clearness of stone and glass-ceramic. The microcrystalline brick is a new type of product that can combine...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/20
Inventor 詹经王永健
Owner GUANGDONG DOWSTONE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap