Double-deck combined type floor

A composite flooring technology, applied in the direction of insulation, floors, buildings, etc., can solve the problems of high production cost, damage to the ecological environment, glue opening and deformation, etc., to eliminate internal stress, reduce weight, and increase adhesion Effect

Active Publication Date: 2018-04-27
ANHUI YINUO WOOD PLASTIC SHEET TECH CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the shortcomings of the existing two-layer composite wood floor, which is high in production cost, destroys the ecological environment, and is prone to glue opening and deformation, and provides a double-layer composite floor, which reduces the The production cost is lower, the ecological environment is protected, and the occurrence of double-layer composite floor glue opening and deformation is effectively avoided.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-deck combined type floor
  • Double-deck combined type floor
  • Double-deck combined type floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] combine figure 1 , The double-layer composite floor of this embodiment is formed by bonding the panel 2 of the upper layer and the substrate 1 of the lower layer, the panel 2 is a solid wood board, and the substrate 1 is a PVC stone-plastic board. The upper surface of the panel 2 is an irregular wear-resistant surface with concave-convex patterns, and the top of the wear-resistant surface with concave-convex patterns is covered with a paint layer. The thickness of the substrate 1 is greater than that of the panel 2 . The upper surface of the substrate 1 is provided with a substrate glue storage tank 104 along the length direction. The substrate glue storage groove 104 is a groove with a V-shaped cross section. The substrate glue storage grooves 104 are adjacently arranged continuously along the width direction of the substrate 1. The two edges along the length direction of the substrate 1 are symmetrically provided with mutually inserted notch and protrusion structures...

Embodiment 2

[0050] combine figure 2 , The double-layer composite floor of this embodiment is formed by bonding the panel 2 of the upper layer and the substrate 1 of the lower layer, the panel 2 is a solid wood board, and the substrate 1 is a PVC stone-plastic board. The upper surface of the panel 2 is an irregular wear-resistant surface with concave-convex patterns, and the top of the wear-resistant surface with concave-convex patterns is covered with a paint layer. The thickness of the substrate 1 is greater than that of the panel 2 . The upper surface of the substrate 1 is provided with a substrate glue storage tank 104 along the length direction. The substrate glue storage groove 104 is a groove with an arc-shaped cross section. The substrate glue storage grooves 104 are adjacently arranged continuously along the width direction of the substrate 1. The two edges along the length direction of the substrate 1 are symmetrically provided with mutually inserted notch and protrusion struct...

Embodiment 3

[0052] combine image 3 , The double-layer composite floor of this embodiment is formed by bonding the panel 2 of the upper layer and the substrate 1 of the lower layer, the panel 2 is a solid wood board, and the substrate 1 is a PVC stone-plastic board. The upper surface of the panel 2 is an irregular wear-resistant surface with concave-convex patterns, and the top of the wear-resistant surface with concave-convex patterns is covered with a paint layer. The lower surface of the panel 2 is provided with a panel glue storage tank 201 along the length direction. The panel glue storage tank 201 is a groove with a V-shaped cross section. The thickness of the substrate 1 is greater than that of the panel 2 . The two edges along the length direction of the substrate 1 are symmetrically provided with mutually inserted notch and protrusion structures 101 , and the two edges of the substrate 1 along the width direction are also symmetrically provided with mutually inserted notch and p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a double-deck combined type floor, and belongs to the field of floors. The double-deck combined type floor is formed by bonding a faceplate of the upper deck and a baseplate ofthe lower deck, wherein the baseplate is made of a PVC stone plastic plate. The upper surface of the faceplate is of an irregular raised grain wearproof surface, and the upper part of the raised grain wearproof surface is covered with a paint coating layer. A baseplate rubber storage tank is arranged on the upper surface of the baseplate in the length direction. A notch structure and a convex opening structure which are in inserted connection with each other are symmetrically formed in the two edges of the baseplate in the length direction, and a notch structure and a convex opening structurewhich are in inserted connection with each other are similarly and symmetrically formed in the two edges of the baseplate in the width direction. The PVC stone plastic plate is made of a PVC stone plastic base material, and the PVC stone plastic base material is prepared by the following steps of step a, raw material mixing and heating; step b, pore generation; step c, extruding and forming; stepd, cooling and forming. According to the double-deck combined type floor, production cost of the double-deck combined type floor is reduced, ecological environment is protected, and the occurrence oftackless and deformation phenomena of the double-deck combined type floor is effectively avoided.

Description

technical field [0001] The invention relates to a floor, more specifically, to a double-layer composite floor. Background technique [0002] At present, composite solid wood flooring is mainly based on multi-layer solid wood composite, and its performance is closer to pure solid wood with three layers. The three-layer solid wood composite floor is composed of three layers of thin solid wood boards through a more complex process. When the three layers are composited, the thinner bottom and surface layer wood grains are arranged vertically, and the thicker middle layer wood grains are arranged horizontally, thus neutralizing the natural deformation of the wood. The surface layer of this three-layer solid wood composite floor is made of high-quality wood (such as: oak, maple, teak, Burmese mahogany, hickory and walnut, etc.), and the middle layer and bottom layer are fast-growing materials with better elasticity ( Such as: pine, poplar, etc.), can effectively solve a series o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/02E04F15/18
CPCE04F15/02038E04F15/181
Inventor 艾华
Owner ANHUI YINUO WOOD PLASTIC SHEET TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products