A kind of diatomite molding composition with hygroscopic function and preparation method thereof

A technology of diatomite and composition, which is applied in the preparation and application field of diatomite-based composite materials, can solve problems such as unfavorable surface cleaning, limitations of raw material formula and manufacturing process, and affect the effect of application, so as to reduce shedding Phenomenon, good water absorption performance, and the effect of improving the moisture absorption function

Active Publication Date: 2020-03-06
桂林良物造环境科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are companies at home and abroad that use diatomite to add composite materials to manufacture various molding composition products, but there are still certain limitations in raw material formulations and manufacturing processes, which affect the application effect.
Due to the strong hygroscopic function of the diatomite molding composition, the outer surfaces of various products made of the diatomite molding composition are prone to breed various bacteria, which is not conducive to keeping the surface of the diatomite molding composition product clean

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of diatomite molding composition with hygroscopic function and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1: Preparation of diatomite molding composition

[0025] The formula is: a diatomaceous earth molding composition with moisture absorption function, the weight percentage of each component of the diatomite molding composition is: 15% diatomaceous earth, 10% tourmaline powder, 5% zeolite powder, bamboo charcoal 3%, antibacterial agent 3%, acrylic resin adhesive 0.1%, the balance is gypsum powder, the antibacterial agent is an inorganic antibacterial agent obtained by attaching silver ions to glass, the particle size of diatomaceous earth is 20μm, and the particle size of tourmaline powder The particle size of gypsum powder is 20μm, and the particle size of bamboo charcoal is 20μm. The preparation method of the antibacterial agent is to take a mixture of metallic silver and glass into a stirring tank at a temperature of 1400°C, and then all the air in the stirring tank Replace with nitrogen, mix and stir for 2 hours. After stirring, take out the mixture and place it ...

Embodiment 2

[0031] Example 2: Preparation of diatomite molding composition

[0032] The formula is: a diatomaceous earth molding composition with moisture absorption function, the weight percentage of each component of the diatomaceous earth molding composition is: diatomaceous earth 20%, tourmaline powder 15%, zeolite powder 8%, bamboo charcoal 5%, antibacterial agent 5%, acrylic resin adhesive 1.0%, the balance is gypsum powder, the antibacterial agent is an inorganic antibacterial agent obtained by attaching silver ions to glass, the particle size of diatomaceous earth is 25μm, and the particle size of tourmaline powder The particle size of gypsum powder is 25μm, and the particle size of bamboo charcoal is 25μm. The preparation method of the antibacterial agent is to take a mixture of metallic silver and glass into a stirring tank at a temperature of 1700℃, and then all the air in the stirring tank Replace with nitrogen, mix and stir for 4 hours. After stirring, take out the mixture and p...

Embodiment 3

[0038] Example 3: Preparation of diatomite molding composition

[0039] The formula is: a diatomaceous earth molding composition with moisture absorption function, the weight percentage of each component of the diatomaceous earth molding composition is: diatomaceous earth 17%, tourmaline powder 12%, zeolite powder 6%, bamboo charcoal 4%, antibacterial agent 4%, acrylic resin adhesive 0.6%, the balance is gypsum powder, the antibacterial agent is an inorganic antibacterial agent obtained by attaching silver ions to glass, the particle size of diatomaceous earth is 22μm, and the particle size of tourmaline powder It is 22μm, the particle size of gypsum powder is 22μm, and the particle size of bamboo charcoal is 22μm. The preparation method of the antibacterial agent is to take a mixture of metallic silver and glass into a stirring tank at a temperature of 1500℃, and then all the air in the stirring tank Replace with nitrogen, mix and stir for 3 hours. After stirring, take out the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a diatomite forming composition with the moisture absorption function and a preparing method thereof. The diatomite forming composition is prepared from diatomite, tourmaline powder, zeolite powder, bamboo charcoal, antibacterial agent, acrylic resin adhesive and gypsum powder. The added antibacterial agent is an inorganic antibacterial agent obtained in the mode that a silver ion is attached to glass, and the inorganic antibacterial agent is high in safety, free of resistant bacteria and remarkable in antibacterial effect; when the antibacterial agent is prepared, metallic silver and the glass are mixed evenly under the high-temperature oxygen-free condition, and it can be avoided that the metallic silver is oxidized; when the antibacterial agent is prepared, a molten mixture is put into the low-temperature oxygen-free environment and cooled to the room temperature, the hardness of the antibacterial agent prepared with the method can be improved, the roughnessof the surface of the antibacterial agent is increased, and the falling-off phenomenon of the antibacterial agent is reduced; the tourmaline powder with the proper ratio and the zeolite powder with the proper ratio are added and can effectively excite negative oxygen ions in the room environment.

Description

Technical field [0001] The invention relates to the technical field of preparation and application of diatomite-based composite materials, in particular to a diatomite molding composition with moisture absorption function and a preparation method thereof. Background technique [0002] Diatomaceous earth is a kind of porous biological siliceous rock formed through preliminary diagenesis after the remains of ancient single-celled lower plant diatoms are deposited and deposited. It is composed of diatom wall shells with multi-level, large number of micropores arranged in an orderly manner, and diatomaceous earth has low density, large specific surface area, good adsorption, acid resistance, alkali resistance, insulation, etc. Characteristics, its unique surface structure and excellent adsorption performance are suitable for use as adsorption materials, and China's diatomite mineral resources are abundant, cheap and easy to obtain. Diatomite is composed of amorphous SiO 2 Compositio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/14C04B41/69C04B111/20
CPCC04B28/14C04B41/009C04B41/5116C04B41/69C04B2111/20C04B14/08C04B14/041C04B14/047C04B14/022C04B41/483C04B41/5022
Inventor 韦仲华卢发昭韦睿
Owner 桂林良物造环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap