Aerogel composite glass preparation method

A composite glass and a manufacturing method technology, applied in the field of aerogel composite glass manufacturing, can solve problems such as difficulty in mixing aerogel and glass melt, eliminate delamination, save additives and heat treatment process, shorten the time The effect of craft time

Active Publication Date: 2018-10-09
CHANGSHA XINGNA AEROGEL
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The solution of the present invention is: (1) Adopt transparent thermal insulation airgel technology with silanol on the surface and hydrophobic inside to solve the problem that airgel and glass melt are difficult to mix

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aerogel composite glass preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention will be described in detail below in conjunction with the accompanying drawings. The description in this part is only exemplary and explanatory, and should not have any limiting effect on the protection scope of the present invention. In addition, those skilled in the art can make corresponding combinations of features in the embodiments in this document and in different embodiments according to the descriptions in this document.

[0023] Embodiments of the present invention are as follows, a method for manufacturing an airgel composite glass, comprising the following steps:

[0024] (1) Heat the glass powder until it melts to obtain molten glass;

[0025] (2) Add the airgel into the molten glass and mix evenly to obtain a mixed molten glass;

[0026] (3) The mixed glass melt is continuously introduced to the float medium to form airgel composite glass by float method;

[0027] (4) Anneal the airgel composite glass.

[0028] The present inventio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
thicknessaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention provides an aerogel composite glass preparation method, wherein the aerogel composite glass comprises an aerogel and a glass phase adhered to the aerogel. The preparation method comprises: (1) preparing a glass melting liquid, wherein glass powder is heated and molten to obtain a glass melting liquid; (2) preparing a mixed glass melting liquid, wherein an aerogel is added to the glass melting liquid, and uniform mixing is performed; (3) molding, wherein the mixed glass melting liquid is continuously introduced onto a floating polishing medium, and float molding is performed; and(4) annealing. According to the present invention, with the manufacturing method, the resources of the float glass production line are completely utilized, the synchronous online production of the float glass and the aerogel composite glass can be achieved by adding the aerogel online and mixing with the glass melting liquid, and the prepared aerogel composite glass has advantages of good heat insulation performance, good light transmittance, good safety, good sound insulation and good noise reduction, and is suitable for the doors, the windows, the curtain wall glasses and the daylighting roofs of environmentally friendly buildings, ultra-low energy consumption buildings and near zero energy buildings, and other fields.

Description

technical field [0001] The invention relates to the technical field of glass preparation, in particular to a method for manufacturing airgel composite glass. Background technique [0002] Airgel is a lightweight nano-solid material that aggregates nanoscale ultrafine particles to form a nanoporous network structure, and fills the network pores with a gaseous dispersion medium. Its porosity is as high as 99.8%, the typical size of pores is 1-40nm, and the specific surface area is 400-1200m 2 / g, while the density can be as low as 3kg / m 3 , the thermal conductivity at room temperature can be as low as 0.010W / (m•K), showing excellent light weight, light transmission, heat insulation, heat preservation, sound insulation, fire resistance, impact resistance, and excellent chemical stability and non-combustibility. It is precisely because of these characteristics that silica airgel materials have broad application potential in thermal, acoustic, optical, microelectronics, and par...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C14/00C03B18/02C03B25/00
CPCC03B18/02C03B25/00C03C14/004
Inventor 卢梦言卢军卢孟磊张丁日卢斌
Owner CHANGSHA XINGNA AEROGEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products