Method for carrying out molten steel silicon alloying and calcium treatment by using metal-calcium-containing silicon-iron alloy
A technology of ferrosilicon alloy and metal calcium, which is applied in the field of iron and steel metallurgy refining, can solve the problems of metal calcium waste and high liquid oxygen content, and achieve the effects of reducing oxygen and nitrogen increase, reducing production cost and improving calcium yield.
Active Publication Date: 2018-10-12
UNIV OF SCI & TECH BEIJING
View PDF5 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Due to the high oxygen content in the molten steel during the tapping process of the converter, the calcium in the ferrosilicon is oxidized, resulting in a waste of metallic calcium
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment
[0025] Taking the 300t converter-LF refining-continuous casting process to produce pipeline steel as an example, according to thermodynamic calculations, the target calcium content in molten steel after calcium treatment for pipeline steel is 10-20ppm. The content of metallic calcium in the ferrosilicon alloy used in production is 0.38%, and the particle size is about 50mm. According to the target composition of silicon and calcium in pipeline steel, it is calculated that the amount of ferrosilicon added in the converter tapping process and the LF refining process is 360kg and 420kg respectively when the total ferrosilicon usage is constant.
[0026] Add slag for pre-refining during the tapping process of the converter, and control the acid-soluble aluminum content in the molten steel to 0.03-0.04% by adding aluminum particles to the molten steel. At the same time, 360 kg of the above-mentioned ferrosilicon alloy was added during the tapping process of the converter. After th...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
Login to view more
Abstract
The invention discloses a method for carrying out molten steel silicon alloying and calcium treatment by using metal-calcium-containing silicon-iron alloy, and belongs to the field of steel metallurgyrefining. The method is characterized in that in the tapping process after converter smelting, silicon alloying is not carried out or partial silicon alloying is carried out, the steel liquid aluminum deoxidation treatment and slag adding pre-refining are carried out at the same time, and the aluminum content is controlled according to the steel type requirement upper limit; and the metal-calcium-containing silicon-iron alloy is added into molten steel after secondary refining to carry out silicon alloying and calcium treatment, then argon is blown at a larger flow for stirring for 1-3 minutes so as to promote melting of the alloy, and then the argon is blown at a smaller flow for stirring so as to out low-flow argon blowing stirring to uniformize molten steel components and promote modification and floating of inclusions. According to the method for carrying out molten steel silicon alloying and calcium treatment by using the metal-calcium-containing silicon-iron alloy, the metal calcium contained in the silicon-iron alloy is utilized, and the targets of molten steel silicon alloying and calcium treatment are achieved at the same time by adjusting the silicon alloying time, so that the conventional calcium feeding line operation is reduced or even eliminated, and the production cost is reduced; and meanwhile, the situation of molten steel splashing caused by a calcium feedingline is avoided, oxygen increasing and nitrogen increasing of the molten steel are reduced, the operation stability and the yield of the calcium are improved, and then the cleanliness of the molten steel is also improved.
Description
technical field [0001] The invention relates to a method for simultaneously performing silicon alloying and calcium treatment of molten steel by using ferrosilicon alloy containing metallic calcium, and belongs to the field of iron and steel metallurgical refining. Background technique [0002] In the production process of aluminum deoxidized steel, calcium treatment process is widely used to prevent the submerged nozzle from being blocked during casting. In addition, calcium treatment is also widely used in the modification of MnS in pipeline steel and other steel types to avoid the formation of hydrogen-induced cracks during service. In iron and steel enterprises, calcium treatment is currently mainly carried out by feeding various calcium-containing cored wires into molten steel. These calcium-containing cored wires include pure calcium wires, silicon-calcium wires, and aluminum-calcium wires. In addition to increasing the cost, due to the high vapor pressure of calcium, ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/00C21C7/06C21C7/064C21C7/072
CPCC21C7/0006C21C7/06C21C7/064C21C7/072
Inventor 杨文张立峰任英
Owner UNIV OF SCI & TECH BEIJING
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap