Organic chemical silver-plating medicinal liquid

A chemical silver plating, organic technology, applied in liquid chemical plating, metal material coating process, coating and other directions, to achieve the effect of dense coating, good corrosion resistance, and solving environmental problems

Active Publication Date: 2018-12-18
厦门银方新材料科技有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing electroless silver plating potions all use water as the medium and belong to aqueous solution, which cannot avoid the occurrence of displacement reactions, so all technical defects are inevitable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic chemical silver-plating medicinal liquid
  • Organic chemical silver-plating medicinal liquid
  • Organic chemical silver-plating medicinal liquid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Organic chemical silver plating solution A, its components and dosage are:

[0036]

[0037] The application method is as follows:

[0038] Add 1 gram of copper powder into dilute sulfuric acid solution and ultrasonically stir for 3 minutes, settle and separate, wash with deionized water for 3 times, then soak in presoaking solution, settle and separate, then add 1L of silver plating solution A drop by drop while ultrasonically stirring and heating to 45°C for reaction 1 hour. After the product is separated by sedimentation, it is washed with post-wash liquid medicine, washed with water, separated and dried.

[0039] It can be observed with the eyes that the color of the copper powder has turned gray after silver plating. The state of the coating on the surface of the copper powder is further observed with an electron microscope (SEM), and analyzed by energy spectroscopy (EDS). The results show that the copper powder has been well coated. Cover the surface of coppe...

Embodiment 2

[0041] Organic chemical silver plating solution B, its components and dosage are:

[0042]

[0043]

[0044] Use the usual horizontal electroless plating production line for printed circuit boards, use silver plating potion B, and carry out silver plating according to the following process:

[0045] Degreasing, microetching, water washing, pre-dipping (the pre-dipping solution is the corresponding silver plating solution without silver salt), immersion silver, post-washing, water washing and drying.

[0046] The silver-plated PCB board is tested by section and metallographic microscope, and the sag rate is ≤1%, which shows that there is basically no "Giavani effect".

Embodiment 3

[0048] Organic chemical silver plating solution C, its components and dosage are:

[0049]

[0050]

[0051] The preparation method and application method are the same as in Example 2. The PCB board has been tested by section and metallographic microscope, and the sag rate is ≤1%, which shows that there is basically no "Giavani effect".

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses organic chemical silver-plating medicinal liquid. The organic chemical silver-plating medicinal liquid comprises the following compositions of 400-1000 g / L of organic solvent,0-600 g / L of water, 0.01-50 g / L of silver salt, 0.1-50 g / L of reducing agent, 1-300 g / L of complexing agent, 0-10 g / L of alkali, and 0.01-10 g / L of surface tension regulator. According to the organicchemical silver-plating medicinal liquid, silver plating does not depend on a displacement reaction mechanism and the organic chemical silver-plating medicinal liquid can be widely applied in copper powder silver plating and printed circuit board silver plating, and the 'Galvanic' effect of printed circuit board industry is avoided; the toxicity of the medicinal liquid is low, a plating solution can be used for a long time without replacement, and the serious environmental problems are solved; and a coating is compact and good in corrosion resistance, and is not prone to being changed in color.

Description

technical field [0001] The invention relates to a chemical solution for electroless silver plating on the surface of a copper substrate. Background technique [0002] At present, the technology of electroless silver plating on the surface of copper substrates basically relies on the mechanism of displacement reaction, that is, the silver ions in the silver plating solution undergo a displacement reaction with the copper substrate, and the silver ions react to form silver atoms and deposit on the surface of the copper substrate. At the same time, part of the copper atoms in the copper substrate become copper ions, detach from the substrate and dissolve in the liquid medicine. [0003] In the process of copper powder silver plating, this displacement reaction will cause the copper nucleus under the silver plating layer to become smaller or disappear; in the process of chemical silver plating of printed circuit boards, this displacement reaction will cause local lines to be bit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C18/44
CPCC23C18/44
Inventor 方斌赵望朱绪敏林芳芳
Owner 厦门银方新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com