Novel coating

A coating and a new technology, applied in the direction of coating, etc., can solve the problems of easy cracking and falling off, low hardness, no heat insulation, etc., and achieve the effect of not easy cracking and falling off, high hardness and good heat insulation effect

Inactive Publication Date: 2019-01-18
四会市中日化工实业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of living conditions, architectural coatings have become an essential material for indoor and outdoor decoration. At present, the widely used new coatings have disadvantages such as low hardness, easy cracking and falling off, and no heat insulation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of novel coating, is made up of following components by weight:

[0020] 90 parts of magnesium carbonate;

[0021] 10 parts of mica powder;

[0022] 10 parts of cellulose;

[0023] 10 parts of fluorescent powder;

[0024] 10 parts of porcelain calcium;

[0025] 4 parts of bentonite;

[0026] 15 parts of rubber powder;

[0027] 5 parts of benzoin powder;

[0028] 20 parts of paraffin alkane.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a novel coating. The coating is prepared from components in parts by weight as follows: 90 parts of magnesium carbonate, 10 parts of mica powder, 10 parts of cellulose, 10 partsof phosphor, 10 parts of vitrified calcium, 4 parts of bentonite, 15 parts of rubber powder, 5 parts of benzoin powder and 20 parts of paraffin alkane. The novel coating has high hardness and is notprone to cracking and peeling, the added benzoin can refresh mind and induce resuscitation, and an added brightener has a good thermal insulation effect.

Description

technical field [0001] The present invention relates to a new type of paint. Background technique [0002] With the improvement of living conditions, architectural coatings have become an essential material for indoor and outdoor decoration. At present, the widely used new coatings have disadvantages such as low hardness, easy cracking and falling off, and no heat insulation. Contents of the invention [0003] The invention aims to provide a novel coating with high hardness, which is not easy to crack and fall off, and the added benzoin can refresh the mind and rejuvenate the mind, and has good heat insulation effect. [0004] Its concrete plan is: a kind of novel coating, comprises following components by weight: [0005] 90 parts of magnesium carbonate; [0006] 10 parts of mica powder; [0007] 10 parts of cellulose; [0008] 10 parts of fluorescent powder; [0009] 10 parts of porcelain calcium; [0010] 4 parts of bentonite; [0011] 15 parts of rubber powder; ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/61C09D7/63C09D7/65
CPCC09D1/00
Inventor 李韬
Owner 四会市中日化工实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com