A high-voltage electrolyte suitable for fast-charging lithium cobalt oxide batteries and its application

An electrolyte and high-voltage technology, applied in the field of lithium-ion batteries, to achieve the effects of improving cycle stability, preventing local film thickness, and improving fast charging performance and low temperature performance

Active Publication Date: 2022-04-19
新乡华锐锂电新能源股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, it is still lacking to develop an effective method that can easily and simultaneously construct a stable and fast lithium ion transport interface protective layer on the negative and positive electrodes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-voltage electrolyte suitable for fast-charging lithium cobalt oxide batteries and its application
  • A high-voltage electrolyte suitable for fast-charging lithium cobalt oxide batteries and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] In an argon-filled glove box (moisture 4 ) and bis(trimethylsilyl)lithium phosphate (LiPO) based on 7.2% of the total mass of the electrolyte 4 (Si(CH 3 ) 3 ) 2 ), and stirred until it was completely dissolved to obtain the lithium-ion battery electrolyte of Example 1.

[0023] Inject the prepared electrolyte into the positive electrode LiCoO 2 Materials, in the pouch battery with graphite material as the negative electrode, the battery is packaged, placed on hold at 45°C, high-temperature formation, secondary packaging, and capacity separation to obtain a high-voltage lithium cobaltate lithium-ion battery.

[0024] As shown in Table 1, in Examples 2-5 and Comparative Examples 1-7, except that the components and proportions of the electrolyte solution are added as shown in Table 1, the others are the same as in Example 1.

[0025] Table 1 Composition and proportioning of the electrolyte solutions of Examples 1-5 and Comparative Examples 1-7

[0026]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-voltage electrolyte suitable for fast-charging lithium cobalt oxide batteries, which contains lithium salts, non-aqueous organic solvents and additives. Amino acid esters and methyl(difluorophosphoryl)methyl carbamate. Additives in LiCoO 2 A uniform, dense, and highly conductive protective film is formed on the surface of the material to inhibit the dissolution of metal ions in the positive electrode material and the collapse of the material structure. Forming a stable partial inorganic low-impedance SEI film at the graphite interface of the negative electrode can inhibit the free migration and reduction of metal ions in the electrolyte and reduce the damage to the electrode surface. Through the synergistic effect of various components in the electrolyte, it can make LiCoO 2 The positive electrode material and graphite negative electrode lithium ion battery have good cycle performance, fast charge performance and low temperature performance under high voltage.

Description

technical field [0001] The invention relates to the technical field of lithium-ion batteries, in particular to a high-voltage electrolyte suitable for fast-charging lithium cobalt oxide batteries and its application. Background technique [0002] Li-ion batteries are now an essential power source for portable electronic devices, electric vehicles, power stations or grid applications. However, its large-scale application still faces great challenges in terms of energy density, cycle life, fast charging performance, and operating temperature range. A possible approach to increase battery energy density is to use high-capacity electrode (cathode or anode) materials and high-voltage cathode materials. Lithium cobalt oxide (LiCoO 2 ) as the earliest commercial positive electrode material has the advantages of high voltage platform and high compaction density, but the capacity of conventional lithium cobalt oxide materials is only 140mAh / g, which is about 50% of its theoretical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/0567H01M10/0568H01M10/0569H01M10/0525
CPCH01M10/0567H01M10/0568H01M10/0569H01M10/0525H01M2300/0025Y02E60/10
Inventor 郭慧芳李娟程树国管利娜孟小平崔文举闫晓宾周亚辉张俊孝王福芳王小华
Owner 新乡华锐锂电新能源股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com