Inorganic real stone paint
A real stone paint, inorganic technology, applied in the direction of coating, etc., can solve the problems of low bonding strength of real stone paint, affecting the effect of real stone paint, cracking, falling off and stain resistance, etc., to achieve good water resistance, water resistance and alkali resistance of the coating Good performance and improved stain resistance
Inactive Publication Date: 2022-03-08
广东美家美福科技有限公司
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] However, when the existing inorganic real stone paint is used, it is prone to low bonding strength of real stone paint, as well as whitening and blooming in contact with water, resulting in cracking and falling off and poor stain resistance, thus affecting the effect of real stone paint in use.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0014] The following clearly and completely describes the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.
[0015] An inorganic real stone paint of the present invention comprises adding a certain amount of deionized water into a container, adding it into a disperser for stirring at 200 to 300 revolutions per minute, and adding disperse latex 03%, Antifreeze 01%, defoamer 1%, thickener 01% and hydroxyethyl methyl cellulose ether 02%, stirring time is 5-10min.
[0016] Wherein, after the stirring is completed, the rotating speed of the disperser is adjusted to 800-1100 revolutions per minute, and the stirring time is 10-12 minutes.
[001...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses an inorganic real stone paint which is prepared by the following steps: adding a certain amount of deionized water into a container, adding the deionized water into a dispersion machine, stirring at 200-300 revolutions per minute, respectively and sequentially adding 03% of dispersed latex, 01% of an antifreezing agent, 1% of a defoaming agent, 01% of a thickening agent and 02% of hydroxyethyl methyl cellulose ether into the dispersion machine, and stirring for 5-10 minutes to obtain the inorganic real stone paint. The coating has the beneficial effects that the stain resistance and the tensile bonding strength of a coating are improved, meanwhile, the coating has relatively good water resistance and alkali resistance and relatively good dry crack resistance in the initial stage, and the coating can have relatively good stability in storage by using 01% of a thickening agent and 02% of hydroxyethyl methyl cellulose ether; certain water resistance and alkali resistance are good, so that the basic requirements of construction are met.
Description
technical field [0001] The invention discloses an inorganic real stone paint, which belongs to the technical field of paint preparation. Background technique [0002] Real stone paint is made by using a variety of natural stone powders of different colors. It is mainly used in the construction field and used on the exterior walls of buildings to achieve the aesthetic effect of imitating stone. [0003] However, when the existing inorganic real stone paint is used, it is prone to low bonding strength of real stone paint, as well as whitening and blooming in contact with water, resulting in cracking and falling off and poor stain resistance, thus affecting the effect of real stone paint in use. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide an inorganic real stone paint, so as to solve the above problems. [0005] In order to achieve the above object, the present invention provides the following technical solutio...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/65C09D7/43
CPCC09D1/00C09D7/65C09D7/43
Inventor 梁传福梁家鑫梁家辉陈良英刘正坤
Owner 广东美家美福科技有限公司