Desulfurizing and dephosphoring refining agent for external refining of molten steel

A technology of refining and refining agents outside the furnace, which is applied in the field of processing molten ferrous alloys. It can solve the problems of molten steel rephosphorization, dephosphorization, and desulfurization, etc., and achieve the effects of improving steel properties, simplifying operations, and improving efficiency.

Inactive Publication Date: 2007-06-06
安徽中实冶金材料工程技术研究有限公司
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defect is: CaO-Al 2 o 3 The refining agent for out-of-furnace desulfurization of molten steel based on molten steel can only desulfurize, but cannot dephosphorize; the refining agent for dephosphorizing outside of molten steel based on CaO-FeO not only cannot desulfurize, but also after refining and making reducing slag, the molten steel will seriously return to phosphorus, polluting the molten steel and affecting production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Desulfurizing and dephosphoring refining agent for external refining of molten steel
  • Desulfurizing and dephosphoring refining agent for external refining of molten steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Under normal temperature and pressure, according to the components and content (weight %), weighing, crushing separately, milling, batching, adding binder, mixing, granulating, drying or baking, bagging. Then carry out desulfurization and dephosphorization trial outside the molten steel furnace, and calculate the desulfurization rate η s (%), and dephosphorization rate η p (%), its experimental data are listed in table 1.

Embodiment 2

[0018] Implement the method and steps of Example 1, and the experimental data are listed in Table 1.

Embodiment 3

[0020] Implement the method and steps of Example 1, and the experimental data are listed in Table 1.

[0021] Content of each component

[0022] It can be seen from Table 1 that the desulfurization and dephosphorization effects of the refining agent of the present invention are very good, and no phosphorus reversion phenomenon occurs at all.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention belongs to the field of ferrous alloy smelting treating agent, and is especially treating agent for external refining of molten steel. The treating agent contains BaO 35-70 wt%, BaF2 10-35 wt%, MnO 5-13 wt%, CaO 4-10 wt%, Al2O3 2-10 wt% and adhesive and impurity for the rest. It is used for desulfurzing and dephosphoring in external refining of molten steel. Compared with available technology, the present invention has the advantages of simultaneous external molten steel refining, desulfurzing and dephosphoring, raised production efficiency, improved molten steel quality, etc.

Description

technical field [0001] The invention belongs to the treatment of molten ferrous alloys, and in particular relates to an added treatment agent for refining outside a furnace. Background technique [0002] With the progress of society and the rapid development of industry, the requirements for the content of sulfur and phosphorus in steel are becoming more and more stringent. Reduce the content of sulfur and phosphorus in steel to produce clean molten steel. One of its main measures is to reduce the phosphorus content of the ferromanganese melt and adopt an out-of-furnace refining process. Refining agent is added during the refining process to desulfurize and dephosphorize molten steel. The current desulfurization uses CaO-Al 2 o 3 Out-of-furnace desulfurization agent based on molten steel, and CaO-FeO-based out-of-furnace dephosphorization refining agent for dephosphorization. Defects are: CaO-Al 2 o 3 The refining agent for out-of-furnace desulfurization of molten stee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C7/064
Inventor 颜根发黄志勇薜敬梅袁庭伟
Owner 安徽中实冶金材料工程技术研究有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com