[0129] Formulation Examples
[0130] To assess its performance properties, the composition according to the invention was stability-tested and its sensory properties were evaluated in a volunteer test. Commercially available wipes (substrate) weighing 60 g / m.sup.2 were coated with compositions 1 to 19 according to the invention and with comparison preparations C1 and C2 in quantities of 0.3 g per gram substrate 195 g / m.sup.2. The wipes coated with the compositions according to the invention are superior to known compositions in regard to sensory properties and storage stability. The storage stability of the wipes was evaluated after 12 weeks' storage after the compositions had been applied to the wipes together with a dye (phase 1) and the wipes had been aftertreated with an aqueous / surfactant-containing solution (phase 2). Any mixing of the phases is easy to see from the dye.
[0131] The quantities mentioned in the following Examples are based on % by weight of the commercially availabl...
Example
1TABLE 1 Composition / evaluation 1 2 3 4 5 6 7 8 9 10 11 12 Lanette .RTM. 14 58.99 47.99 47.99 47.99 20.0 Novata .RTM. B 64.99 54.99 49.99 39.99 58.99 30 19.99 10 Lanette .RTM. 16 32 33 Lanette .RTM. O 20 20 1 30 Lanette .RTM. 18 23 25 20 25 Cegesoft .RTM. HF 52 5 10 20 20 Cegesoft .RTM. GPO 5 Cegesoft .RTM. PS 6 3 10 10 Eumulgin .RTM. VL 75 2 2 2 10 10 Eumulgin .RTM. B1 3 2 1 15 5 Cutina .RTM. MD 4 2 1 25 20 10 20 Monomuls .RTM. 90-L 12 14 Cithrol .RTM. 10 MS 15 14 14 10 10 5 Distearyl carbonate 2 5 5 2 5 1 5 2 Distearyl ether7 1 2 5 5 Tocopherol 1 1 1 2 1 1 1 1 1 Tospearl .RTM. 145 A 5 2 5 Dye DC Green 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 Zinc stearate11 2 Panthenol1 1 1 3 Bisabolol 1 Water to 100
[0132] The penetration values as measured with a penetrometer (Petrotester PNR 10, microcone, 5 secs., 20.degree. C.) are 0.54 mm-2.43 mm.
2TABLE 2 Composition / evaluation 13 14 15 16 17 18 19 C1 C2 Lanette .RTM. 14 47.99 47.99 75 Novata .RTM. B 47.99 47.99 40.0 55.99 50.99...
PUM
Property | Measurement | Unit |
---|---|---|
Temperature | aaaaa | aaaaa |
Percent by mass | aaaaa | aaaaa |
Percent by mass | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap