Strip castings of immiscible metals
a strip casting and metal technology, applied in the field of metal casting, can solve the problems of low productivity, high cost, and inability to achieve the desired soft phase distribution, and achieve the effect of high speed and high uniformity of structur
Inactive Publication Date: 2013-08-22
ARCONIC INC
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
The method achieves a highly uniform distribution of fine particles, enhancing productivity and eliminating the need for heat treatment, resulting in a cast strip suitable for bearings with improved lubricating properties.
Problems solved by technology
In the prior art, the soft second phase in these alloys separates during solidification and often appears in the form of non uniform distribution.
A drawback of twin roll casting, however, is that the method is slow, yields low productivity and creates a distribution of the soft phase(s) that is not completely desirable.
Suitable results are also produced using a powder metallurgy process; however this method is expensive.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0012]The accompanying drawings and the description which follows set forth this invention in its preferred embodiments. It is contemplated, however, that persons generally familiar with casting processes will be able to apply the novel characteristics of the structures and methods illustrated and described herein in other contexts by modification of certain details. Accordingly, the drawings and description are not to be taken as restrictive on the scope of this invention, but are to be understood as broad and general teachings. When referring to any numerical range of values, such ranges are understood to include each and every number and / or fraction between the stated range minimum and maximum.
[0013]Finally, for purposes of the description hereinafter, the terms “upper”, “lower”, “right”, “left”, “vertical”, “horizontal”, “top”, “bottom”, and derivatives thereof shall relate to the invention, as it is oriented in the drawing figures.
The phrases “aluminum alloys”, are intended to ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| dimensions | aaaaa | aaaaa |
| size | aaaaa | aaaaa |
| size | aaaaa | aaaaa |
Login to View More
Abstract
The present invention discloses a method of strip casting an aluminum alloy from immiscible liquids that yields a highly uniform structure of fine second phase particles. The results of the present invention are achieved by using a known casting process to cast the alloy into a thin strip at high speeds. In the method of the present invention, the casting speed is preferably in the region of about 50-300 feet per minute (fpm) and the thickness of the strip preferably smaller than 0.08-0.25 inches. Under these conditions, favorable results are achieved when droplets of the immiscible liquid phase nucleate in the liquid ahead of the solidification front established in the casting process. The droplets of the immiscible phase are engulfed by the rapidly moving freeze front into the space between the Secondary Dendrite Arms (SDA).
Description
RELATED APPLICATIONS[0001]This application is a continuation of U.S. application Ser. No. 11 / 734,113, filed on Apr. 11, 2007. The entirety of this application is hereby incorporated herein by reference for the teachings therein.FIELD OF THE INVENTION[0002]This invention relates to the casting of metals and to a method of strip casting immiscible metals in particular.BACKGROUND OF THE INVENTION[0003]Aluminum based alloys containing Sn, Pb and Cd are commonly used in bearings found in internal combustion engines. The bearing function in these alloys is performed by the soft second phase particle of the alloying element which melts in the event of lubricant failure and prevents contact between the aluminum in the alloy and the steel protected by the bearing.[0004]In the prior art, the soft second phase in these alloys separates during solidification and often appears in the form of non uniform distribution. In many cases the second phase forms at grain boundaries as a continuous layer,...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(United States)
IPC IPC(8): B22D25/06
CPCB22D11/0605B22D25/06C22C21/00B22D11/112
Inventor TOMES, JR., DAVID A.WYATT-MAIR, GAVIN F.TIMMONS, DAVID W.UNAL, ALI
Owner ARCONIC INC