Water-based organic silicon waterproof agent

A waterproofing, water-based technology, applied in other chemical processes, chemical instruments and methods, etc., can solve problems such as defects that have not been overcome, and achieve the effect of improving strength and improving impermeability.

Inactive Publication Date: 2011-06-15
郭元华
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Products in the prior art still do not overcome the existing defects of sodium methyl siliconate aqua

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based organic silicon waterproof agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Under stirring, first dissolve 20g of SSOPA and 20g of polyethylene glycol (PEG 6000) in 100ml of hot water at about 60°C, then add 40g of alum, 25g of silane coupling agent KH-550 and 375g of sodium methyl siliconate, After uniformity, adjust the pH value to 7.5 with phosphoric acid, and finally add water to make up to 1000ml.

Embodiment 2

[0063] Under stirring, first dissolve 20g of SSOPA and 20g of polyethylene glycol (PEG 4000) in 100ml of hot water at about 60°C, then add 40g of alum, 30g of silane coupling agent KH-550 and 470g of sodium methyl siliconate, After uniformity, adjust the pH value to 7.5 with phosphoric acid, and finally add water to make up to 1000ml.

Embodiment 3

[0065] While stirring, first dissolve 20g of SSOPA and 20g of polyethylene glycol (PEG 6000) in 100ml of hot water at about 60°C, then add 40g of alum, 25g of silane coupling agent KH-550 and 475g of sodium methyl siliconate, After uniformity, adjust the pH value to 7.0 with phosphoric acid, and finally add water to make up to 1000ml.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a water-based organic silicon waterproof agent by taking sodium methylsilanolate as a main raw material, and is particularly suitable for moving penetration waterproof processing of a porous structure, such as bricks, stone materials, concrete, mortar, cement slurry and the like.

Description

field of invention [0001] The invention relates to a water-based silicone waterproofing agent for building materials, in particular to a water-based silicone waterproofing agent with sodium methyl siliconate as the main raw material. Background technique [0002] Concrete and masonry structures often fail to reach the designed service life due to insufficient durability. Factors leading to the deterioration of concrete properties include steel corrosion, freeze-thaw damage, chemical attack and alkali-aggregate reaction. Water plays a very important role in the process of physical damage and chemical attack to which concrete structures are subjected. If cement-based materials are exposed to water, a series of corrosion reactions will occur. Under the action of one or more of these factors, the service life of concrete will be reduced. [0003] The corrosion effect of water on concrete can be divided into four aspects: (1) In the long-term contact with the cement substrate,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/18C04B103/65C04B41/49C04B24/42
Inventor 郭元华
Owner 郭元华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com