Processing method for preventing porous mould of laboratory gene memory board from cracking

A porous mold and processing method technology, applied in the direction of manufacturing tools, furnaces, heat treatment equipment, etc., can solve problems such as cracking, stress accumulation, and steel materials that cannot be synchronized, and achieve good surface finish, good rigidity, and frequent fracture prevention.

Active Publication Date: 2010-06-02
SHENZHEN CHANGHONG TECH CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 2. There are two types of hardness in the material, which leads to the inconsistency of the inner and outer steel materials when elastic deformation occurs, resulting in internal stress. During the production process, the mold repeatedly opens and closes, resulting in stress accumulation and the possibility of cracking;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing method for preventing porous mould of laboratory gene memory board from cracking
  • Processing method for preventing porous mould of laboratory gene memory board from cracking

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Below in conjunction with embodiment the present invention is described in further detail:

[0017] The processing method for preventing the cracking of the porous mold of the laboratory gene storage plate includes:

[0018] (1) The core of the mold is made of steel, and the groove at the bottom of the mold insert after grinding is formed into a rounded corner;

[0019] (2) Carry out high temperature quenching at 1020 degrees;

[0020] (3) Carry out subzero 150 ° cryogenic tempering;

[0021] (4) After 2 times of 300 ° low temperature tempering;

[0022] (5) Carry out precision machining to the steel, and carry out mold assembly after finish machining;

[0023] (6) After the mold trial is qualified, the mold is again subjected to low-temperature stress-relief tempering within the range of 250° to 275°.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a processing method for preventing a porous mould of a laboratory gene memory board from cracking, comprising the following steps: (1) the core of the mould is made of steel, bottom end slot position of a mould insert, which goes through grinding is molded into a filleted corner; (2) hot quenching is carried out at 1020 degrees; (3) copious cooling and tempering are carried out at -150 degrees; (4) low temperature tempering is carried out at 300 degree twice; (5) precision finishing is carried out on the steel, and as the mould is assembled after the precision finishing is finished; and (6) low temperature destressing tempering is performed on the mould within the range of 250-275 degrees after mould testing is qualified. The processing method of the invention solves the technical problem that the mould insert is frequently cracked and ensures the mould can keep favorable rigidity and optimum tenacity in the production process.

Description

technical field [0001] The invention relates to a processing method for preventing cracking of a porous mold of a laboratory gene storage plate. Background technique [0002] Known molds are mostly used for medical consumables such as laboratory gene storage boards. The mold is composed of 117 pillars, and the pillars are separated by grooves. The mold is prone to breakage during the production process. According to statistics, when a newly made back mold core is produced to 100,000 products, an average of 20 to 25 pillars will break, and when the number of broken pillars reaches about 25 pieces , the mold is scrapped. According to the analysis of the fracture, it is found that there is regularity, the fracture is at the same position, and the shape of the crack is also very close. Through the microscopic observation of the mold insert, it is found that the surface of the steel has irregular particles evenly distributed on the part of the steel surface that has been cut by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D9/00C21D1/18
Inventor 谢如文
Owner SHENZHEN CHANGHONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com