Medical cross-linking sodium hyaluronate gel derivative product and preparation method thereof

A technology of cross-linked hyaluronic acid and hyaluronic acid, which is applied in the field of medical cross-linked sodium hyaluronate gel derivatives and its preparation, and can solve the problem of reduced viscoelasticity and unsatisfactory maintenance time of cross-linked hyaluronic acid gel , easy to cause inflammatory reactions in the body and other problems, to achieve good tissue compatibility and biodegradability, good effect and durability, and good filling effect

Inactive Publication Date: 2010-06-30
上海建华精细生物制品有限公司
View PDF0 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when administered to a living body, the residual cross-linking agent is likely to cause an inflammatory reaction in the body. If the amount of cross-linking agent used is reduced by conventional methods, the viscoelasticity of the obtained cross-linked hyaluronic acid gel will be reduced, and it will not be soft. Unsatisfactory effect or unsatisfactory maintenance time when used as a drug sustained-release preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical cross-linking sodium hyaluronate gel derivative product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Put 3.3g of hyaluronic acid fine powder with a molecular weight of 2 million Daltons in a container filled with 30ml of 0.25M NaOH solution, and stir and mix for 3 hours;

[0031] During stirring, add 0.3ml of 1,4-butanediol diglycidyl ether (BDDE), and then place the solution in a water bath at 45°C for 5 hours to form a cross-linked hyaluronic acid gel;

[0032] Subsequently, 500 mL of PBS buffer solution with a pH of 7.3 was added, soaked and washed repeatedly for 6 times, and washed for 2.5 days.

[0033] Then put the hyaluronic acid gel in the pressure extrusion device, set the hole diameter to 500 μm, pressurize 7kg / cm 2 , Extrude the hyaluronic acid gel into a microgel.

[0034] Then stir and mix the particulate hyaluronic acid gel and hyaluronic acid to obtain a product, wherein the final concentration of hyaluronic acid is 2 mg / ml. Filling and autoclaving (121° C., 30 minutes).

Embodiment 2

[0036] Put 4g of hyaluronic acid fine powder with a molecular weight of 2 million Daltons in a container containing 30ml of 0.25M NaOH solution, and stir and mix for 4 hours;

[0037] During stirring, add 0.4ml 1,4-butanediol diglycidyl ether (BDDE), and then place the solution in a water bath at 50°C for 5 hours to form a cross-linked hyaluronic acid gel;

[0038] Then add 500mL deionized water to soak and wash repeatedly 8 times, and wash for 3 days.

[0039] Then put the hyaluronic acid gel in the pressure extrusion device, set the hole diameter to 550 μm, pressurize 8kg / cm 2 , Extrude the hyaluronic acid gel into a microgel. Then stir and mix the particulate hyaluronic acid gel with hyaluronic acid, and the final concentration of hyaluronic acid is 2mg / ml. Filling and autoclaving (121° C., 30 minutes).

Embodiment 3

[0041] Put 2.6g of hyaluronic acid fine powder with a molecular weight of 2 million Daltons in a container filled with 30ml of 0.25M NaOH solution, and stir and mix for 4 hours;

[0042] During stirring, add 0.3ml of 1,4-butanediol diglycidyl ether (BDDE), and then place the solution in a water bath at 40°C for 3 hours to form a cross-linked hyaluronic acid gel;

[0043] Then add 500mL deionized water to soak and wash 6 times repeatedly for 2.5 days.

[0044] Then put the hyaluronic acid gel in the pressure extrusion device, set the hole diameter to 550 μm, pressurize 8kg / cm 2 , Extrude the hyaluronic acid gel into a microgel.

[0045] Then stir and mix the particulate hyaluronic acid gel with hyaluronic acid, and the final concentration of hyaluronic acid is 1mg / ml. Filling and autoclaving (121° C., 30 minutes).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention provides a medical cross-linking sodium hyaluronate gel derivative product and a preparation method thereof. The preparation contains cross-linking hyaluronic acid and non-crosslinked hyaluronic acid; the cross-linking hyaluronic acid reacts with hyaluronic acid molecules by using a cross-linking agent under the alkaline environment and forms cross-linking hyaluronic acid gel, and then the cross-linking agent is removed to prepare the medical cross-linking sodium hyaluronate gel derivative product. The product has good biocompatibility and longer half-life period and is suitable for tissue filling, bone articular lubrication or medicine sustained-release preparation and the like.

Description

technical field [0001] The invention relates to a medical cross-linked sodium hyaluronate gel derivative product and a preparation method thereof. Background technique [0002] Hyaluronic Acid (HA) gel is widely used in ophthalmology, orthopedics, gynecology, plastic surgery and other fields. It has been in clinical practice for more than ten years, and its safety and effectiveness have been recognized by all medical circles. generally accepted. Natural exogenous hyaluronic acid has a molecular weight of about 100,000 to 5 million Daltons, and its retention time in the body is about 3 to 15 days, which largely limits its application in certain fields. For example, it is used for tissue filling to improve facial wrinkles and creases, improve lip shape and correct facial contours, etc.; or for bone and joint lubrication, the effect duration is too short and continuous injection is required. [0003] Cross-linked hyaluronic acid gel is a cross-linked product of hyaluronic aci...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L5/08C08J3/24C08K5/1515C08K5/07C08K5/41
Inventor 任彩霞孔淑静侯永泰
Owner 上海建华精细生物制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap